Tensile Behavior of Carbon Fiber-Reinforced Polymer Composites Incorporating Nanomaterials after Exposure to Elevated Temperature
Table 1
Geometry and properties of nanomaterials.
| Nanomaterials | Carbon purity (wt.%) | Sizes |
| Multiwalled carbon nanotubes (MWCNTs) | >95 | Outside diameter: 10–20 nm | Inside diameter: 5–10 nm | Length: 10–30 μm | Specific surface | Density: 2.1 g/cm3 |
| Graphene nanoplatelets (GnPs) | >90 | Average number of | Median size (diameter): 5–7 μm | Density: 2.25 g/cm3 |
| Short multiwalled carbon nanotubes functionalized COOH (S-MWCNT-COOH) | >90 | Outside diameter: 30–50 nm | Inside diameter: 5–12 nm | Length: 0.5–2 μm | Specific surface | Density: 2.1 g/cm3 |
|
|