Design and Preparation of Cross-Linked Polystyrene Nanoparticles for Elastomer Reinforcement
Table 6
Mechanical properties of the cross-linked PS-filled SBR, NBR, and NR nanocomposites.
| Samples | Shore A Hardness | Stress at 100% Elongation/MPa | Stress at 300% Elongation/MPa | Tensile Strength/MPa | Elongation at Break/% | Permanent Set/% | Tear Strength/KN/m |
| Pure SBR | 48 | 1.1 | 1.5 | 2.0 | 461 | 4 | 11 | PS (30)/SBR | 81 | 2.7 | 4.8 | 12.9 | 601 | 36 | 39 |
| Pure NBR | 55 | 1.2 | 2.2 | 3.5 | 438 | 0 | 16 | PS(30)/NBR | 80 | 2.7 | 7.6 | 9.3 | 345 | 12 | 33 |
| Pure NR | 35 | 0.7 | 1.6 | 28.3 | 801 | 16 | 30 | PS(30)/NR | 75 | 1.9 | 3.9 | 19.7 | 650 | 56 | 76 |
|
|
Note that filler loading was 30 phr, all samples were cured with sulfur.
|