Influence of Selected Alkoxysilanes on Dispersive Properties and Surface Chemistry of Titanium Dioxide and TiO2–SiO2 Composite Material
Table 3
Adsorption properties of modified TiO2 and TiO2–SiO2 composite material.
| Sample | Modifying agent | Amount of modifying agent (wt./wt.) | (m2/g) | (cm3/g) | (nm) |
| A11 | — | — | 10.0 | 0.020 | 7.6 | U-511 silane | 0.5 | 8.5 | 0.001 | 5.8 | 3 | 7.1 | 0.005 | 3.0 | U-611 silane | 0.5 | 9.0 | 0.004 | 2.0 | 3 | 7.4 | 0.004 | 1.6 | U-15D silane | 0.5 | 5.6 | 0.004 | 3.0 | 3 | 4.9 | 0.004 | 3.1 |
| R001 | — | — | 14.0 | 0.030 | 7.6 | U-511 silane | 0.5 | 8.2 | 0.006 | 3.0 | 3 | 5.3 | 0.004 | 3.0 | U-611 silane | 0.5 | 9.6 | 0.007 | 2.8 | 3 | 9.3 | 0.006 | 2.4 | U-15D silane | 0.5 | 8.3 | 0.006 | 2.9 | 3 | 5.6 | 0.004 | 3.0 |
| R213 | — | — | 35.0 | 0.090 | 9.8 | U-511 silane | 0.5 | 25.2 | 0.017 | 2.8 | 3 | 21.0 | 0.015 | 2.8 | U-611 silane | 0.5 | 25.7 | 0.018 | 2.9 | 3 | 23.6 | 0.017 | 2.8 | U-15D silane | 0.5 | 25.1 | 0.018 | 2.8 | 3 | 20.8 | 0.014 | 2.6 |
| TP10 | — | — | 36.0 | 0.040 | 4.6 | U-511 silane | 0.5 | 27.3 | 0.018 | 2.0 | 3 | 23.2 | 0.016 | 1.8 | U-611 silane | 0.5 | 26.9 | 0.016 | 2.0 | 3 | 24.1 | 0.013 | 1.9 | U-15D silane | 0.5 | 25.8 | 0.014 | 2.0 | 3 | 21.6 | 0.011 | 1.8 |
|
|