Influence of Metallic Molar Ratio on the Electron Spin Resonance and Thermal Diffusivity of Zn–Al Layered Double Hydroxide

Ahmed, Abdullah Ahmed Ali; Talib, Zainal Abidin; Hussein, Mohd Zobir

doi:https://doi.org/10.1155/2013/639354

Journal of Nanomaterials

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2013 | Article ID 639354 | https://doi.org/10.1155/2013/639354

Influence of Metallic Molar Ratio on the Electron Spin Resonance and Thermal Diffusivity of Zn–Al Layered Double Hydroxide

Abdullah Ahmed Ali Ahmed,^1,2Zainal Abidin Talib,¹and Mohd Zobir Hussein³

Academic Editor: Christian Brosseau

Received25 Jun 2013

Revised06 Aug 2013

Accepted07 Aug 2013

Published12 Sept 2013

Abstract

The coprecipitation method was used to prepare Zn–Al layered double hydroxide (Zn–Al–NO₃-LDH) at pH 7.5 and different Zn²⁺/Al³⁺ molar ratios of 2, 3, 4, 5, and 6. The elemental, structural, and textural properties of prepared samples were studied. The crystallinity of prepared LDH nanostructure decreases as Zn²⁺/Al³⁺ molar ratio increases. The electron spin resonance (ESR) spectroscopy of different LDH samples showed new ESR spectra. These spectra were produced due to the presence of different phases with formed LDH such as ZnO phase and ZnAl₂O₄ spinel. At low Zn²⁺/Al³⁺ molar ratio, the ESR signals were produced from the presence of free nitrate anions in the LDH interlayer. Above Zn²⁺/Al³⁺ = 2, the ESR signals were attributed to the existence of ZnO phase and ZnAl₂O₄ spinel in the samples. Because the nuclear magnetic moment of ⁶⁷Zn is lower than ²⁷Al, the increasing in Zn²⁺/Al³⁺ molar ratio causes a reduction of the magnetic activity of ZnAl₂O₄ spinel. Thermal diffusivity versus in situ temperature showed nonlinear relation for different samples due to the changing in the water content of LDH as temperature increases. The dc conductivity of samples decreased as Zn²⁺/Al³⁺ molar ratio.

1. Introduction

Layered double hydroxides (LDHs), also known as hydrotalcite structure, are a family of lamellar solids. LDHs may be represented by the general formula . and are divalent and trivalent cations, respectively, which are situated at the center of octahedral () units of the brucite-like layers with charge-balancing anions () in the hydrated interlayer regions. is the charge of anions () that lead to the electroneutrality of LDH. The value is defined by , and is the amount of LDH interlayer water molecules [1, 2]. The coprecipitation method is a common method to prepare the LDHs [1, 3, 4] and is done by the mixing of salts of divalent and trivalent cations under certain parameters (such as pH value, stirring, and cations molar ratio).

Electron spin resonance (ESR) spectroscopy is an important tool in research due to its ability to investigate several features of examined samples. The geometry and the arrangement components of intercalated guests into LDH interlayer could be identified using ESR spectroscopy [5, 6]. ESR has also been used to study the electronic structure of metallic centers of a mixed LDH and oxide material to explain its interaction with cations of LDH layers [7]. In a recent study, ESR has been used to investigate the isolation of the sebacate when this material was intercalated into LDH [8]. In our recent observation [9], ESR spectra have been used to explain the effect of temperature treatment on the nature of nitrate anions in LDH interlayer.

Thermal properties (including thermal diffusivity) of clays (soils, sands, LDHs, etc.) are very vital parameters in the heat transfer from or to buildings, in the distribution rate of electric cables and in the design of heating systems [10]. Thermal diffusivity of sands (Utah tar sands) has been measured [11] and had a range of 5 × 10⁻⁷–9 × 10⁻⁷ m² s⁻¹ over the temperature range of 27–147°C using a constant applied heat flux method. Thermal diffusivity of soils has been measured using the line heat source transient method [10] between the temperature –10°C and 35°C. The effect of moisture content up to 40% on diffusivity was also studied. Hinkel [12] has estimated thermal diffusivity of soils from two different regions which was between 1.5 and 2.1 × 10⁻⁷ m² s⁻¹. In our recent paper [9], the effect of in situ temperatures in the range of 27–210°C on thermal diffusivity of Zn–Al–NO₃-LDH has been studied.

