Consolidation of Amorphous A l 𝟖 𝟎 F e 𝟏 𝟎 T i 𝟓 N i 𝟓 Powders by Hot Pressing

Figure 3

SEM cross-sectional micrographs of Al-10%Fe-5%Ti-5%Ni powder mixture after different milling times: (a) 0.25 h, (b) 0.5 h, (c) 1 h, (d) 5 h, and (e) 10 h.