Effect of Water-Cement Ratio on the Macrocell Polarization Behavior of Reinforcing Steel

Table 2

Case design for the effect of water-cement ratio.

Case number	A-side	B-side	Case number	A-side	B-side
9-1	P45-0-1	P45-3-1	9-2	P45-0-2	P45-3-2
10-1	P60-0-1	P60-3-1	10-2	P60-0-3	P60-3-2
11-1	P70-0-1	P70-3-1	11-2	P70-0-2	P70-3-2

Note: in this table, the steel with polished surface was marked as P. The W/C ratio of specimen was marked as 45, 60, and 70. The chloride content of specimen was marked as 0 and 3. The serial number of specimens was marked as 1, 2, and 3. For example of P45-0-1, P means the steel had polished surface, 45 means the W/C ratio of specimen was 0.45, 0 means the chloride content of specimen was 0 wt% of cement, and 1 means the serial number of specimens was 1.