In this work, a series of Zn–Al–NO₃-LDH samples were prepared by the coprecipitation method at different Zn²⁺/Al³⁺ molar ratios of (2, 3, 4, 5, and 6) and at constant pH value of 7.5. The structural and textural properties of samples were studied. The effect of Zn²⁺/Al³⁺ molar ratios on ESR spectra and thermal diffusivity of Zn–Al–NO₃-LDHs were obtained.

2. Experimental

2.1. Materials and Preparation of Samples

The starting chemicals of zinc nitrate (Zn(NO₃)₂6H₂O) (Systerm, 98%), aluminum nitrate (Al(NO₃)₃9H₂O) (Hamburg Chemicals Co., 99.4%), and sodium hydroxide (NaOH) (Merck Co., 99%) were used without further purification. Deionized water was used as solvent throughout this study. The preparation of Zn–Al–NO₃-LDH precursors with starting value of molar ratio Zn²⁺/Al³⁺ = 2, 3, 4, 5, and 6 has been carried out using coprecipitation method and has been presented elsewhere [13]. The samples were labeled as ZnrAl-LDH, where r represents the Zn²⁺/Al³⁺ molar ratio.

2.2. Characterizations

Elemental analyses for Zn and Al were measured by inductively coupled plasma emission spectroscopy (ICP) (Perkin-Elmer, Optima 2000 DV) after dissolving the samples in hydrochloric acid. Powder X-ray diffraction (PXRD) patterns of the samples were recorded on a X-ray diffractometer (X’pert-PRO Panalytical) using CuK_α (λ = 1.54187 Å) at 40 kV and 30 mA. The surface areas and pore volumes of the samples were characterized using the nitrogen gas adsorption-desorption technique at 77 K using a Micromeritics ASAP 2000 instrument (Norcross, GA). Electron spin resonance (ESR) spectra were recorded using a JEOL ESR spectrometer (JES-FA200). Thermal diffusivity versus temperature was performed using NETZSCH model LFA 457 MicroFlash. The dielectric measurements of samples have been obtained using novocontrol high resolution dielectric analyzer.

3. Results and Discussion

3.1. Elemental Chemical Analysis

In this section, in addition to ICP analysis, we have used TGA data from our published paper [13] to calculate the chemical formulae of different samples. The chemical compositions of prepared Zn–Al–NO₃-LDH samples at Zn²⁺/Al³⁺ molar ratio of 2, 3, 4, 5, and 6 are listed in Table 1. The experimental Zn²⁺/Al³⁺ molar ratio is close to that in the starting solutions. As seen in Table 1, the formula considers that nitrate is the only compensating anion in the LDH interlayer region. Carbonate impurities do not take into account the possible presence in the interlayer gallery. These results are in good agreement with that reported by Rojas Delgado et al. [14].

3.2. Powder X-Ray Diffraction (PXRD) Study

Figure 1 exhibits the PXRD patterns of Zn–Al–NO₃-LDH precursors with Zn²⁺/Al³⁺ molar ratio of 2, 3, 4, 5, and 6. The characteristic reflections of Zn–Al–NO₃-LDH samples show the different planes which are listed in Table 2. For the samples Zn4Al-LDH, Zn5Al-LDH, and Zn6Al-LDH, the PXRD patterns show the characteristic reflections of ZnO phase and the patterns of ZnAl₂O₄ spinel [15]. The decreasing of PXRD intensity of the LDH peaks was observed as the Zn²⁺/Al³⁺ molar ratio increases. These changes are attributed to the formation of other phases (ZnO phase and ZnAl₂O₄ spinel) with low crystallinity. This caused the distortion of the hydroxide layers networks of the LDH crystal by the larger difference in ionic radii of Zn²⁺ and Al³⁺ [16]. Yan et al. have employed the density functional theory to study the influence of cations ratio on the host layer structure of Zn–Al-LDHs [17]. They have shown that the formation or bonding stability of the corresponding ZnrAl-LDH (r: molar ratio = 2, 3, 4, 5, and 6) clusters decreases with increasing the molar ratio (r). Another study has also demonstrated that the decreasing of Al³⁺ concentration in Zn–Al-LDH solution causes the decreasing of the crystallinity of LDH phase [18]. Our results are in good agreement with all of those literatures which exhibited significant increase in crystallinity of ZnrAl-LDH as Zn²⁺/Al³⁺ molar ratio decreases.

