Martensitic Twinning in Alpha + Beta Ti-3.5Al-4.5Mo Titanium Alloy
Figure 3
(a) The TEM bright field image of the sample quenched from 910°C, (b) the corresponding SAED pattern of the encircled area obtained from sample quenched from 910°C, the martensite is in the class B transformation, namely, the compound twinning. (c) A representative TEM bright field micrograph structure in the sample quenched from 840°C and the SAED pattern from the circled region is shown in (d); and the martensite is type I twinning, belonging to class A transformation.