Influence of Metallic Molar Ratio on the Electron Spin Resonance and Thermal Diffusivity of Zn–Al Layered Double Hydroxide
Table 1
Elemental chemical analysis data and interlayer water content of Zn-Al-NO3-LDH samples and their calculated formulae using ICP analysis.
| Sample | % Zn | % Al | % H2Oa | | Chemical formulae |
| Zn2Al-LDH | 38.67 | 7.73 | 7.38 | 2.06 | Zn0.67Al0.33(OH)2(NO3)0.33·0.47H2O | Zn3Al-LDH | 42.98 | 6.06 | 7.18 | 2.93 | Zn0.75Al0.25(OH)2(NO3)0.25·0.45H2O | Zn4Al-LDH | 49.74 | 5.17 | 6.02 | 3.97 | Zn0.80Al0.20(OH)2(NO3)0.20·0.37H2O | Zn5Al-LDH | 51.18 | 4.26 | 5.89 | 4.95 | Zn0.83Al0.17(OH)2(NO3)0.17·0.36H2O | Zn6Al-LDH | 50.01 | 3.72 | 6.26 | 5.54 | Zn0.85Al0.15(OH)2(NO3)0.15·0.38H2O |
|
|
These results were obtained by TGA data from our work [13].
|