3.3. N₂ Adsorption-Desorption Study

The pore size distribution of the prepared samples was studied using the Barrett-Joyner-Halenda (BJH) method from the desorption branch of the isotherms as shown in Table 2. The observation is supported by the analyses of the pore structure and surface area of the samples. Figure 2 shows the nitrogen adsorption-desorption isotherms of Zn–Al–NO₃-LDH prepared at different Zn²⁺/Al³⁺ molar ratio. All the isotherms are generally Type III-like with a distinct H3 hysteretic loop in the range of 0.2–1.0 P/P₀. These results show the presence of macroporous materials (the volume of pores are greater than 0.05 μm) according to IUPAC classifications [19]. Results from Rojas Delgado et al. on the total layer specific area for Zn–Al–Cl-LDH [14] reflect an increase from 924 m²/g (for Zn²⁺/Al³⁺ molar ratio = 2.4) to 941 m²/g (for Zn²⁺/Al³⁺ molar ratio = 4.8). As seen in Table 2, the BET surface area increases from 0.12 to 8.34 m²/g when Zn²⁺/Al³⁺ molar ratio increases from 2 to 6 due to the increasing of electrostatic repulsion between adjacent trivalent metals in the layers [14, 20]. On the other hand, the BJH average pore diameter has the opposite behavior of BET surface area with the highest value of 18.86 μm at Zn²⁺/Al³⁺ molar ratio of 2.

(a)

(b)

(c)

(d)

(e)

3.4. Electron Spin Resonance (ESR) Spectra

New ESR spectra of the LDH samples exhibit signal with different intensities and sharpness at room temperature as shown in Figure 3. For Zn2Al-LDH, a broad and weak signal with a g-factor = 2.01105 is observed, which is attributed to the interaction between nitrate anions from the interlayer region and a close aluminum nucleus () from the LDH sheets. This signal is characteristic of ions with D_3h symmetry in the LDH interlayer [21]. As seen in our recent paper [13], the FT-IR results showed that the LDH interlayer anions existed with a D_3h symmetry. There is also a possibility that this signal is due to a weak interaction of the free electron of radical with the nuclear magnetic moment of protons of the water matrix in LDH interlayer [22]. Two signals with stronger intensity begin to appear for samples at Zn²⁺/Al³⁺ molar ratio of 3 and above; the first one with a g-factor = 2.18870 is attributed to the formation of ZnAl₂O₄ spinel, while the second signal with a g-factor = 1.93337 is ascribed to the existence of ZnO phase in the samples.

In ZnAl₂O₄, the most probable centers that can be observed are the V centers (a hole trapped in a cation vacancy) and F⁺ centers (an electron trapped in an anion vacancy) [23]. The signal of ZnAl₂O₄ is due to the presence of an interaction between the oxygen vacancies of ZnAl₂O₄ and the aluminium nucleus . For the ZnO signal, the oxygen vacancies on the ZnO surface are responsible for the generation of the ESR signals. The Zn⁺ ion, which has a 4s¹ orbital, will also appear on the ZnO surface and produces a parametric signal [24].

