Temperature-Driven Spin Reorientation Transition in CoPt/AlN Multilayer Films
Figure 2
In-plane and out-of-plane hysteresis loops of a CoPt/AlN multilayer film with the CoPt layer thickness of 4 nm measured at room temperature (a), 250°C (b), and 350°C (c). The saturation magnetizations () at various temperatures are shown in (d).