Degradation of FBL Dye Wastewater by Magnetic Photocatalysts from Scraps

Liu, Robert; Wu, Chia Feng; Ger, Ming Der

doi:https://doi.org/10.1155/2015/651021

Journal of Nanomaterials

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2015 | Article ID 651021 | https://doi.org/10.1155/2015/651021

Degradation of FBL Dye Wastewater by Magnetic Photocatalysts from Scraps

Robert Liu,^1,2Chia Feng Wu,¹and Ming Der Ger³

Academic Editor: Chunyi Zhi

Received29 Sept 2014

Accepted06 Jan 2015

Published29 Apr 2015

Abstract

Magnetic photocatalyst solves the separation problem between wastewater and TiO₂ photocatalysts by the application of magnetic field. This research investigates the treatment of simulated FBL dye wastewater using Mn-Zn ferrite/TiO₂ magnetic photocatalyst. The magnetic Mn-Zn ferrite powder was first produced by a chemical coprecipitation method from spent dry batteries and spent pickling acid solutions. These two scraps comprise the only constituents of Mn-Zn ferrite. The as-synthesized Mn-Zn ferrite was then suspended in a solution containing Ti(SO₄)₂ and urea. Subsequently a magnetic photocatalyst was obtained from the solution by chemical coprecipitation. The prepared Mn-Zn ferrite powder and magnetic photocatalyst (Mn-Zn ferrite/TiO₂) were characterized using XRD, EDX, SEM, SQUID, BET, and so forth. The photocatalytic activity of the synthesized magnetic photocatalysts was tested using degradation of FBL dye wastewater. The adsorption and degradation studies by the TOC and ADMI measurement were carried out, respectively. The adsorption isotherm and Langmuir-Hinshelwood kinetic model for the prepared magnetic TiO₂ were proved to be applicable for the treatment. This research transforms waste into a valuable magnetic photocatalyst.

1. Introduction

Wastewaters from textile and dyeing industries are highly colored by various nonbiodegradable dyes which cause serious environmental problems [1]. Advanced oxidation processes such as UV/H₂O₂ [2], ozonation [1, 3–5], Fenton processes [5–8], ozone/Fenton [9], TiO₂, and modified TiO₂ [10–17] are promising alternatives for the mineralization of textile dyes or other pollutants. Among them, the semiconductor TiO₂’s simultaneous photocatalytic oxidation and reduction process show the significant potential due to its being photoreactive, nontoxic, chemically and biologically inert, photostable, and lower in cost. Among different advanced oxidation processes (AOPs), a relatively new AOP, sonolysis or hybrid AOPs with combination of sonolysis, has drawn increasing attention as it generates the •OH-free radical through the phenomenon of transient cavitation by ultrasound irradiation [18–20]. Cavitation is essentially nucleation, growth, and transient implosive collapse of gas bubbles driven by ultrasound wave.

Manganese zinc ferrites are important ferrimagnetic materials because of their high magnetic permeability and low magnetic hysteresis loss [21]. Ferrites are commonly produced using a ceramic process that involves a high temperature calcination of oxide and/or carbonates. Their main disadvantages are their large and nonuniform size distribution, poor reproducibility, contamination, and a need for the application of high temperature for production [22]. Therefore, several wet chemical methods have been used to prepare fine Mn-Zn ferrite powders, such as the citrate precursor method [23, 24], the autocombustion method [25], the hydrothermal method [26], the sol-gel method [27], and the coprecipitation method [28]. A rather new technique for the ferrite synthesis is the sonochemical method in which ferrite nanoparticles are prepared using ultrasound irradiation or sonication of the reaction mixture [29, 30].

