Recent Progress in Dye-Sensitized Solar Cells for Improving Efficiency: TiO<sub>2</sub> Nanotube Arrays in Active Layer

Rho, Won-Yeop; Jeon, Hojin; Kim, Ho-Sub; Chung, Woo-Jae; Suh, Jung Sang; Jun, Bong-Hyun

doi:https://doi.org/10.1155/2015/247689

Journal of Nanomaterials

On this page

Abstract Introduction Conclusions References Copyright Related Articles

Review Article | Open Access

Volume 2015 | Article ID 247689 | https://doi.org/10.1155/2015/247689

Recent Progress in Dye-Sensitized Solar Cells for Improving Efficiency: TiO₂ Nanotube Arrays in Active Layer

Won-Yeop Rho,¹Hojin Jeon,²Ho-Sub Kim,³Woo-Jae Chung,⁴Jung Sang Suh,³and Bong-Hyun Jun¹

Academic Editor: Nageh K. Allam

Received31 Dec 2014

Revised21 Feb 2015

Accepted01 Mar 2015

Published30 Mar 2015

Abstract

Dye-sensitized solar cells (DSSCs) have been widely studied due to several advantages, such as low cost-to-performance ratio, low cost of fabrication, functionality at wide angles and low intensities of incident light, mechanical robustness, and low weight. This paper summarizes the recent progress in DSSC technology for improving efficiency, focusing on the active layer in the photoanode, with a part of the DSSC consisting of dyes and a TiO₂ film layer. In particular, this review highlights a huge pool of studies that report improvements in the efficiency of DSSCs using TiO₂ nanotubes, which exhibit better electron transport. Finally, this paper suggests opportunities for future research.

1. Introduction

For nearly two centuries, mankind has employed fossil fuels as the primary energy source, and now we are facing serious problems as a result. Excessive emission of carbon dioxide and other greenhouse gases leads to environmental risk [1]. The price of fossil fuels continues to rise because of the increasing worldwide energy consumption. The need for an affordable, sustainable, and carbon-free renewable energy source is greater than ever, as the rapid growth rate of renewable energy consumption suggests [2, 3].

Amongst all the renewable energy sources, solar energy has been regarded as very promising due to the abundance of its resource—sunlight—and the fact that it yields no harmful byproducts. The amount of solar energy that radiates upon earth in one hour is equivalent to the annual energy need of mankind [4]. Such high energy output, however, has not been achieved due to thermodynamic and technical constraints as well as few other reasons. Conventional commercial solar cells, which use crystalline and polycrystalline silicon, achieve over 20% energy conversion efficiency for residential end users [5]. However, there are some problems, such as complicated and difficult fabrication processing and high cost [6].

Dye-sensitized solar cells (DSSCs) are one potential alternative to silicon solar cells. DSSCs separate the light absorption and charge transfer processes, unlike Si-based cells. The organic dyes, or sensitizer molecules, adsorbed on the surface of the metal oxide nanostructure take the role of absorbing the incoming light, and the rest of the structure transfers the generated charge. An early version of a DSSC fabricated by O’Regan and Grätzel used ruthenium-based dye and 10-μm-thick porous TiO₂ nanoparticle films for the photoelectrode [7]. The cell yielded 7% power conversion efficiency (PCE), which was high enough to motivate further research on cells with similar structures. DSSCs provide several advantages, such as low price-to-performance ratio, low processing cost, ability to work at wide angles and low intensities of incident light, mechanical robustness, light weight, and aesthetically appealing transparent design. DSSCs have a number of remarkable properties that allow them to be used for several niche applications; they are low in weight and able to display various colors and transparency, and they work effectively in a broad range of wavelengths [8, 9]. However, there are still several weaknesses that require improvement, such as relatively low efficiency, high cost of the ruthenium dyes, conducting glass, and platinum, temperature stability problems, and low scalability. Among the various potential solutions, some of the most widely investigated ones are the development of new sensitizers to cover a broader solar spectrum and the fabrication of new photoanode structures with enhanced light utilization. Studies have reported several different methods to improve the efficiency of DSSCs, such as the use of panchromatic sensitizers or 3-dimensional metal oxide nanostructures [10–14]. This review highlights another huge pool of studies that report improvements in the efficiency of DSSCs, especially those that employ the use of TiO₂ nanotubes. Moreover, we will introduce recent papers on high PCEs and the use of TiO₂ nanotube arrays in DSSCs. These papers describe the use of the space in TiO₂ nanotube array channels and how to overcome the barrier layer that exists at the bottom of these arrays to achieve a high PCE in DSSCs.

2. Principle of DSSCs

A DSSC consists of a photoelectrode, counter electrode, and electrolyte. The photoelectrode is made up of a transparent conductive oxide (TCO) glass substrate, a metal oxide such as mesoporous TiO₂ nanoparticles and a sensitizer such as ruthenium- (Ru-) complex dye. The electrolyte consists of a redox couple and diffusing reducing/oxidizing agent ions, and the counter electrode is coated with Pt as shown in Figure 1(a). In general, fluorine-doped tin oxide (FTO) glass is used on DSSCs instead of indium tin oxide (ITO) glass because of the better thermal stability at high temperatures [15]. During the sintering at 450–500°C, which crystallizes the mesoporous TiO₂ nanoparticles, the sheet resistance of ITO increases and affects the energy conversion efficiency of the DSSCs. However, the sheet resistance of FTO is independent of the temperature up to 500°C, which makes it favorable for applications that utilize the sintering step. TiO₂ nanoparticles are primarily used as electron acceptors on DSSCs that incorporate ruthenium dye. The counter electrode consists of FTO glass coated with platinum (Pt) or carbon to resist the oxidation and to work as a catalyst during the redox reaction in the electrolyte.

(a)

(b)

(c)

(d)

The principle of DSSCs is shown in Figure 1(b). When sensitizers absorb the light energy, and electrons are generated by the sensitizers and are transferred to the metal oxide films. During the hopping process in the metal oxide films, the generated electrons are transferred to the TCO and circulated. After the circulation, the sensitizers are reduced by an iodide redox process. In general, a Ru-complex dye is used as the sensitizer, and TiO₂ nanoparticles are used as the electron acceptors on DSSCs due to their high efficiency [20–22].

The energy diagram shown in Figure 1(c) demonstrates the electron transfer process of DSSCs. When the Ru-complex dyes absorb the light, the electrons change from the ground state to the excited state within a time on the order of nanoseconds (ns), as shown in the reaction (Figure 1(c)-(1)): Although the detailed mechanism of the injection process is under debate, the electron injection from the Ru-complex dye into the conduction band of mesoporous TiO₂ nanoparticles takes about a femtosecond (fs) following the reaction shown in Figure 1(c)-(2). The energy level of electrons in the Ru-complex dye is higher than that of the conduction band of mesoporous TiO₂ nanoparticles, which enables the transfer of electrons into the mesoporous TiO₂ nanoparticles: The excited state of the Ru-complex dye lasts around 20–60 ns, which is long enough for kinetic competition between electron injection and excited state decay in the Ru-complex dye.

The electrons injected into TiO₂ nanoparticles diffuse through mesoporous TiO₂ nanoparticles in about a millisecond (ms) in the reaction shown in Figure 1(c)-(3). However, when the injected electrons are trapped on mesoporous TiO₂ nanoparticles, they return to the oxidized Ru-complex dye by the reaction shown in Figure 1(c)-(4) or reduce the triiodide by the reaction shown in Figure 1(c)-(5). These processes are called as the recombination: The Ru-complex dye is reduced by an iodide ion to accept the electron, as shown in the reaction in Figure 1(c)-(6):The injected electrons on TiO₂ nanoparticles drive the external circuit and perform work, as in the reaction shown in Figure 1(c)-(7).

When the triiodide ion reduces to iodide to accept the electrons from the counter electrode by the reaction shown in Figure 1(c)-(8), the iodide ion causes the electron in the Ru-complex dye to return to the ground state, with the reaction shown in Figure 1(c)-(6).

Figure 1(d) illustrates the performance of DSSCs, and the solar power () can be calculated by the equation:The energy conversion efficiency of DSSCs is described by the ratio of the maximum electrical power output to the solar energy input . The maximum electrical power output is calculated by the maximum current and the maximum voltage : The solar power input is taken as the product of the irradiance of the incident light that is measured in W/m²: The fill factor is a measure of the quality of the solar cell, and it can be calculated by comparing the maximum short-circuit current and maximum open-circuit voltage to the maximum current and maximum voltage : (100 mW/cm²) is the solar cell testing standard under terrestrial conditions with air mass AM1.5.