As seen in Figure 4, the evolution of the normalized ESR intensity against Zn²⁺/Al³⁺ molar ratio for ZnO phase and ZnAl₂O₄ spinel is plotted. The relative intensity of samples increases until Zn²⁺/Al³⁺ molar ratio = 5 which has the highest ESR intensity for ZnO phase, and then it starts to decrease. For the ZnAl₂O₄ spinel, the highest ESR intensity was at Zn²⁺/Al³⁺ molar ratio = 4. Aluminum and zinc cations in ZnAl₂O₄ have isotopes with nuclear spin of 5/2: ²⁷Al and ⁶⁷Zn. ²⁷Al is much more abundant (100%) than ⁶⁷Zn (4.11%), and its nuclear magnetic moment is higher (3.6385) than that of ⁶⁷Zn (0.8753) [25]. The increase in Zn²⁺/Al³⁺ molar ratio causes a reducing of the magnetic activity of ZnAl₂O₄ because the nuclear magnetic moment of ⁶⁷Zn is lower than ²⁷Al. On the other hand, for ZnO phase, the magnetic activity increases which may be attributed to the increase in parametric of oxygen in the excess of Zn cations of LDH. The rapidly drop in the intensity of ZnO and stability of ZnAl₂O₄ may refer to the low crystallinity of whole system due to the distortion of the hydroxide layers networks of the LDH crystal as seen in PXRD results.

3.5. Thermal Diffusivity

Thermal diffusivity () measures the ability of a material to conduct thermal energy relative to its ability to store thermal energy. The relation between thermal diffusivity (under transient conditions) and thermal conductivity () (under steady-state conditions) described the heat transport in materials using the following equation [26]: where is the specific heat capacity and is the density.

In this work, LFA-457 NETSCH equipment has been used to measure the thermal diffusivity. The setup consists of a laser source which radiates a short-time energy pulse that strikes the front of the cylindrical sample (diameter 10 mm and thick between 1 and 2 mm). The transient temperature at the opposite side, which increases over time, is measured by infrared detector triggered simultaneously with laser beam. The mathematical thermal model of the experiment is represented by differential equation whose solution of this equation can be expressed as where is the thickness of the sample and is the highest temperature at the rear surface of sample. The mathematical analysis of the temperature versus time plot by (2) enables one to determine the thermal diffusivity as the following [27]: where is the time corresponding to 50% of the increase in the temperature measured on the opposite surface of the sample.

Figure 5 shows a nonlinear relation of thermal diffusivity versus in situ temperatures for Zn–Al-LDH at different Zn²⁺/Al³⁺ molar ratios. The values of thermal diffusivity for samples were found between 2.4 and 3.3 × 10⁻⁷ m² s⁻¹ which are close to the values that have been reported [9, 28]. For Zn2Al-LDH, the thermal diffusivity is almost constant as temperature increases until around 150°C. Above 150°C, the values of thermal diffusivity drop rapidly as temperature increases because the water molecules start to release from LDH. The thermal diffusivity of this sample in this temperature range may be attributed to the high crystallinity of Zn2Al-LDH, and this sample is almost free from other phases as shown in PXRD results.

From TGA results [13], water molecules were completely removed and LDH starts to collapse at 180°C and above. For the samples Zn3Al-LDH, Zn4Al-LDH, Zn5Al-LDH, and Zn6Al-LDH, in general, the behavior of thermal diffusivity increases as in situ temperature increases until around 180°C and then drops rapidly as temperature increases. Thus thermal behavior in this range is strongly influenced by the water content in LDH [29]. Above 180°C, ZnO phase is purely responsible for the decrease in the thermal diffusivity [9].

Figure 6 shows a nonlinear relation of the thermal diffusivity as a function of Zn²⁺/Al³⁺ molar ratio of LDH for all measured temperatures. The thermal diffusivity decreases as the molar ratio increases which can be attributed to the presence of ZnO and ZnAl₂O₄ phases. At temperature 210°C, the behavior is different due to the collapse of LDH structure [30, 31]. In addition to the decrease in the crystallinity as Zn²⁺/Al³⁺ molar ratio increases, the presence of Zn–O and Al–O in an octahedral coordination state in LDH brucite-like sheet causes decreasing of thermal conductivity as temperature increases which may result from the random disorder phonon scattering induced by the Al deficient sites [32].

3.6. The Dc Conductivity

The dc conductivity or ionic conductivity () can be calculated using the Jonscher power law [33]: where is the preexponential factor and the value of is between 0 and 1 for this material. The equation (4) has been used to fit the experimental data of real part of conductivity which were presented in the previous work [13] as shown in Figure 7. The solid line denotes the fit to power law expression of data, and the values (, , and ) can be achieved using Origin nonlinear curve fitting software and listed in Table 3. The disagreement in the fit curves with experimental data at low frequency was attributed to the polarization effect of the electrode.

