Thermal Behavior with Mechanical Property of Fluorinated Silane Functionalized Superhydrophobic Pullulan/Poly(vinyl alcohol) Blends by Electrospinning Method

<table>DSC data of PULL/PVA blend membranes (a) without PFOTES, and (b) with PFOTES using electrospinning method (Applied voltage = 15 kV, TCD = 15 cm, Blend ratio (PULL/PVA) = 80/20, and Total polymer concentration = 9 wt.%).</table>