The ideal power density of DSSCs is the product of and . The maximum power density is the product of and , and the difference between the two comes from the resistances of the cell, electrolyte, electrode, and other components. The energy conversion efficiency of DSSCs is related to the ideal power density and maximum power density as shown in Figure 2(a). When the fill factor is equal to 1, and are the same as and . The series resistance includes the cell, electrolyte, electrode, and interface resistance. The increasing means that electrons are lost, so the voltage decreases earlier as shown in Figure 2(b). The shunt resistance results from the recombination of electrons that are transferred in another way or are trapped by something. The decreasing means that there are few recombination sites, so the electrons are transferred to each layer as shown in Figure 2(c).

(a)

(b)

(c)

3. Dye

The dyes commonly used for DSSC applications share certain characteristics [23]: (i) excellent spectral absorption profile, like the panchromatic absorption; (ii) a surface-anchoring group, such as a carboxylate or phosphonate group; (iii) a LUMO matching the edge of the conduction band of the photoanode; (iv) a HOMO comparable to the electrolytes’ Fermi level; and (v) the stability to endure 10⁸ turnovers (20 years of exposure).

Generally, dyes fall into two categories: metal-complex-based polypyridyl dyes and metal-free organic dyes. While metal-complex—mostly ruthenium—dyes show high efficiencies due to high absorbance ranges extending to the near-infrared range, the metal-free organic dyes appeal to the market with their low processing cost and limited Ru requirements.

3.1. Metal-Complex-Based Dyes

Metal-complex dye sensitizers generally consist of a central metal ion and a subsidiary ligand, typically a bipyridine or tetrapyridine that contains anchoring groups. The central metal ion performs the light absorbance. Subsidiary ligands can be structurally modified to fine-tune the photovoltaic properties.

Ruthenium complexes, as shown in Figure 3, have demonstrated excellent photovoltaic properties, such as broad absorbance profiles and well-fitted energy levels [24]. These factors, combined with electrochemical stability, make Ru complexes unrivaled for sensitizer uses [10, 25, 26]. One representative Ru-based dye is the N3 dye, whose reported conversion efficiency is over 10%.

(a)

(b)

(c)

(d)

Another one is N749 dye, which is called the black dye due to its enhanced absorption spectrum. It shows an enhanced efficiency as high as 10.4%. Recent research on this family of dyes includes the work conducted by Robson et al., in which the NCS ligands of the black dye were replaced with anionic tridentate chelating ligands to adjust the HOMO and LUMO of the dye sensitizers to increase the photocurrent without compromising other DSSC properties [27]. When a triphenylamine group was substituted for the NCS group and a phenyl-bipyridine-OMe group was used as the chelating ligand, an 8.02% PCE was measured.

There have been attempts to use metals other than Ru as the dye sensitizer. Such metals include Os [28], Re [29], Fe [30–32], Pt [33–36], and Cu [37, 38]. Os(II) complexes have better absorption spectra compared to Ru complexes. However, Alebbi et al. reported a lower energy conversion efficiency, attributing it to the slower electron transfer from the iodine electrolyte to the osmium complex [39]. Pt(II) diimine-dithiolate complexes showed a high IPCE of 47% at 500 nm [33] but had a poor light absorption capacity at longer wavelengths. The tenability of photophysical properties, due to possible structural modification of the substituents on the diimine and dithiolate, was notable. Cu(I) complexes have very similar photophysical properties to Ru complexes. According to Constable et al., the - characteristic of these complexes was sensitive to the location of the conjugated pi-bond.

Polyphyrins are also of interest due to their good absorption and stability. With zinc-polyphyrin dye and a Co(III) tris(bipyridyl)-based redox electrolyte, Yella et al. reported a breakthrough efficiency of 12.3% and attributed this high efficiency to the suppression of electron backtransfer by the dye structure [40].

3.2. Metal-Free Organic Dyes

N3 and N719 dyes exhibit high performances with very fast electron injections. However, the molar extinction coefficients in the visible and near-IR ranges are relatively low. Moreover, there are concerns about the cost effectiveness of ruthenium and the environmental impacts.

Organic dyes also enable easy synthesis and design of the dye molecules. The predominant structure of metal-free organic dyes is the donor--acceptor (D--A) structure. It works as a basic template to design new dye molecules by adjusting the functional group or the whole moiety of the donor, pi-bridge, or acceptor of an existing dye.

Zhang et al. reported a high power conversion efficiency of 11.5–12.8% with cyclopentadithiophene-benzothiadiazole derivatives [41]. This research group cografted the dyes having poor light absorption abilities, by which they successfully removed the penetration channels for Co(III) redox ions and thereby restricted the charge recombination at the titania surface. The dyes they used contain triphenylamine and benzoic acid moieties on each end of the cyclopentadithiophene-benzothiadiazole group, where different orders of the moieties generate two different dyes. The high PCE of 12.8% is even comparable to the Ru-based dyes, which proves that metal-free organic DSSCs can be as efficient as conventional DSSCs and sets a new standard for organic DSSCs for peer researchers.

Another approach taken by Qu et al. studied the diketopyrrolopyrrole (DPP) dyes and their photovoltaic characteristics as shown in Figure 4 [42]. These dyes commonly had a triphenylamine donor, carboxylic acid acceptor, and DPP pi-bridge. The introduction of DPP moieties improved the spectral absorption at longer wavelengths. The PCE was 3.44%, relatively high, and was attributed by the authors to high dye aggregation and electron recombination. Adding 1.5 mM of chenodeoxycholic acid (CDCA) partly resolved the aggregation issue and raised the PCE to 4.14%, with mA cm⁻², V, and a fill factor of 0.7 under AM1.5 solar light and with an iodine electrolyte.

Another approach to DSSC dyes involves extracting the natural dyes and structurally adjusting them for solar cell applications [49]. None of them so far has led to a PCE significantly higher than those of other organic dye sensitizers. One reason for their low PCEs is thought to be the low interaction between the dyes and TiO₂. High adsorption of dyes onto the TiO₂ structure is vital for high , because electron recombination can occur. In fact, most of the natural dye-based DSSCs suffer from low . Low stability of natural dyes is another issue. Therefore, improvements either in or in stability are essential in order to justify further studies using this approach.

4. Metal Oxide

Metal oxide nanostructures have also been integrated into DSSCs to maximize the number of adsorbed dyes and thereby maximize the photocurrent. O’Regan and Grätzel used a mesoporous layer of TiO₂ to produce a 1000-fold increase in the surface area [7]. TiO₂ NPs are generally preferred for DSSC applications due to their high stability. The group also studied various alternatives, such as ZnO, SnO₂, or Nb₂O₅ [50], which were chosen because their energy band structures are similar to that of TiO₂. However, these alternatives rarely yielded PCEs comparable to those of TiO₂-based cells [51].

4.1. TiO₂ Nanoparticle Films Based DSSCs

TiO₂ has three types of crystallinities: anatase, rutile, and brookite. A comparative study between anatase and rutile TiO₂ nanoparticle films was conducted by Park et al. [52]. This study concluded that the anatase TiO₂ nanoparticles have better electron transport than do rutile TiO₂ nanoparticles in DSSCs.

While nanoparticle films have shown significantly higher PCEs compared to those of other nanostructures, due to their excessive number of adsorbed dyes, they have a clear disadvantage in charge transport. In nanoparticle films, the generated charge has to pass several nanoparticles before it reaches the substrate. Since the particles slightly differ in their energy states, the combined energy band might contain several trap states, and the charge may be trapped in such states, losing the energy and delaying the charge transfer process [53]. Moreover, the grain boundary between nanoparticles is not effective for electron transport.

In TiO₂ nanotubes, the electron transport is better than TiO₂ nanoparticles due to the absence of a grain boundary. However, the small surface area for sensitizers is one of the main obstacles to achieving a high PCE in DSSCs. To retain the advantage in the surface area while improving the charge transport, numerous studies have been conducted to test DSSCs based on TiO₂ nanotubes.

4.2. TiO₂ Nanotube Arrays

4.2.1. Titanium Anodization

Anodic titanium oxide TiO₂ nanotube arrays have properties that make them more effective than many other forms of TiO₂ for applications in photocatalysis [54, 55], gas sensors [44, 56–59], photoelectrolysis [60–62], and photovoltaics [63–65]. Since Zwilling reported on the TiO₂ nanotube arrays in chromic acid and hydrofluoric acid in 1999 [66], TiO₂ nanotube arrays have been studied in terms of fabrication, characterization, application, and formation mechanism [44, 67].