(a)

(b)

(c)

(d)

(e)

The obtained values from the fit curves for all samples were plotted against Zn²⁺/Al³⁺ molar ratio as shown in Figure 8. This relation illustrated that dc conductivity decreased exponentially with the increase in the Zn²⁺/Al³⁺ molar ratio of the prepared samples. This may suggest that the dc conductivity decreased due to the decrease in the crystallinity of samples as shown in PXRD results.

4. Conclusions

Powder XRD results showed that the crystallinity of Zn–Al–NO₃-LDH phase decreased as Zn²⁺/Al³⁺ molar ratio increases due to the distortion of the hydroxide layers networks by the larger difference in ionic radii of Zn²⁺ and Al³⁺. Other phases of ZnO and ZnAl₂O₄ were formed for LDH with Zn²⁺/Al³⁺ molar ratio above 2. The prepared LDH samples were macroporous materials due to their volume diameter of pores which was found between 0.28 and 18.86 μm. The characteristic ESR signal of ions with D_3h symmetry in the LDH interlayer was obtained due to the interaction between nitrate anions from the interlayer region and a close aluminum nucleus in brucite-like layer of LDH. At Zn²⁺/Al³⁺ molar ratio of 3 and above, two ESR signals with stronger intensity were produced due to the formation of ZnAl₂O₄ and ZnO phases in LDH samples. Thermal diffusivity of LDH samples was found between 2.4 and 3.3 × 10⁻⁷ m² s⁻¹. The nonlinear behavior of thermal diffusivity against the examined in situ temperature is attributed to the presence of water molecules in the LDH below 180°C. The dc conductivity which found from the fit curves of experimental data decreased as Zn²⁺/Al³⁺ molar ratio increased which may be attributed to the decrease in the crystallinity of samples.

Conflict of Interests

The authors declare that they have no conflict of interests in this work.

Acknowledgments

This study was financed by ERGS/1/11/STG/UPM/02/4 (Postdoctoral Grant). Authors would like to thank Universiti Putra Malaysia (UPM) for supporting this work. A. A. A. Ahmed thanks RMC-UPM and Thamar University, Yemen, for the support.

