Statistical Study of the Effects of the Composition on the Oxidation Resistance of Ni-Based Superalloys
Table 2
Results of regression analysis for mass gain after oxidation tests (
= 0.07235,
-square = 87.5%, and
-square (adjusted) = 70.7%).
| Term | Coefficient | SE coefficient | | |
| Constant | 1.09641 | 0.398121 | 2.754 | 0.011 | Co | −0.00155 | 0.016121 | −0.096 | 0.924 | Cr | −0.03997 | 0.043708 | −0.914 | 0.369 | Mo | −0.02271 | 0.048362 | −0.47 | 0.643 | W | −0.04579 | 0.024181 | −1.894 | 0.069 | Al | −0.12666 | 0.053758 | −2.356 | 0.026 | Ti | 0.02162 | 0.048362 | 0.447 | 0.659 | Ta | −0.01862 | 0.024181 | −0.77 | 0.448 | CoCo | 0.00048 | 0.00035 | 1.373 | 0.181 | CrCr | 0.0011 | 0.001608 | 0.687 | 0.498 | MoMo | −0.00319 | 0.003151 | −1.011 | 0.321 | WW | −0.00024 | 0.000788 | −0.307 | 0.761 | AlAl | 0.00677 | 0.003151 | 2.15 | 0.041 | TiTi | 0.00448 | 0.003151 | 1.422 | 0.167 | TaTa | 0.00083 | 0.000788 | 1.055 | 0.301 | CoCr | −0.00002 | 0.000974 | −0.021 | 0.983 | CoMo | 0.00024 | 0.001364 | 0.174 | 0.864 | CoW | 0.00079 | 0.000682 | 1.153 | 0.26 | CoAl | −0.00037 | 0.001364 | −0.271 | 0.789 | CoTi | −0.00016 | 0.001364 | −0.12 | 0.905 | CoTa | −0.00156 | 0.000682 | −2.293 | 0.03 | CrMo | 0.00168 | 0.002923 | 0.574 | 0.571 | CrW | 0.00451 | 0.001462 | 3.086 | 0.005 | CrAl | −0.00141 | 0.002923 | −0.482 | 0.634 | CrTi | 0.0027 | 0.002923 | 0.924 | 0.364 | CrTa | −0.00125 | 0.001462 | −0.858 | 0.399 | MoW | 0.00152 | 0.002046 | 0.741 | 0.465 | MoAl | 0.00558 | 0.004093 | 1.363 | 0.185 | MoTi | 0.00346 | 0.004093 | 0.845 | 0.406 | MoTa | −0.00237 | 0.002046 | −1.16 | 0.257 | WAl | −0.0005 | 0.002046 | −0.244 | 0.809 | WTi | −0.00199 | 0.002046 | −0.971 | 0.341 | WTa | −0.00076 | 0.001023 | −0.742 | 0.465 | AlTi | −0.0071 | 0.004093 | −1.734 | 0.095 | AlTa | 0.00575 | 0.002046 | 2.808 | 0.009 | TiTa | 0.00068 | 0.002046 | 0.331 | 0.743 |
|
|