Gong et al. reported on TiO₂ nanotube arrays in a 0.5 wt% HF aqueous solution at room temperature using different anodizing voltages [68]. The film thickness could not be increased above 400–500 nm when an HF-based electrolyte was used. The fluoride solution dissolves TiO₂ by forming anions. The acidity of HF electrolytes is too high and results in a rapid dissolution of TiO₂. To overcome this problem, Mor et al. reported that the addition of acetic acid to a 0.5 wt% HF electrolyte in a 1 : 7 ratio resulted in more mechanically robust TiO₂ nanotube arrays without changing their shape or size [57, 69]. The surface morphology of TiO₂ nanotube arrays anodized in an electrolyte containing 2.5% HNO₃ and 1% HF at 20 V for 4 hours exhibited a uniform, clean, and regular TiO₂ nanotube array structure with a length of about 400 nm as reported by Ruan. The anodization with an electrolyte composed of 0.5 M H₃BO₃, 2.5% HNO₃, and 1% HF at 20 V for 4 h led to irregular pore of TiO₂ nanotube arrays but a long length of about 560 nm [70]. To increase the length of the TiO₂ nanotube arrays, Ti was anodized with KF or NaF in the electrolyte [71]. The acidity of the electrolyte could be controlled by adding HF, H₂SO₄, or Na₂SO₄ to adjust the balance of the dissociation of TiO₂ at the electrolyte/oxide interface and the oxidation of TiO₂ at the oxide/metal interface [72, 73].

Grimes et al. obtained TiO₂ nanotube arrays up to approximately 1000 μm using a variety of organic electrolytes, such as dimethyl sulfoxide, formamide, ethylene glycol, and N-methylformamide [74–76].

The key to constructing longer TiO₂ nanotube arrays is to reduce the water content in the anodization bath to less than 5%. In organic electrolytes, a little water content reduces the dissociation of the oxide in the fluorine-containing electrolytes.

The chemical reaction of titanium anodization should be the same as that of aluminum anodization [44, 74, 77, 78]. The key processes are the growth of an anodic TiO₂ when the surface of Ti is oxidized with oxide anion and the dissociation of oxide anions through dissociation and field-assisted dissolution in water, as shown in Figure 5 [43]. At the electrolyte/oxide interface, the reaction is written as

The cations move to the cathode and undergo the reaction:

The oxide ions, or , migrate through the oxide layer to form TiO₂:where is yet to be determined. Titanium hydroxide decomposes to form TiO₂ at the oxide/hydroxide interface. F⁻ in the electrolyte moves to the anode and undergoes the reaction:

The overall reaction of TiO₂ nanotube arrays iswhere was introduced to indicate the ratio of the dissociation rate of water to the dissolution rate of TiO₂.

Pores develop from pits on the Ti plate surface, and a schematic diagram for the equifield strength model is shown in Figure 6.

(a)

(b)

(c)

(d)

(e)

The initiation and growth of pores are associated with accelerated dissolution of TiO₂ due to the influence of an electric field [79]. Many defects, such as impurities, dislocation, grain boundaries, or nonmetallic inclusions, could cause a faster dissolution rate and lead to pit growth [80, 81]. When Ti⁴⁺ cations escape from the oxide surface because of an applied field, Ti⁴⁺cation vacancies can appear and accumulate to form high-density voids in the oxide layer, which can aid in the propagation of pits [82, 83].

4.2.2. TiO₂ Nanotube Arrays Based DSSCs

Grimes et al. reported backside-illuminated DSSCs based on TiO₂ nanotube array electrodes in 2006. They were based on 6 μm long, highly ordered nanotube-array films sensitized by a self-assembled monolayer of N719 sensitizer which showed an 8.79 mA cm⁻² short-circuit current density, an 841 mV open-circuit potential, and a 0.57 fill factor, yielding a PCE of 4.24% under AM1.5 sun. This investigation was the first attempt to construct a DSSC of TiO₂ nanotube arrays. However, it used backside illumination. Therefore, incident sunlight had to pass a Pt-coated counter electrode and electrolyte that absorbed light near 400 nm. To increase the energy conversion efficiency using TiO₂ nanotube arrays in DSSCs, the structure should be designed with front illumination.

Several approaches using TiO₂ nanotube arrays in DSSC designs have incorporated a thin film consisting of TiO₂ nanotube arrays with the photoanode of the DSSCs, improving the scattering-driven light harvesting and suppressing the charge recombination. Park et al. reported a simple method for preparing TiO₂ nanotube arrays on the FTO glass [16]. In this method, a thin film of TiO₂ was anodized with NH₄F to form an array of TiO₂ nanotubes. The nanotube array was then detached from the metallic Ti substrate by the use of an HCl solution and was annealed onto a sheet of FTO glass at 500°C for 30 min. The photoanode fabricated with this method was equipped with a Pt counter electrode, Ru(II)LL′(NCS)₂ dye (L = 2,2-bipyridyl-4,4-dicarboxylic acid; L′ = 2,2-bipyridyl-4,4-ditetrabutylammonium carboxylate), and an iodine electrolyte to yield 7.6% power conversion efficiency under 1 sun illumination.

Chen and Xu produced a crystalline TiO₂ nanotube array thin film [17]. The crystalline TiO₂ nanotube arrays were usually obtained by annealing the array at a high temperature, and the high-temperature annealing caused the TiO₂ nanotube arrays to curl. The researchers circumvented this problem by introducing an additional step of anodization after annealing, which results in a double-layer structure of TiO₂ nanotube arrays, in which the lower layer is later dissolved in an H₂O₂ solution. The resulting free-standing TiO₂ nanotube arrays did not need any support to maintain their crystal structure, enabling them to be attached to FTO glass and to fabricate a front-illuminated DSSC. The front illumination of the DSSC enhanced the irradiation intensity by 11% compared to the conventional back-illuminated method. Additionally, the crystalline free-standing TiO₂ nanotube arrays provided a longer electron lifetime, which caused the PCE to increase from 2.8% with a back-illuminated DSSC equipped with thick TiO₂ nanotube arrays on a Ti substrate to 5.5% with a front-illuminated, crystal-structured, TiO₂ nanotube array-based DSSC.

Lin et al. fabricated open-ended TiO₂ nanotube arrays, which differed from the previously mentioned nanotube structures in that there was no blocking layer of TiO₂ at the junction point between the FTO glass and the TiO₂ nanotube arrays [18]. The DSSC devices were fabricated with the open-ended TiO₂ nanotube arrays interconnected to the FTO glass by NP-TiO₂ paste, N719 dyes, Pt-FTO glass, and an iodine-based electrolyte for front-side illumination. The open-ended nanotube arrays were prepared by the simple introduction of an oxalic acid solution as an etching agent. Compared to the close-ended TiO₂ nanotube arrays, the open-ended TiO₂ nanotube arrays dramatically increased the short-circuit current, resulting in a high PCE of 9.1%. The increase in the short-circuit current was attributed by the authors to the enhanced interaction between the electrolyte and NP-TiO₂ underlayer due to the absence of the bottom caps. The open-ended nanotube array showed a strong enhancement in capturing incident photons with longer wavelengths, which also indicated that opening the tube bottom enabled the DSSC device to collect the excited electrons over the entire length of the nanotubes.

Li et al. reported on the fabrication of crystalline TiO₂ nanotube arrays using the secondary anodization step in a similar manner to Chen et al. [17, 19]. With these free-standing crystalline TiO₂ nanotube arrays, they used a dry-etching method with a plasma reactor under BCl₃/Cl₂ to make the nanotube bottom open-ended and compared this array to a close-ended nanotube array fabricated with the same methodology, but without the etching step. The resulting PCE was higher for the open-ended nanotube arrays (6.24%) than it was for the close-ended nanotube arrays (4.84%). The authors explained this difference as the result of the interface between nanotube arrays and FTO being more compactly adhered, leading to improved electron diffusion and charge collection. This conclusion is similar to that of Lin et al.

