The Effect of Microstructure on Stress-Strain Behaviour and Susceptibility to Cracking of Pipeline Steels
Figure 10
X65 steel furnace cooled after 5 hours at 1175°C, then air cooled after 20 minute at 950°C and again furnace cooled after 20 minutes at 1000°C.