Research Article
Electrospun Poly(L-Lactide-co-ε-Caprolactone)/Polyethylene Oxide/Hydroxyapaite Nanofibrous Membrane for Guided Bone Regeneration
Table 2
Mechanical properties and contact angles of the PLCL/PEO/HA composite fibrous membranes.
| | Materails and their concentration (g/mL) | Tensile strength (MPa) | Elongation at break (%) | Contact angle in 5 minutes (C) | Contact angle in 5 seconds (C) |
| | PLCL (6) | 9.88 ± 0.64 | 1.85 ± 0.43 | 130.0 | — | | PLCL/PEO/HA (6/0.3/0.03) | 10.64 ± 0.38 | 3.53 ± 0.35 | 60.9 | — | | PLCL/PEO/HA (6/0.4/0.03) | 13.97 ± 0.74 | 2.61 ± 0.12 | 0 | 0 | | PLCL/PEO/HA (6/0.5/0.03) | 17.19 ± 0.32 | 2.79 ± 1.20 | 0 | 73.5 | | PLCL/PEO/HA (6/0.6/0.03) | 10.47 ± 1.24 | 2.21 ± 0.46 | 32.9 | — | | PLCL/PEO/HA (6/0.4/0.01) | 8.83 ± 0.28 | 2.08 ± 0.02 | 0 | 37.5 | | PLCL/PEO/HA (6/0.4/0.03) | 13.97 ± 0.74 | 2.61 ± 0.12 | 0 | 0 | | PLCL/PEO/HA (6/0.4/0.05) | 12.50 ± 1.03 | 2.00 ± 0.15 | 0 | 109.1 | | PLCL/PEO/HA (6/0.4/0.1) | 8.22 ± 1.01 | 2.24 ± 0.22 | 129.2 | — |
|
|
The data are representative of three samples and expressed as mean ± SD ().
|