Low-Temperature Preparation of Amorphous-Shell/ Nanocrystalline-Core Nanostructured Electrodes for Flexible Dye-Sensitized Solar Cells
Figure 2
XRD patterns of the TiO2 electrodes (a) before and (b) after sintering as
well as (c) the TiO2 resulted from 0.5 M TiCl4 water solution sintered at 100°C
for 12 hours (small peaks resulted from SnO2 conductive glass).