References

F. Cavani, F. Trifirò, and A. Vaccari, “Hydrotalcite-type anionic clays: preparation, properties and applications,” Catalysis Today, vol. 11, no. 2, pp. 173–301, 1991.
View at: Publisher Site | Google Scholar
D. Evans and R. Slade, in Layered Double Hydroxides, X. Duan and D. G. Evans, Eds., vol. 119, p. 1, Springer, Berlin, Germany, 2006.
S. Jin, P. H. Fallgren, J. M. Morris, and Q. Chen, “Removal of bacteria and viruses from waters using layered double hydroxide nanocomposites,” Science and Technology of Advanced Materials, vol. 8, pp. 67–70, 2007.
View at: Google Scholar
H. Tamura, J. Chiba, M. Ito, T. Takeda, and S. Kikkawa, “Synthesis and characterization of hydrotalcite-ATP intercalates,” Solid State Ionics, vol. 172, no. 1–4, pp. 607–609, 2004.
View at: Publisher Site | Google Scholar
J. Tronto, F. Leroux, M. Dubois, J. F. Borin, C. F. de Oliveira Graeff, and J. B. Valim, “Hyperfine interaction in Zn-Al layered double hydroxides intercalated with conducting polymers,” Journal of Physics and Chemistry of Solids, vol. 69, no. 5-6, pp. 1079–1083, 2008.
View at: Publisher Site | Google Scholar
J. Tronto, F. Leroux, M. Dubois et al., “New layered double hydroxides intercalated with substituted pyrroles. 2. 3-(pyrrol-1-yl)-propanoate and 7-(pyrrol-1-yl)-heptanoate LDHs,” Journal of Physics and Chemistry of Solids, vol. 67, no. 5-6, pp. 973–977, 2006.
View at: Publisher Site | Google Scholar
K. Bahranowski, R. Dula, F. Kooli, and E. M. Serwicka, “ESR study of the thermal decomposition of V-containing layered double hydroxides,” Colloids and Surfaces A, vol. 158, no. 1-2, pp. 129–136, 1999.
View at: Publisher Site | Google Scholar
G. Abellán, E. Coronado, C. J. Gómez-García, C. Martí-Gastaldo, and A. Ribera, “Intercalation of cobalt(II)-tetraphenylporphine tetrasulfonate complex in magnetic NiFe-layered double hydroxide,” Polyhedron, vol. 52, pp. 216–221, 2013.
View at: Google Scholar
A. A. Ali Ahmed, Z. Abidin Talib, and M. Z. B. Hussein, “ESR spectra and thermal diffusivity of ZnAl layered double hydroxide,” Journal of Physics and Chemistry of Solids, vol. 73, no. 1, pp. 124–128, 2012.
View at: Publisher Site | Google Scholar
M. M. Sorour, M. M. Saleh, and R. A. Mahmoud, “Thermal conductivity and diffusivity of soil,” International Communications in Heat and Mass Transfer, vol. 17, no. 2, pp. 189–199, 1990.
View at: Google Scholar
W. R. Lindberg, R. R. Thomas, and R. J. Christensen, “Measurements of specific heat, thermal conductivity and thermal diffusivity of Utah tar sands,” Fuel, vol. 64, no. 1, pp. 80–85, 1985.
View at: Google Scholar
K. M. Hinkel, “Estimating seasonal values of thermal diffusivity in thawed and frozen soils using temperature time series,” Cold Regions Science and Technology, vol. 26, no. 1, pp. 1–15, 1997.
View at: Google Scholar
A. A. A. Ahmed, Z. A. Talib, M. Z. bin Hussein, and A. Zakaria, “Zn-Al layered double hydroxide prepared at different molar ratios: preparation, characterization, optical and dielectric properties,” Journal of Solid State Chemistry, vol. 191, pp. 271–278, 2012.
View at: Publisher Site | Google Scholar
R. Rojas Delgado, C. P. De Pauli, C. B. Carrasco, and M. J. Avena, “Influence of MII/MIII ratio in surface-charging behavior of Zn-Al layered double hydroxides,” Applied Clay Science, vol. 40, no. 1–4, pp. 27–37, 2008.
View at: Publisher Site | Google Scholar
D. Carriazo, M. del Arco, E. García-López et al., “Zn,Al hydrotalcites calcined at different temperatures: preparation, characterization and photocatalytic activity in gas–solid regime,” Journal of Molecular Catalysis A, vol. 342-343, pp. 83–90, 2011.
View at: Publisher Site | Google Scholar
T. Ishikawa, K. Matsumoto, K. Kandori, and T. Nakayama, “Synthesis of layered zinc hydroxide chlorides in the presence of Al(III),” Journal of Solid State Chemistry, vol. 179, no. 4, pp. 1110–1118, 2006.
View at: Publisher Site | Google Scholar
K. Dutta, S. Das, and A. Pramanik, “Concomitant synthesis of highly crystalline Zn-Al layered double hydroxide and ZnO: phase interconversion and enhanced photocatalytic activity,” Journal of Colloid and Interface Science, vol. 366, no. 1, pp. 28–36, 2012.