Despite existing technologies, nanosized TiO₂ particles remain difficult to separate from treated wastewater. Fixed-film-TiO₂ systems are undermined by their own immobility, while magnetic TiO₂ systems offer to overcome this limitation. For example, Ma et al. [31] synthesized titania-coated Mn-Zn ferrite by hydrolysis of titanium chloride (TiCl₄) in the presence of Mn-Zn ferrite nanoparticles, which were prepared by a stearic acid sol-gel method. The magnetization of the TiO₂-coated Mn-Zn ferrite particles was reduced, unlike the uncoated ferrite nanoparticles, and high coercivity was obtained for both prepared uncoated and coated ferrite particles. It was also found that the synthesized photocatalysts were not superparamagnetic. Chen and Zhao [32] reported a magnetically separable photocatalyst of TiO₂/SiO₂/γ-Fe₂O₃ which was prepared using the solid phase synthesis method. The addition of a SiO₂ membrane between the γ-Fe₂O₃ core and the TiO₂ shell weakened the adverse effects of γ-Fe₂O₃ on the photocatalysis of TiO₂. The photocatalyst described in Chen and Zhao’s article showed good photocatalytic activity and it was able to separate from the solution through the use of a magnetic field. Gao et al. [33] synthesized a magnetically separated photocatalyst of TiO₂/γ-Fe₂O₃ by a sol-gel method. The sample sintered at 500°C showed the highest activity for the degradation of an acridine dye aqueous solution, with the optimal supporting amount of TiO₂ approximating 50%. Fu et al. [34] successfully prepared TiO₂/NiCuZn ferrite composite powder as a magnetic photocatalyst. The core NiCuZn ferrite powder was synthesized using waste material from steel and electroplating industries. The shell of the TiO₂ nanocrystal was prepared by a sol-gel hydrolysis method of titanium isopropoxide with NiCuZn ferrite powder, followed by heat treatment. In their study [34], the optimum dosage of the magnetic photocatalyst was 2.67 g/L for treating a methylene blue solution.

In this research, a simple magnetic photocatalyst preparation method was undertaken. First, Mn-Zn magnetic ferrite powder was prepared from spent Mn-Zn dry batteries and ferrous sulfate containing spent acid solution from steel plants by using coprecipitation method. Then, the magnetic powder was added to a titanium sulfate solution and the hydroxides of titanium were precipitated at desired pH using urea solution. After filtration, drying, and grinding, the precipitates were sintered at 500°C under N₂ atmosphere to form the magnetic photocatalyst, Mn-Zn ferrite/TiO₂. The adsorption and degradation of simulated FBL (Everdirect Supra Turquoise Blue) dye wastewater were carried out by applying self-prepared magnetic photocatalysts under dark as well as under solar irradiation. The adsorption isotherm and L-H kinetic model were also studied.

2. Materials and Methods

2.1. Preparation of Magnetic Mn-Zn Ferrite Powder and Magnetic Photocatalyst

The flow diagram for preparing the Mn-Zn ferrite powder and ferrite is shown in Figure 1. The designed composition used was ZnO : MnO : Fe₂O₃ = 12.5 : 35 : 52.5 by molar ratio and 8.56 : 20.89 : 70.55 by weight percentages or Zn : Mn : Fe = 0.25 : 0.7 : 2.1 by moles and Zn : Mn : Fe = 9.3 : 22.4 : 68.3 by weight percentages. The reactions are shown as follows:Due to the presence of Cu⁺² in the waste acid, iron powder was added to replace copper by reaction (2).

The magnetic photocatalyst was prepared by adding Mn-Zn ferrite magnetic powder 10 g and urea (N₂H₄CO) of 150 g into 92 mL of Ti(SO₄)₂ solution. The ratio of Mn-Zn ferrite powder to TiO₂ was 1 : 1 (wt%). The flow chart for the preparation of the magnetic photocatalyst of Mn-Zn ferrite/TiO₂ is shown in Figure 2. The reactions followed would be

2.2. Characterization

The crystalline structure of both magnetic powder and magnetic photocatalyst was examined by XRD (X-ray diffractometer, XRD-6000, Shimadzu, Japan). Their M-H loops were measured by SQUID (superconducting quantum interference device, MPM57, Quantum Design, USA). The chemical compositions of the particles were analyzed by XRF (X-ray fluorescence, XEPOS/XEPO1, