Research Article
Dielectric Properties of Paper Made from Pulps Loaded with Ferroelectric Particles
Table 4
Ceramic rate/paper porosity.
| Agave | Halfa | Pennisetum | Junc | Typha | Kraft | TMP | % | | % | | % | | % | | % | | % | | % | |
| SrTiO3 (%: ceramic loading; : porosity⋅10−3 mL/min) | 15.3 | 6.2 | 11.3 | 26.9 | 9.7 | 12.9 | 7.9 | 14.3 | 9.8 | 1.4 | 7.7 | 13.5 | 11.8 | 10.2 | 20.4 | 11.4 | 19.8 | 33.6 | 21.4 | 13.15 | 21.5 | 13.13 | 21.7 | 2.1 | 17.9 | 13.3 | 19.9 | 10.2 | 27.7 | 11.6 | 24.7 | 25.7 | 31.1 | 13.3 | 28.6 | 13.5 | 24.5 | 3.9 | 27.5 | 13.5 | 27.1 | 11.7 | 35.7 | 11.6 | 37.3 | 26.7 | 37.9 | 13.4 | 38.4 | 15.1 | 41.0 | 4.5 | 33.2 | 14.2 | 31.4 | 11.5 |
| BaTiO3 (%: ceramic loading; : porosity⋅10−3 mL/min) | 12.6 | 8.1 | 9.2 | 36.4 | 11.5 | 13.8 | 10.2 | 12.8 | 11.8 | 1.1 | 8.5 | 13.9 | 7.5 | 7.5 | 18.7 | 9.2 | 18.2 | 29.1 | 18.6 | 13.6 | 20.1 | 13.6 | 22.2 | 1.7 | 15.5 | 13.1 | 19.4 | 8.1 | 29.5 | 10.0 | 24.1 | 26.3 | 27.0 | 14.2 | 27.3 | 14.3 | 22.7 | 1.9 | 22.8 | 14.0 | 27.1 | 8.4 | 35.4 | 11.6 | 31.2 | 22.7 | 32.1 | 13.5 | 37.6 | 14.0 | 38.1 | 2.5 | 30.5 | 13.2 | 33.0 | 6.4 |
|
|