The open-ended TiO₂ nanotube arrays generally show a better photoelectric performance than do the close-ended nanotube arrays. Rho et al. studied the effect of the thickness of the bottom cap (barrier layer) of the nanotube arrays, as shown in Figure 7 [45]. The authors fabricated the TiO₂ nanotube arrays with two anodization steps, followed by ion milling with argon ions. The thickness of the barrier layer was controlled by varying the time for the ion-milling step. The resulting PCEs varied from 2.5% to 3.7%. As the barrier layer was removed, the PCE increased. When the DSSC was designed with back-side illumination, the efficiency was lower than when it was designed with front-side illumination. In back-side illumination, the existence of the barrier layer does not affect the incident light intensity, as the light reaches the barrier layer after it is absorbed by the dye molecules. Rather, in this case, the more decisive factor influencing the conversion efficiency was the efficiency of electron diffusion, as the barrier layer may significantly hinder the electron transport.

(a)

(b)

(c)

(d)

The energy conversion efficiency of DSSCs based on open-end TiO₂ nanotube arrays was much higher than the efficiency based on closed-end ones. This result means that the barrier layer, corresponding to the under layer of the detached TiO₂ nanotube arrays, has a marked effect on the conversion efficiency, since the barrier layer has been removed in open-end TiO₂ nanotube arrays but left intact in closed-end TiO₂ nanotube arrays. The barrier layer could affect the conversion efficiency by preventing the diffusion of materials like electrolytes and dye molecules, by reducing the transmittance of light, and by hindering the electron transport. The electrons generated by excitation of the dyes adsorbed on the TiO₂ nanotube arrays could transfer to the electrode through the TiO₂ nanotube arrays. In this case, they must pass the barrier layer to reach the electrode. (DSSCs with free-standing TiO₂ nanotube array were summarized in Table 1.)

4.2.3. Development of TiO₂ Nanotube Arrays for DSSC

The various approaches mentioned in the earlier sections exploited TiO₂ nanotube arrays to achieve DSSC systems with higher efficiencies. Generally, the techniques to increase the efficiencies of TiO₂ nanoparticle systems can be also applied to TiO₂ nanotube systems. For example, combining plasmonic enhancement and/or TiCl₄ could benefit TiO₂ nanotube arrays, which have large spaces in them.

(1) Plasmonic TiO₂ Nanotube Arrays for DSSCs. Plasmonic solar cells are photovoltaic devices that use noble metal surface plasmons. Most solar cells have weak absorbers. To absorb larger amounts and longer wavelengths of incident light, the morphology of the substrate is etched with pyramids with sizes of 2–10 μm to obtain a wavelength-scale texture. This structure improves the light trapping for solar cells but increases the surface recombination and reduces the material quality [84, 85].

There is another approach involving the use of noble metal nanoparticles in solar cells. The light can be absorbed and scattered from the noble metal nanoparticles that are excited at the surface plasmon resonance.

The mechanism of plasmonic solar cells can be used to explain the photocurrent enhancement by metal nanoparticles incorporated into or on solar cells, as shown in Figure 8 [46]. One is scattering from the metal nanoparticles, which can be used as subwavelength scattering elements to couple and trap plane waves propagating from the Sun into the semiconductor thin film, by folding the light into a thin absorber layer as shown in Figure 8(a).

(a)

(b)

(c)

Light is preferentially scattered and trapped in the semiconductor thin film by multiple high-angle scatterings, effectively increasing the optical path length in the cell. In inorganic plasmonic solar cells, the photocurrent enhancement is increased by scattering from metal nanoparticles. Another approach makes use of the near-field enhancement from metal nanoparticles that can be used as subwavelength antennas in which the plasmonic near-field is coupled to the semiconductor, increasing its effective absorption cross-section, as shown in Figure 8(b). In organic plasmonic solar cells, the photocurrent enhancement is increased by near-field enhancement. The direct generation of charge carriers in the semiconductor substrate has also been studied. A corrugated metallic film on the back surface of a thin photovoltaic absorber layer can couple sunlight into surface plasmon polariton (SPP) modes supported at the metal/semiconductor interface as well as guided modes in the semiconductor slab, whereupon the light is converted to photocarriers in the semiconductor as shown in Figure 8(c) [86–88].

Stuart and Hall reported an 18-fold photocurrent enhancement for light-sensitive devices with a 165-nm-thick silicon-on-insulator photodetector at a wavelength of 800 nm by using silver nanoparticles on the surface of the device [89]. The gold nanoparticles used for scattering and absorption of light on highly doped wafer-based solar cells were reported on by Schaadt et al. [90]. Gold nanoparticles on thin-film amorphous silicon solar cells gained an 8% overall increase in conversion efficiency as reported by Derkacs et al. [91]. Silver nanoparticles on 1.25-μm-thick silicon-on-insulator solar cells and planar wafer-based cells obtained 33% and 19% photocurrent increases, respectively, as reported by Pillai et al. [92]. Enhancement in the photocurrent by up to a factor of 2.7 for ITO-copper phthalocyanine-indium structures was reported by Stenzel. Enhancement for silver clusters incorporated in ITO and zinc phthalocyanine solar cells was reported by Westphalen et al. [93]. Enhanced efficiencies for ultrathin film organic solar cells due to 5 nm diameter silver nanoparticles were reported by Rand. An increase in efficiency by a factor of 1.7 for organic bulk heterojunction solar cells was reported by Morfa et al. [94]. Increased photocurrents for CdSe/Si heterostructures [95] and enhanced carrier generation in dye-sensitized solar cells have also been reported [96].

Rho et al. attached TiO₂ nanotube arrays, which were prepared by the electrochemical anodization method, onto a TCO glass to fabricate a transparent photoanode and a front-illuminated DSSC as shown in Figure 9 [47]. With this cell design, the N719 dyes were sensitized more directly by the incident light compared to the conventional back-illuminated DSSCs in which light has to pass through the transparent counter electrode in order to reach the dyes. Ag nanoparticles with diameters smaller than the light wavelength can improve the light absorption dramatically due to the surface plasmon resonance effect. The authors varied the time of exposure to irradiation to examine the Ag nanoparticle deposition kinetics and the existence of the optimal irradiation. The Ag nanoparticles were deposited not only on the outside of the TiO₂ nanotube arrays but also on the inside. The photovoltaic properties measured for DSSCs without Ag nanoparticles and DSSCs with nanoparticles and varying irradiation times indicated the same tendency. The highest energy conversion efficiency achieved was 6.14%, around 32% improvement of the energy conversion efficiency for DSSCs without Ag nanoparticles, 4.64%. Comparison was also made between front-illuminated and back-illuminated DSSCs. The highest efficiency reported for the back-illuminated DSSCs was 3.077%, which was lower than the front-illuminated DSSCs’ highest efficiency. Notably, the effect of incorporating Ag nanoparticles was also lower for back-illuminated DSSCs. The back-illuminated DSSCs showed only a 9.46% increase in the efficiency after the deposition of Ag nanoparticles, which was lower than the 32% increase in the front-illuminated DSSCs. The authors attributed this difference to the reduced intensity of the light passing through the counter electrode and electrolyte layer in the back-illuminated DSSCs, which caused the surface plasmon radiation to occur only at the top part of the TiO₂ nanotube arrays.

(a)

(b)

(2) TiCl₄ with TiO₂ Nanotube Arrays for DSSC Solar Cells. TiO₂ nanoparticles have been deposited to fill the microcracks formed in TiO₂ nanotube arrays using an electrophoretic method [97]. By depositing nanoparticles, the conversion efficiency was improved from 4% to 5.2%. Nanoparticles were found in the cracks and on the surface of the nanotubes. The total inner space of the nanotubes might be much larger than the space of the microcracks. However, nanoparticles might not be deposited deep inside the pores. Since TiO₂ nanotube arrays are semiconductors, electrochemical depositions take place at or near the entrances of their pores. There is no driving force to push the deposited nanoparticles into the deep parts of the pores. In vacuum filtering, the solvent provides a driving force, and nanoparticles can be filled throughout the long channels of the TiO₂ nanotube arrays. The TiO₂ nanoparticles that fill the channels of TiO₂ nanotube arrays can make contact with the tubes directly or through other nanoparticles. Since nanotubes are more efficient in electron transfer than are nanoparticles or composites of nanoparticles and nanotubes, electron transfer to the electrode could also be more efficient.

DSSCs based on TiO₂ nanotube arrays filled with TiO₂ nanoparticles have also been fabricated as shown in Figure 10 [48]. The energy conversion efficiency was enhanced by about 21% by filling the channels of the membrane with TiO₂ nanoparticles. By treating with TiCl₄ after filling with nanoparticles, the efficiency was enhanced significantly by about 40% due to an increase in the total available surface area for dye adsorption and better electron transfer to the electrode. The method of filling the channels of the TiO₂ membrane with TiO₂ nanoparticles and then treating with TiCl₄ was used to improve the energy conversion efficiency of DSSCs based on TiO₂ nanotube arrays.

