Fabrication of Aligned Carbon Nanotube/Polycaprolactone/Gelatin Nanofibrous Matrices for Schwann Cell Immobilization
Table 1
Sample notation, electrospinning parameters, and average diameters of random PG and PGC nanofibers.
| sample notation | Polycaprolactone concentration (mg/mL) | Gelatin concentration (mg/mL) | Carbon nanotube concentration (mg/mL) | Electrospinning parameters (applied voltage, working distance, and flow rate) | Average diameter ± standard deviation (nm) |
| PG | 42.55 | 42.55 | 0 | 15 kV, 15 cm, 3.81 mL/hour | | PG3C | 42.55 | 42.55 | 3.54 | 15 kV, 15 cm, 3.81 mL/hour | | PG5C | 42.55 | 42.55 | 4.47 | 15 kV, 15 cm, 3.81 mL/hour | |
|
|