Thermomechanical Stresses in Fullerenes at Nanotube

Table 2

Computed values for C82@(10,10), thermomechanical stresses are in the gigapascal range.

T [K]	𝑟^/𝑜 [nm]	𝑅^/𝑖 [nm]	𝑝 [MPa]	𝜎𝑟𝑓,𝜎𝑟𝑛 [MPa]	𝜎𝜗𝑓 [MPa]	𝜎𝜗𝑛 [MPa]	𝑟^∗𝑜 [nm]	𝑅^∗𝑖 [nm]
290	0.56000	0.53000	18939.39	−18939.39	−12941.92	42929.29	0.55469	0.55919
280	0.55997	0.53004	18892.14	−18892.14	−12909.63	42822.18	0.55468	0.55916
270	0.55994	0.53009	18849.84	−18849.84	−12880.72	42726.29	0.55466	0.55914
260	0.55992	0.53012	18812.49	−18812.49	−12855.20	42641.64	0.55465	0.55912
250	0.55991	0.53016	18780.09	−18780.09	−12833.06	42568.21	0.55465	0.55911
240	0.55990	0.53019	18752.65	−18752.65	−12814.31	42506.01	0.55464	0.55909
230	0.55989	0.53022	18730.16	−18730.16	−12798.95	42455.04	0.55464	0.55909
220	0.55989	0.53024	18712.63	−18712.63	−12786.96	42415.30	0.55464	0.55909
210	0.55989	0.53027	18700.05	−18700.05	−12778.37	42386.78	0.55465	0.55909
200	0.55990	0.53029	18692.42	−18692.42	−12773.16	42369.49	0.55466	0.55910
190	0.55991	0.53030	18689.75	−18689.75	−12771.33	42363.44	0.55467	0.55911
180	0.55992	0.53031	18692.03	−18692.03	−12772.89	42368.61	0.55469	0.55913
170	0.55994	0.53032	18699.27	−18699.27	−12777.83	42385.01	0.55471	0.55915
160	0.55997	0.53033	18711.46	−18711.46	−12786.16	42412.63	0.55473	0.55917
150	0.56000	0.53033	18728.60	−18728.60	−12797.88	42451.49	0.55475	0.55920
140	0.56004	0.53033	18750.69	−18750.69	−12812.97	42501.57	0.55478	0.55923
130	0.56007	0.53033	18777.74	−18777.74	−12831.46	42562.89	0.55481	0.55927
120	0.56012	0.53032	18809.75	−18809.75	−12853.33	42635.43	0.55485	0.55932
110	0.56017	0.53031	18846.70	−18846.70	−12878.58	42719.20	0.55489	0.55936
100	0.56022	0.53030	18888.62	−18888.62	−12907.22	42814.19	0.55493	0.55942
90	0.56028	0.53029	18935.48	−18935.48	−12939.24	42920.42	0.55497	0.55947
80	0.56034	0.53027	18987.30	−18987.30	−12974.65	43037.88	0.55502	0.55953
70	0.56041	0.53024	19044.07	−19044.07	−13013.45	43166.56	0.55508	0.55960
60	0.56037	0.53022	19033.19	−19033.19	−13006.02	43141.91	0.55504	0.55956
50	0.56032	0.53019	19020.96	−19020.96	−12997.66	43114.18	0.55499	0.55951
40	0.56027	0.53016	19007.37	−19007.37	−12988.37	43083.36	0.55494	0.55946
30	0.56021	0.53012	18992.41	−18992.41	−12978.15	43049.47	0.55489	0.55940
20	0.56014	0.53009	18976.10	−18976.10	−12967.00	43012.49	0.55483	0.55933
10	0.56007	0.53004	18958.43	−18958.43	−12954.92	42972.43	0.55476	0.55927