View at: Publisher Site | Google Scholar
H. Yan, M. Wei, J. Ma, and X. Duan, “Density functional theory study on the influence of cation ratio on the host layer structure of Zn/Al double hydroxides,” Particuology, vol. 8, no. 3, pp. 212–220, 2010.
View at: Publisher Site | Google Scholar
K. S. W. Sing, D. H. Everett, R. A. W. Haul et al., “Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity,” Pure and Applied Chemistry, vol. 57, no. 4, pp. 603–619, 1985.
View at: Publisher Site | Google Scholar
M. Shao, J. Han, M. Wei, D. G. Evans, and X. Duan, “The synthesis of hierarchical Zn–Ti layered double hydroxide for efficient visible-light photocatalysis,” Chemical Engineering Journal, vol. 168, no. 2, pp. 519–524, 2011.
View at: Publisher Site | Google Scholar
S. I. Bannov and V. A. Nevostruev, “Formation and properties of NO₃²⁻, NO₃ and ONOO radicals in nitrate-containing matrices,” Radiation Physics and Chemistry, vol. 68, no. 5, pp. 917–924, 2003.
View at: Publisher Site | Google Scholar
R. P. Wayne, I. Barnes, P. Biggs et al., “The nitrate radical: physics, chemistry, and the atmosphere,” Atmospheric Environment A, vol. 25, no. 1, pp. 1–203, 1991.
View at: Google Scholar
S. Menon, B. Dhabekar, E. Alagu Raja, S. P. More, T. K. Gundu Rao, and R. K. Kher, “TSL, OSL and ESR studies in ZnAl₂O₄:Tb phosphor,” Journal of Luminescence, vol. 128, no. 10, pp. 1673–1678, 2008.
View at: Publisher Site | Google Scholar
B. Yu, C. Zhu, F. Gan, and Y. Huang, “Electron spin resonance properties of ZnO microcrystallites,” Materials Letters, vol. 33, no. 5-6, pp. 247–250, 1998.
View at: Publisher Site | Google Scholar
R. C. Weast, Handbook of Chemistry and Physics, CRC Press, Cleveland, Ohio, USA, 1971.
M. Boutinguiza, F. Lusquiños, J. Pou, R. Soto, F. Quintero, and R. Comesaña, “Thermal properties measurement of slate using laser flash method,” Optics and Laser in Engineering, vol. 50, no. 5, pp. 727–730, 2012.
View at: Publisher Site | Google Scholar
H. S. Carslaw and J. C. Jaeger, Conduction of Heat in Solids, Clarendon Press, Oxford, UK, 1959.
W. M. M. Yunus, M. Ranjbar, M. Z. B. Hussein, and L. M. Yee, “Thermal diffusivity of zinc-aluminum layered double hydroxide using PVDF photoflash technique,” Journal of Materials Science and Engineering, vol. 4, p. 7, 2010.
View at: Google Scholar
M. H. Sharqawy, “New correlations for seawater and pure water thermal conductivity at different temperatures and salinities,” Desalination, vol. 313, pp. 97–104, 2013.
View at: Google Scholar
X. Cheng, X. Huang, X. Wang, and D. Sun, “Influence of calcination on the adsorptive removal of phosphate by Zn-Al layered double hydroxides from excess sludge liquor,” Journal of Hazardous Materials, vol. 177, no. 1–3, pp. 516–523, 2010.
View at: Publisher Site | Google Scholar
M. Z. B. Hussein, T.-Y. Yun-Hin, M. M. B. Tawang, and R. Shahadan, “Thermal degradation of (zinc-aluminium-layered double hydroxide-dioctyl sulphosuccinate) nanocomposite,” Materials Chemistry and Physics, vol. 74, no. 3, pp. 265–271, 2002.
View at: Publisher Site | Google Scholar
X. Qu, D. Jia, and S. Lv, “Thermoelectric properties and electronic structure of Al-doped ZnO,” Solid State Communications, vol. 151, no. 4, pp. 332–336, 2011.
View at: Publisher Site | Google Scholar
A. K. Jonscher, Dielectric Relaxation in Solids, Chelsea Dielectrics Press, London, UK, 1983.

Copyright

Copyright © 2013 Abdullah Ahmed Ali Ahmed et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1486

Downloads

1272

Citations

Journal of Nanomaterials

Influence of Metallic Molar Ratio on the Electron Spin Resonance and Thermal Diffusivity of Zn–Al Layered Double Hydroxide

Abstract

1. Introduction

2. Experimental

2.1. Materials and Preparation of Samples

2.2. Characterizations

3. Results and Discussion

3.1. Elemental Chemical Analysis

3.2. Powder X-Ray Diffraction (PXRD) Study

3.3. N2 Adsorption-Desorption Study

3.4. Electron Spin Resonance (ESR) Spectra

3.5. Thermal Diffusivity

3.6. The Dc Conductivity

4. Conclusions

Conflict of Interests

Acknowledgments

References

Copyright

3.3. N₂ Adsorption-Desorption Study