Comparative Characterization of Multiscale Carbon Fiber Composite with Long and Short MWCNTs at Higher Weight Fractions
Table 1
Thermal diffusivity and specific heat values of LMWNT and SMWNT samples.
| | | LMWNT | SMWNT | | | | | | |
| 25°C | 0.5 wt% | 0.662 | 0.863 | 0.695 | 0.851 | 1.0 wt% | 0.642 | 0.882 | 0.622 | 0.811 | 5.0 wt% | 0.641 | 0.885 | 0.618 | 0.786 | 10.0 wt% | 0.528 | 1.277 | 0.490 | 0.943 |
| 50°C | 0.5 wt% | 0.648 | 1.014 | 0.674 | 0.982 | 1.0 wt% | 0.625 | 1.045 | 0.608 | 0.955 | 5.0 wt% | 0.617 | 1.034 | 0.606 | 0.859 | 10.0 wt% | 0.493 | 1.456 | 0.476 | 1.052 |
| 100°C | 0.5 wt% | 0.615 | 1.120 | 0.638 | 1.246 | 1.0 wt% | 0.592 | 1.156 | 0.575 | 1.209 | 5.0 wt% | 0.582 | 1.136 | 0.572 | 1.014 | 10.0 wt% | 0.464 | 1.614 | 0.444 | 1.199 |
| 200°C | 0.5 wt% | 0.537 | 1.465 | 0.557 | 1.513 | 1.0 wt% | 0.516 | 1.547 | 0.502 | 1.495 | 5.0 wt% | 0.504 | 1.475 | 0.497 | 1.405 | 10.0 wt% | 0.387 | 2.276 | 0.371 | 1.720 |
|
|