Fabrication of Aligned Carbon Nanotube/Polycaprolactone/Gelatin Nanofibrous Matrices for Schwann Cell Immobilization
Table 2
Sample notation, electrospinning parameters, average diameters, and angular distributions of aligned PG and PGC nanofibers.
| Sample notation | Polycaprolactone concentration (mg/mL) | Gelatin concentration (mg/mL) | Carbon nanotube concentration (mg/mL) | Electrospinning parameters (applied voltage, working distance, and flow rate) | Average diameter ± standard deviation (nm) | Angular distribution of aligned nanofibers (full width at half maximum, degrees) |
| PG | 42.55 | 42.55 | 0 | 15 kV, 15 cm, 0.51 mL/hour | | 26 | PG3C | 42.55 | 42.55 | 3.54 | 20 kV, 15 cm, 0.76 mL/hour | | 21 | PG5C | 42.55 | 42.55 | 4.47 | 20 kV, 10 cm, 6.36 mL/hour | | 43 |
|
|