(3) Additional Layer Technique. Introducing a scattering layer such as TiO₂, ZrO₂, or SiO₂ can increase the total energy conversion efficiency of DSSCs [98]. TiO₂ is a good material to use for a scattering layer due to its chemical stability and dye-adsorption capability; hence, many DSSCs are fabricated using TiO₂ nanoparticle films with a TiO₂ scattering layer on top of the active layer.

Comparison has been made between DSSCs using closed- and open-ended TiO₂ nanotube arrays when a TiO₂ scattering layer is introduced. The energy conversion efficiency was enhanced by 5.15% due to the removal of the barrier layer, which was present in the closed-ended TiO₂ nanotube arrays, causing an improvement in electron transport. By introducing the TiO₂ scattering layer on the open-ended TiO₂ nanotube arrays, the energy conversion efficiency was enhanced by 10.30% due to the improved light harvesting. Additionally, the energy conversion efficiency of the open-ended TiO₂ nanotube arrays treated with TiCl₄ was enhanced by 5.51% due to increased dye adsorption. Each component could enhance the DSSC yields.

5. Conclusions and Future Work

In the future, photovoltaic cells will be used in many fields, such as mobile commerce, building integrated photovoltaics (BIPVs), and vehicles. Moreover, photovoltaic cells are essential in the Smart Grid, which is utilized in our daily lives. To apply solar energy in the Smart Grid, photovoltaic cells are required to have transparency, flexibility, light weight, low cost, and high energy conversion efficiency. In terms of low cost and light weight, organics, inorganics, and hybrid materials have brighter prospects than the semiconductors. In hybrid materials, photovoltaic cells have been prepared with the advantages of organics or inorganics selectively. However, it is not easy to increase the energy conversion efficiency. One potential solution is to use 3-dimensional nanostructures, such as nanotubes, nanowires, composite films with metal, or other types of nanostructures. As of today, 0-dimensional nanoparticles in photovoltaic cells still yield the higher energy conversion efficiency by supplying larger surface areas for the sensitizer adsorption. However, the electron transport and flexibility are sufficiently high in 3-dimensional nanostructures. To improve the energy conversion efficiency of 3-dimensional nanostructure based solar cells and take both advantages of 0-dimensional nanoparticles and 3-dimensional nanostructures, the light harvesting ability must be reinforced. One way of achieving the better light harvesting ability is to fill the 0-dimensional nanoparticles in the cavities of 3-dimensional nanostructure, which is another currently active field of study [99].

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Authors’ Contribution

Won-Yeop Rho and Hojin Jeon contributed equally to this work.

Acknowledgment

This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT & Future Planning (2014-A002-0065).

