Journal of Nanomaterials / 2015 / Article / Tab 1 / Research Article
Easy Formation of Nanodisk-Dendritic ZnO Film via Controlled Electrodeposition Process Table 1 The different types of hexagonal ZnO disk based on preparation method.
Researcher Preparation methods Findings References Yin et al. (2014) Simple double-solvothermal method in the presence of glycine Complex superstructure was assembled by hexagonal disks; the thickness of the disk is about 300 nm [25 ] Zeng et al. (2009) Hydrothermal methodUniform single-crystalline ZnO nanodisks were well developed with 1.5 m in diameter and 300 nm in thickness [17 ] Zhang et al. (2007) Electrodeposition method, HBO3 as an electrolyte with zinc foil as anode, voltage 180 V, and the system kept at 2°CZinc/ZnO core-shell hexagonal nanodisk dendrites were produced with diameter from about 100 nm to several hundred nanometers and thicknesses are about 20–40 nm. [15 ] Li et al. (2007) Electrochemical deposition methodThe shape of the ZnO dendritic structure is similar to the branch of a fern; ZnO dendritic structure is in the range of 6–10 m and 200 nm of thickness [26 ] Xu et al. (2004) Vapour phase transport (VPT) methodZinc oxide nanodisk; 3 m in diagonal and 300 nm in thickness [21 ]