Consolidation of Amorphous
A
l
𝟖
𝟎
F
e
𝟏
𝟎
T
i
𝟓
N
i
𝟓
Powders by Hot Pressing
Figure 9
Fracture surface photographs of samples hot pressed under (a) 200 MPa, (b) 300 MPa, (c) 400 MPa, (d) 500 MPa, and (e) 600 MPa pressure at a constant temperature 550°C.