References

EPA, “Inventory of U.S. greenhouse gas emissions and sinks: 1990–1998,” EPA 236-R-00-001, U.S. Environmental Protection Agency, 2000.
View at: Google Scholar
International Engergy Outlook 2013, U. S. Briefing, 2013.
M. A. Qaeed, K. Ibrahim, K. M. Saron, M. A. Ahmed, and N. K. Allam, “Low-temperature solution-processed flexible solar cells based on (In,Ga)N nanocubes,” ACS Applied Materials & Interfaces, vol. 6, no. 13, pp. 9925–9931, 2014.
View at: Publisher Site | Google Scholar
L. Tsakalakos, “Nanostructures for photovoltaics,” Materials Science and Engineering R: Reports, vol. 62, no. 6, pp. 175–189, 2008.
View at: Publisher Site | Google Scholar
S. O'Rourke, P. Kim, and H. Polavarapu, Solar Photovoltaic Industry: Looking through the Storm, vol. 56, Deutsche Bank, 2009.
T. W. Hamann, R. A. Jensen, A. B. F. Martinson, H. van Ryswyk, and J. T. Hupp, “Advancing beyond current generation dye-sensitized solar cells,” Energy & Environmental Science, vol. 1, no. 1, pp. 66–78, 2008.
View at: Publisher Site | Google Scholar
B. O'Regan and M. Grätzel, “A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO₂ films,” Nature, vol. 353, no. 6346, pp. 737–740, 1991.
View at: Publisher Site | Google Scholar
L. M. Goncalves, V. de Zea Bermudez, H. A. Ribeiro, and A. M. Mendes, “Dye-sensitized solar cells: a safe bet for the future,” Energy & Environmental Science, vol. 1, no. 6, pp. 655–667, 2008.
View at: Publisher Site | Google Scholar
M. K. Nazeeruddin, E. Baranoff, and M. Grätzel, “Dye-sensitized solar cells: a brief overview,” Solar Energy, vol. 85, no. 6, pp. 1172–1178, 2011.
View at: Publisher Site | Google Scholar
D. Kuang, C. Klein, S. Ito et al., “High-Efficiency and stable mesoscopic dye-sensitized solar cells based on a high molar extinction coefficient ruthenium sensitizer and nonvolatile electrolyte,” Advanced Materials, vol. 19, no. 8, pp. 1133–1137, 2007.
View at: Publisher Site | Google Scholar
F. Ribeiro, J. MaçAira, R. Cruz, J. Gabriel, L. Andrade, and A. Mendes, “Laser assisted glass frit sealing of dye-sensitized solar cells,” Solar Energy Materials and Solar Cells, vol. 96, no. 1, pp. 43–49, 2012.
View at: Publisher Site | Google Scholar
J. Wu, S. Hao, Z. Lan et al., “An all-solid-state dye-sensitized solar cell-based poly(N-alkyl-4-vinyl-pyridine iodide) electrolyte with efficiency of 5.64%,” Journal of the American Chemical Society, vol. 130, no. 35, pp. 11568–11569, 2008.
View at: Publisher Site | Google Scholar
W. Wu, J. Li, F. Guo, L. Zhang, Y. Long, and J. Hua, “Photovoltaic performance and long-term stability of quasi-solid-state fluoranthene dyes-sensitized solar cells,” Renewable Energy, vol. 35, no. 8, pp. 1724–1728, 2010.
View at: Publisher Site | Google Scholar
J. H. Yum, S. J. Moon, C. S. Karthikeyan et al., “Heteroleptic ruthenium complex containing substituted triphenylamine hole-transport unit as sensitizer for stable dye-sensitized solar cell,” Nano Energy, vol. 1, no. 1, pp. 6–12, 2012.
View at: Publisher Site | Google Scholar
T. Kawashima, T. Ezure, K. Okada, H. Matsui, K. Goto, and N. Tanabe, “FTO/ITO double-layered transparent conductive oxide for dye-sensitized solar cells,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 164, no. 1–3, pp. 199–202, 2004.
View at: Publisher Site | Google Scholar
J. H. Park, T. W. Lee, and M. G. Kang, “Growth, detachment and transfer of highly-ordered TiO₂ nanotube arrays: use in dye-sensitized solar cells,” Chemical Communications, no. 25, pp. 2867–2869, 2008.
View at: Publisher Site | Google Scholar
Q. W. Chen and D. S. Xu, “Large-scale, noncurling, and free-standing crystallized TiO₂ nanotube arrays for dye-sensitized solar cells,” Journal of Physical Chemistry C, vol. 113, no. 15, pp. 6310–6314, 2009.
View at: Publisher Site | Google Scholar
C.-J. Lin, W.-Y. Yu, and S.-H. Chien, “Transparent electrodes of ordered opened-end TiO₂-nanotube arrays for highly efficient dye-sensitized solar cells,” Journal of Materials Chemistry, vol. 20, no. 6, pp. 1073–1077, 2010.
View at: Publisher Site | Google Scholar
L.-L. Li, Y.-J. Chen, H.-P. Wu, N. S. Wang, and E. W.-G. Diau, “Detachment and transfer of ordered TiO₂ nanotube arrays for front-illuminated dye-sensitized solar cells,” Energy & Environmental Science, vol. 4, no. 9, pp. 3420–3425, 2011.
View at: Publisher Site | Google Scholar
R. Buscaino, C. Baiocchi, C. Barolo et al., “A mass spectrometric analysis of sensitizer solution used for dye-sensitized solar cell,” Inorganica Chimica Acta, vol. 361, no. 3, pp. 798–805, 2008.
View at: Publisher Site | Google Scholar
M. Grätzel, “Recent advances in sensitized mesoscopic solar cells,” Accounts of Chemical Research, vol. 42, no. 11, pp. 1788–1798, 2009.
View at: Publisher Site | Google Scholar
M. K. Nazeeruddin, F. de Angelis, S. Fantacci et al., “Combined experimental and DFT-TDDFT computational study of photoelectrochemical cell ruthenium sensitizers,” Journal of the American Chemical Society, vol. 127, no. 48, pp. 16835–16847, 2005.
View at: Publisher Site | Google Scholar
J. Gong, J. Liang, and K. Sumathy, “Review on dye-sensitized solar cells (DSSCs): fundamental concepts and novel materials,” Renewable and Sustainable Energy Reviews, vol. 16, no. 8, pp. 5848–5860, 2012.
View at: Publisher Site | Google Scholar
W. Sharmoukh and N. K. Allam, “TiO₂ nanotube-based dye-sensitized solar cell using new photosensitizer with enhanced open-circuit voltage and fill factor,” ACS Applied Materials and Interfaces, vol. 4, no. 8, pp. 4413–4418, 2012.
View at: Publisher Site | Google Scholar
D. Kuang, S. Ito, B. Wenger et al., “High molar extinction coefficient heteroleptic ruthenium complexes for thin film dye-sensitized solar cells,” Journal of the American Chemical Society, vol. 128, no. 12, pp. 4146–4154, 2006.
View at: Publisher Site | Google Scholar
S. A. Haque, E. Palomares, B. M. Cho et al., “Charge separation versus recombination in dye-sensitized nanocrystalline solar cells: the minimization of kinetic redundancy,” Journal of the American Chemical Society, vol. 127, no. 10, pp. 3456–3462, 2005.
View at: Publisher Site | Google Scholar
K. C. D. Robson, B. D. Koivisto, A. Yella et al., “Design and development of functionalized cyclometalated ruthenium chromophores for light-harvesting applications,” Inorganic Chemistry, vol. 50, no. 12, pp. 5494–5508, 2011.
View at: Publisher Site | Google Scholar
D. Kuciauskas, J. E. Monat, R. Villahermosa, H. B. Gray, N. S. Lewis, and J. K. McCusker, “Transient absorption spectroscopy of ruthenium and osmium polypyridyl complexes adsorbed onto nanocrystalline TiO₂ photoelectrodes,” Journal of Physical Chemistry B, vol. 106, no. 36, pp. 9347–9358, 2002.
View at: Publisher Site | Google Scholar
G. M. Hasselmann and G. J. Meyer, “Sensitization of nanocrystalline TiO₂ by Re(I) polypyridyl compounds,” Zeitschrift für Physikalische Chemie, vol. 212, part 1, pp. 39–44, 1999.
View at: Publisher Site | Google Scholar
S. Ferrere, “New photosensitizers based upon [Fe^II(L)₂(CN)₂] and [Fe^IIL₃], where L is substituted 2,2′-bipyridine,” Inorganica Chimica Acta, vol. 329, no. 1, pp. 79–92, 2002.
View at: Publisher Site | Google Scholar
S. Ferrere and B. A. Gregg, “Photosensitization of TiO₂ by [Fe(II)(2,2′-bipyridine-4,4′-dicarboxylic acid)₂(CN)₂]: band selective electron injection from ultra-short-lived excited states,” Journal of the American Chemical Society, vol. 120, no. 4, pp. 843–844, 1998.
View at: Publisher Site | Google Scholar
S. Ferrere, “New photosensitizers based upon [Fe(L)₂(CN)₂] and [Fe(L)₃] (L = substituted 2,2′-bipyridine): yields for the photosensitization of TiO₂ and effects on the band selectivity,” Chemistry of Materials, vol. 12, no. 4, pp. 1083–1089, 2000.
View at: Publisher Site | Google Scholar
A. Islam, H. Sugihara, K. Hara et al., “Dye sensitization of nanocrystalline titanium dioxide with square planar platinum(II) diimine dithiolate complexes,” Inorganic Chemistry, vol. 40, no. 21, pp. 5371–5380, 2001.
View at: Publisher Site | Google Scholar
E. A. M. Geary, L. J. Yellowlees, L. A. Jack et al., “Synthesis, structure, and properties of [Pt(II)(diimine)(dithiolate)] dyes with 3, $3^{'}$ -, 4, $4^{'}$ -, and 5, $5^{'}$ -disubstituted bipyridyl: applications in dye-sensitized solar cells,” Inorganic Chemistry, vol. 44, no. 2, pp. 242–250, 2005.
View at: Publisher Site | Google Scholar
