Experimental Study of the Interaction between Recrystallization and Precipitation Processes of an AA8011 Commercial Alloy
Figure 4
(a) Thermoelectric power versus temperature for 85-DHS samples preaged during different times at 300°C, then annealed isochronously for 25 minutes at each temperature. (b) Amplified initial part of curve (a) for high preaging times at 300°C.