Research Article
Estimation of Optimum Dilution in the GMAW Process Using Integrated ANN-GA
Table 4
Design matrix and observed values of clad bead geometry.
| Trial no. | Design matrix | Bead parameters | | | | | Ac | (mm) | (mm) | (mm) | (%) |
| 1 | −1 | −1 | −1 | −1 | 1 | 6.9743 | 1.67345 | 6.0262 | 10.72091 | 2 | 1 | −1 | −1 | −1 | −1 | 7.6549 | 1.9715 | 5.88735 | 12.16746 | 3 | −1 | 1 | −1 | −1 | −1 | 6.3456 | 1.6986 | 5.4519 | 12.74552 | 4 | 1 | 1 | −1 | −1 | 1 | 7.7635 | 1.739615 | 6.0684 | 10.61078 | 5 | −1 | −1 | 1 | −1 | −1 | 7.2683 | 2.443 | 5.72055 | 16.67303 | 6 | 1 | −1 | 1 | −1 | 1 | 9.4383 | 2.4905 | 5.9169 | 15.96692 | 7 | −1 | 1 | 1 | −1 | −1 | 6.0823 | 2.4672 | 5.49205 | 16.5894 | 8 | 1 | 1 | 1 | −1 | −1 | 8.4666 | 2.07365 | 5.9467 | 14.98494 | 9 | −1 | −1 | −1 | 1 | −1 | 6.3029 | 1.5809 | 5.9059 | 10.2749 | 10 | 1 | −1 | −1 | 1 | 1 | 7.0136 | 1.5662 | 5.9833 | 9.707297 | 11 | −1 | 1 | −1 | 1 | 1 | 6.2956 | 1.58605 | 5.5105 | 11.11693 | 12 | 1 | 1 | −1 | 1 | −1 | 7.741 | 1.8466 | 5.8752 | 11.4273 | 13 | −1 | −1 | 1 | 1 | 1 | 7.3231 | 2.16475 | 5.72095 | 15.29097 | 14 | 1 | −1 | 1 | 1 | −1 | 9.6171 | 2.69495 | 6.37445 | 18.54077 | 15 | −1 | 1 | 1 | 1 | −1 | 6.6335 | 2.3089 | 5.554 | 17.23138 | 16 | 1 | 1 | 1 | 1 | 1 | 10.514 | 2.7298 | 5.4645 | 20.8755 | 17 | −2 | 0 | 0 | 0 | 0 | 6.5557 | 1.99045 | 5.80585 | 13.65762 | 18 | 2 | 0 | 0 | 0 | 0 | 7.4772 | 2.5737 | 6.65505 | 15.74121 | 19 | 0 | −2 | 0 | 0 | 0 | 7.5886 | 2.50455 | 6.4069 | 15.77816 | 20 | 0 | 2 | 0 | 0 | 0 | 7.5014 | 2.1842 | 5.6782 | 16.82349 | 21 | 0 | 0 | −2 | 0 | 0 | 6.1421 | 1.3752 | 6.0976 | 8.941799 | 22 | 0 | 0 | 2 | 0 | 0 | 8.5647 | 3.18536 | 5.63655 | 22.94721 | 23 | 0 | 0 | 0 | −2 | 0 | 7.9575 | 2.2018 | 5.8281 | 15.74941 | 24 | 0 | 0 | 0 | 2 | 0 | 7.7085 | 1.85885 | 6.07515 | 13.27285 | 25 | 0 | 0 | 0 | 0 | −2 | 7.8365 | 2.3577 | 5.74915 | 16.63287 | 26 | 0 | 0 | 0 | 0 | 2 | 8.2082 | 2.3658 | 5.99005 | 16.38043 | 27 | 0 | 0 | 0 | 0 | 0 | 7.9371 | 2.1362 | 6.0153 | 15.18374 | 28 | 0 | 0 | 0 | 0 | 0 | 8.4371 | 2.17145 | 5.69895 | 14.82758 | 29 | 0 | 0 | 0 | 0 | 0 | 9.323 | 3.1425 | 5.57595 | 22.8432 | 30 | 0 | 0 | 0 | 0 | 0 | 9.2205 | 3.2872 | 5.61485 | 23.6334 | 31 | 0 | 0 | 0 | 0 | 0 | 10.059 | 2.86605 | 5.62095 | 21.55264 | 32. | 0 | 0 | 0 | 0 | 0 | 8.9953 | 2.72068 | 5.7052 | 19.60811 |
|
|
: width; : penetration; : reinforcement; : dilution %.
|