E. A. M. Geary, K. L. McCall, A. Turner et al., “Spectroscopic, electrochemical and computational study of Pt-diimine-dithiolene complexes: rationalising the properties of solar cell dyes,” Dalton Transactions, no. 28, pp. 3701–3708, 2008.
View at: Publisher Site | Google Scholar
E. A. M. Geary, N. Hirata, J. Clifford et al., “Synthesis, structure and properties of [Pt(2,2′-bipyridyl-5,5′-dicarboxylic acid)(3,4-toluenedithiolate)]: tuning molecular properties for application in dye-sensitised solar cells,” Dalton Transactions, no. 19, pp. 3757–3762, 2003.
View at: Publisher Site | Google Scholar
S. Sakaki, T. Kuroki, and T. Hamada, “Synthesis of a new copper(I) complex,[Cu(tmdcbpy)₂]⁺ (tmdcbpy = 4,4′,6,6′-tetramethyl-2,2′-bipyridine-5,5′- dicarboxylic acid), and its application to solar cells,” Journal of the Chemical Society, Dalton Transactions, no. 6, pp. 840–842, 2002.
View at: Google Scholar
T. Bessho, E. C. Constable, M. Graetzel et al., “An element of surprise—efficient copper-functionalized dye-sensitized solar cells,” Chemical Communications, no. 32, pp. 3717–3719, 2008.
View at: Publisher Site | Google Scholar
M. Alebbi, C. A. Bignozzi, T. A. Heimer, G. M. Hasselmann, and G. J. Meyer, “The limiting role of iodide oxidation in cis-Os(dcb)₂(CN)₂/TiO₂ photoelectrochemical cells,” The Journal of Physical Chemistry B, vol. 102, no. 39, pp. 7577–7581, 1998.
View at: Publisher Site | Google Scholar
A. Yella, H.-W. Lee, H. N. Tsao et al., “Porphyrin-sensitized solar cells with cobalt (II/III)-based redox electrolyte exceed 12 percent efficiency,” Science, vol. 334, no. 6056, pp. 629–634, 2011.
View at: Publisher Site | Google Scholar
M. Zhang, Y. Wang, M. Xu, W. Ma, R. Li, and P. Wang, “Design of high-efficiency organic dyes for titania solar cells based on the chromophoric core of cyclopentadithiophene-benzothiadiazole,” Energy & Environmental Science, vol. 6, no. 10, pp. 2944–2949, 2013.
View at: Publisher Site | Google Scholar
S. Qu, W. Wu, J. Hua, C. Kong, Y. Long, and H. Tian, “New diketopyrrolopyrrole (DPP) dyes for efficient dye-sensitized solar cells,” Journal of Physical Chemistry C, vol. 114, no. 2, pp. 1343–1349, 2010.
View at: Publisher Site | Google Scholar
S. Minagar, C. C. Berndt, J. Wang, E. Ivanova, and C. Wen, “A review of the application of anodization for the fabrication of nanotubes on metal implant surfaces,” Acta Biomaterialia, vol. 8, no. 8, pp. 2875–2888, 2012.
View at: Publisher Site | Google Scholar
G. K. Mor, O. K. Varghese, M. Paulose, K. Shankar, and C. A. Grimes, “A review on highly ordered, vertically oriented TiO₂ nanotube arrays: fabrication, material properties, and solar energy applications,” Solar Energy Materials and Solar Cells, vol. 90, no. 14, pp. 2011–2075, 2006.
View at: Publisher Site | Google Scholar
C. Rho, J.-H. Min, and J. S. Suh, “Barrier layer effect on the electron transport of the dye-sensitized solar cells based on TiO₂ nanotube arrays,” Journal of Physical Chemistry C, vol. 116, no. 12, pp. 7213–7218, 2012.
View at: Publisher Site | Google Scholar
H. A. Atwater and A. Polman, “Plasmonics for improved photovoltaic devices,” Nature Materials, vol. 9, no. 3, pp. 205–213, 2010.
View at: Publisher Site | Google Scholar
W.-Y. Rho, H.-S. Kim, S. H. Lee et al., “Front-illuminated dye-sensitized solar cells with Ag nanoparticle-functionalized freestanding TiO₂ nanotube arrays,” Chemical Physics Letters, vol. 614, pp. 78–81, 2014.
View at: Publisher Site | Google Scholar
C. Rho and J. S. Suh, “Filling TiO₂ nanoparticles in the channels of TiO₂ nanotube membranes to enhance the efficiency of dye-sensitized solar cells,” Chemical Physics Letters, vol. 513, no. 1-3, pp. 108–111, 2011.
View at: Publisher Site | Google Scholar
M. R. Narayan, “Review: dye sensitized solar cells based on natural photosensitizers,” Renewable and Sustainable Energy Reviews, vol. 16, no. 1, pp. 208–215, 2012.
View at: Publisher Site | Google Scholar
R. Nashed, P. Szymanski, M. A. El-Sayed, and N. K. Allam, “Self-Assembled nanostructured photoanodes with staggered bandgap for efficient solar energy conversion,” ACS Nano, vol. 8, no. 5, pp. 4915–4923, 2014.
View at: Publisher Site | Google Scholar
J. Z. Ou, R. A. Rani, M.-H. Ham et al., “Elevated temperature anodized Nb₂O₅: a photoanode material with exceptionally large photoconversion efficiencies,” ACS Nano, vol. 6, no. 5, pp. 4045–4053, 2012.
View at: Publisher Site | Google Scholar
N.-G. Park, J. van de Lagemaat, and A. J. Frank, “Comparison of dye-sensitized rutile- and anatase-based TiO₂ solar cells,” Journal of Physical Chemistry B, vol. 104, no. 38, pp. 8989–8994, 2000.
View at: Google Scholar
Q. Zhang and G. Cao, “Nanostructured photoelectrodes for dye-sensitized solar cells,” Nano Today, vol. 6, no. 1, pp. 91–109, 2011.
View at: Publisher Site | Google Scholar
M. Adachi, Y. Murata, M. Harada, and S. Yoshikawa, “Formation of titania nanotubes with high photo-catalytic activity,” Chemistry Letters, no. 8, pp. 942–943, 2000.
View at: Google Scholar
S.-Z. Chu, S. Inoue, K. Wada, D. Li, H. Haneda, and S. Awatsu, “Highly porous (TiO₂-SiO₂-TeO₂)/Al₂O₃/TiO₂ composite nanostructures on glass with enhanced photocatalysis fabricated by anodization and sol-gel process,” The Journal of Physical Chemistry B, vol. 107, no. 27, pp. 6586–6589, 2003.
View at: Publisher Site | Google Scholar
O. K. Varghese, D. Gong, M. Paulose, K. G. Ong, E. C. Dickey, and C. A. Grimes, “Extreme changes in the electrical resistance of titania nanotubes with hydrogen exposure,” Advanced Materials, vol. 15, no. 7-8, pp. 624–627, 2003.
View at: Publisher Site | Google Scholar
G. K. Mor, M. A. Carvalho, O. K. Varghese, M. V. Pishko, and C. A. Grimes, “A room-temperature TiO₂-nanotube hydrogen sensor able to self-clean photoactively from environmental contamination,” Journal of Materials Research, vol. 19, no. 2, pp. 628–634, 2004.
View at: Publisher Site | Google Scholar
M. Paulose, O. K. Varghese, G. K. Mor, C. A. Grimes, and K. G. Ong, “Unprecedented ultra-high hydrogen gas sensitivity in undoped titania nanotubes,” Nanotechnology, vol. 17, no. 2, pp. 398–402, 2006.
View at: Publisher Site | Google Scholar
O. K. Varghese, G. K. Mor, C. A. Grimes, M. Paulose, and N. Mukherjee, “A titania nanotube-array room-temperature sensor for selective detection of hydrogen at low concentrations,” Journal of Nanoscience and Nanotechnology, vol. 4, no. 7, pp. 733–737, 2004.
View at: Publisher Site | Google Scholar
G. K. Mor, K. Shankar, M. Paulose, O. K. Varghese, and C. A. Grimes, “Enhanced photocleavage of water using titania nanotube arrays,” Nano Letters, vol. 5, no. 1, pp. 191–195, 2005.
View at: Publisher Site | Google Scholar
G. K. Mor, K. Shankar, O. K. Varghese, and C. A. Grimes, “Photoelectrochemical properties of titania nanotubes,” Journal of Materials Research, vol. 19, no. 10, pp. 2989–2996, 2004.
View at: Publisher Site | Google Scholar
O. K. Varghese, M. Paulose, K. Shankar, G. K. Mor, and C. A. Grimes, “Water-photolysis properties of micron-length highly-ordered titania nanotube-arrays,” Journal of Nanoscience and Nanotechnology, vol. 5, no. 7, pp. 1158–1165, 2005.
View at: Publisher Site | Google Scholar
S. Uchida, R. Chiba, M. Tomiha, N. Masaki, and M. Shirai, “Application of titania nanotubes to a dye-sensitized solar cell,” Electrochemistry, vol. 70, no. 6, pp. 418–420, 2002.
View at: Google Scholar
M. Adachi, Y. Murata, I. Okada, and S. Yoshikawa, “Formation of titania nanotubes and applications for dye-sensitized solar cells,” Journal of the Electrochemical Society, vol. 150, no. 8, pp. G488–G493, 2003.
View at: Publisher Site | Google Scholar
M. Paulose, K. Shankar, O. K. Varghese, G. K. Mor, B. Hardin, and C. A. Grimes, “Backside illuminated dye-sensitized solar cells based on titania nanotube array electrodes (vol 17, pg 1446, 2006),” Nanotechnology, vol. 21, no. 38, 2010.
View at: Google Scholar
V. Zwilling, M. Aucouturier, and E. Darque-Ceretti, “Anodic oxidation of titanium and TA₆V alloy in chromic media. An electrochemical approach,” Electrochimica Acta, vol. 45, no. 6, pp. 921–929, 1999.
View at: Publisher Site | Google Scholar
N. K. Allam, K. Shankar, and C. A. Grimes, “Photoelectrochemical and water photoelectrolysis properties of ordered TiO2 nanotubes fabricated by Ti anodization in fluoride-free HCl electrolytes,” Journal of Materials Chemistry, vol. 18, no. 20, pp. 2341–2348, 2008.
View at: Publisher Site | Google Scholar
D. Gong, C. A. Grimes, O. K. Varghese et al., “Titanium oxide nanotube arrays prepared by anodic oxidation,” Journal of Materials Research, vol. 16, no. 12, pp. 3331–3334, 2001.
