Surface Modification and Alloying of Aluminum and Titanium Alloys with Low-Energy, High-Current Electron Beams
Figure 11
Volume loss versus sliding distance for Ti-6Al-4V alloy samples before and after LEHCEB irradiation at different initial temperatures. Wear tests were performed in dry conditions using a ball-on-plate configuration with Ti-6Al-4V alloy sliding against steel 100 Cr6, ball diameter 5 mm; N, sliding rate 0.015 m/s.