Surface Modification and Alloying of Aluminum and Titanium Alloys with Low-Energy, High-Current Electron Beams
Figure 10
XRD patterns of Ti-6Al-4V alloy samples before and after LEHCEB irradiation at different initial temperatures. Incident angle is 1°.