Experimental Study of the Interaction between Recrystallization and Precipitation Processes of an AA8011 Commercial Alloy
Figure 3
(a) Thermoelectric power and (b) derivative of the thermoelectric power versus temperature for the homogenized AA8011 alloy, quenched and deformed at different rolling degrees, then heated isochronously during 10 minutes at each temperature.