View at: Publisher Site | Google Scholar
G. K. Mor, O. K. Varghese, M. Paulose, and C. A. Grimes, “A self-cleaning, room-temperature titania-nanotube hydrogen gas sensor,” Sensor Letters, vol. 1, no. 1, pp. 42–46, 2003.
View at: Publisher Site | Google Scholar
C. Ruan, M. Paulose, O. K. Varghese, and C. A. Grimes, “Enhanced photoelectrochemical-response in highly ordered TiO₂ nanotube-arrays anodized in boric acid containing electrolyte,” Solar Energy Materials & Solar Cells, vol. 90, no. 9, pp. 1283–1295, 2006.
View at: Publisher Site | Google Scholar
Q. Y. Cai, M. Paulose, O. K. Varghese, and C. A. Grimes, “The effect of electrolyte composition on the fabrication of self-organized titanium oxide nanotube arrays by anodic oxidation,” Journal of Materials Research, vol. 20, no. 1, pp. 230–236, 2005.
View at: Publisher Site | Google Scholar
R. Beranek, H. Hildebrand, and P. Schmuki, “Self-organized porous titanium oxide prepared in H₂SO₄/HF electrolytes,” Electrochemical and Solid-State Letters, vol. 6, no. 3, pp. B12–B14, 2003.
View at: Publisher Site | Google Scholar
J. M. MacAk, K. Sirotna, and P. Schmuki, “Self-organized porous titanium oxide prepared in Na₂SO₄/NaF electrolytes,” Electrochimica Acta, vol. 50, no. 18, pp. 3679–3684, 2005.
View at: Publisher Site | Google Scholar
M. Paulose, K. Shankar, S. Yoriya et al., “Anodic growth of highly ordered TiO₂ nanotube arrays to 134 $μ$ m in length,” Journal of Physical Chemistry B, vol. 110, no. 33, pp. 16179–16184, 2006.
View at: Publisher Site | Google Scholar
K. Shankar, G. K. Mor, H. E. Prakasam et al., “Highly-ordered TiO₂ nanotube arrays up to 220 μm in length: use in water photoelectrolysis and dye-sensitized solar cells,” Nanotechnology, vol. 18, no. 6, Article ID 065707, 2007.
View at: Publisher Site | Google Scholar
M. Paulose, H. E. Prakasam, O. K. Varghese et al., “TiO₂ nanotube arrays of 1000 μm length by anodization of titanium foil: phenol red diffusion,” Journal of Physical Chemistry C, vol. 111, no. 41, pp. 14992–14997, 2007.
View at: Publisher Site | Google Scholar
L. V. Taveira, J. M. Macák, H. Tsuchiya, L. F. P. Dick, and P. Schmuki, “Initiation and growth of self-organized TiO₂ nanotubes anodically formed in NH₄F/(NH₄)₂SO₄ electrolytes,” Journal of the Electrochemical Society, vol. 152, no. 10, pp. B405–B410, 2005.
View at: Publisher Site | Google Scholar
Z. X. Su and W. Z. Zhou, “Formation mechanism of porous anodic aluminium and titanium oxides,” Advanced Materials, vol. 20, no. 19, pp. 3663–3667, 2008.
View at: Publisher Site | Google Scholar
T. P. Hoar and N. F. Mott, “A mechanism for the formation of porous anodic oxide films on aluminium,” Journal of Physics and Chemistry of Solids, vol. 9, no. 2, pp. 97–99, 1959.
View at: Google Scholar
K. R. Hebert, H. Wu, T. Gessmann, and K. Lynn, “Positron annihilation spectroscopy study of interfacial defects formed by dissolution of aluminum in aqueous sodium hydroxide,” Journal of the Electrochemical Society, vol. 148, no. 2, pp. B92–B100, 2001.
View at: Publisher Site | Google Scholar
R. Huang, K. R. Hebert, T. Gessmann, and K. G. Lynn, “Effect of impurities on interfacial void formation in aluminum,” Journal of the Electrochemical Society, vol. 151, no. 4, pp. B227–B232, 2004.
View at: Publisher Site | Google Scholar
C. Y. Chao, L. F. Lin, and D. D. Macdonald, “A point defect model for anodic passive films. 1. Film growth kinetics,” Journal of the Electrochemical Society, vol. 128, no. 6, pp. 1187–1194, 1981.
View at: Publisher Site | Google Scholar
L. F. Lin, C. Y. Chao, and D. D. Macdonald, “A point-defectmodel for anodic passive films .II. Chemical breakdown and pit initiation,” Journal of the Electrochemical Society, vol. 128, no. 6, pp. 1194–1198, 1981.
View at: Publisher Site | Google Scholar
J. Meier, S. Dubail, S. Golay et al., “Microcrystalline silicon and the impact on micromorph tandem solar cells,” Solar Energy Materials and Solar Cells, vol. 74, no. 1-4, pp. 457–467, 2002.
View at: Publisher Site | Google Scholar
J. Müller, B. Rech, J. Springer, and M. Vanecek, “TCO and light trapping in silicon thin film solar cells,” Solar Energy, vol. 77, no. 6, pp. 917–930, 2004.
View at: Publisher Site | Google Scholar
H. A. Atwater and A. Polman, “Plasmonics for improved photovoltaic devices (vol 9, pg 205, 2010),” Nature Materials, vol. 9, no. 10, p. 865, 2010.
View at: Publisher Site | Google Scholar
S. Pillai and M. A. Green, “Plasmonics for photovoltaic applications,” Solar Energy Materials and Solar Cells, vol. 94, no. 9, pp. 1481–1486, 2010.
View at: Publisher Site | Google Scholar
K. R. Catchpole and A. Polman, “Plasmonic solar cells,” Optics Express, vol. 16, no. 26, pp. 21793–21800, 2008.
View at: Publisher Site | Google Scholar
H. R. Stuart and D. G. Hall, “Island size effects in nanoparticle-enhanced photodetectors,” Applied Physics Letters, vol. 73, no. 26, pp. 3815–3817, 1998.
View at: Publisher Site | Google Scholar
D. M. Schaadt, B. Feng, and E. T. Yu, “Enhanced semiconductor optical absorption via surface plasmon excitation in metal nanoparticles,” Applied Physics Letters, vol. 86, no. 6, Article ID 063106, pp. 1–3, 2005.
View at: Publisher Site | Google Scholar
D. Derkacs, S. H. Lim, P. Matheu, W. Mar, and E. T. Yu, “Improved performance of amorphous silicon solar cells via scattering from surface plasmon polaritons in nearby metallic nanoparticles,” Applied Physics Letters, vol. 89, no. 9, Article ID 093103, 2006.
View at: Publisher Site | Google Scholar
S. Pillai, K. R. Catchpole, T. Trupke, and M. A. Green, “Surface plasmon enhanced silicon solar cells,” Journal of Applied Physics, vol. 101, no. 9, Article ID 093105, 2007.
View at: Publisher Site | Google Scholar
M. Westphalen, U. Kreibig, J. Rostalski, H. Lüth, and D. Meissner, “Metal cluster enhanced organic solar cells,” Solar Energy Materials and Solar Cells, vol. 61, no. 1, pp. 97–105, 2000.
View at: Publisher Site | Google Scholar
A. J. Morfa, K. L. Rowlen, T. H. Reilly II, M. J. Romero, and J. van de Lagemaat, “Plasmon-enhanced solar energy conversion in organic bulk heterojunction photovoltaics,” Applied Physics Letters, vol. 92, no. 1, Article ID 013504, 2008.
View at: Publisher Site | Google Scholar
R. B. Konda, R. Mundle, H. Mustafa et al., “Surface plasmon excitation via Au nanoparticles in n-CdSe/p-Si heterojunction diodes,” Applied Physics Letters, vol. 91, no. 19, 2007.
View at: Publisher Site | Google Scholar
C. Hägglund, M. Zäch, and B. Kasemo, “Enhanced charge carrier generation in dye sensitized solar cells by nanoparticle plasmons,” Applied Physics Letters, vol. 92, no. 1, Article ID 013113, 2008.
View at: Publisher Site | Google Scholar
K. Shin, Y. Jim, G. Y. Han, and J. H. Park, “Effect of incorporation of TiO₂ nanoparticles into oriented TiO₂ nanotube based dye-sensitized solar cells,” Journal of Nanoscience and Nanotechnology, vol. 9, no. 12, pp. 7436–7439, 2009.
View at: Publisher Site | Google Scholar
S. Hore, C. Vetter, R. Kern, H. Smit, and A. Hinsch, “Influence of scattering layers on efficiency of dye-sensitized solar cells,” Solar Energy Materials and Solar Cells, vol. 90, no. 9, pp. 1176–1188, 2006.
View at: Publisher Site | Google Scholar
J. Maçaira, L. Andrade, and A. Mendes, “Review on nanostructured photoelectrodes for next generation dye-sensitized solar cells,” Renewable and Sustainable Energy Reviews, vol. 27, pp. 334–349, 2013.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2015 Won-Yeop Rho et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

7923

Downloads

6341

Citations

Journal of Nanomaterials

Recent Progress in Dye-Sensitized Solar Cells for Improving Efficiency: TiO2 Nanotube Arrays in Active Layer

Abstract

1. Introduction

2. Principle of DSSCs

3. Dye

3.1. Metal-Complex-Based Dyes

3.2. Metal-Free Organic Dyes

4. Metal Oxide

4.1. TiO2 Nanoparticle Films Based DSSCs

4.2. TiO2 Nanotube Arrays

4.2.1. Titanium Anodization

4.2.2. TiO2 Nanotube Arrays Based DSSCs

4.2.3. Development of TiO2 Nanotube Arrays for DSSC

5. Conclusions and Future Work

Conflict of Interests

Authors’ Contribution

Acknowledgment

References

Copyright

Recent Progress in Dye-Sensitized Solar Cells for Improving Efficiency: TiO₂ Nanotube Arrays in Active Layer

4.1. TiO₂ Nanoparticle Films Based DSSCs

4.2. TiO₂ Nanotube Arrays

4.2.2. TiO₂ Nanotube Arrays Based DSSCs

4.2.3. Development of TiO₂ Nanotube Arrays for DSSC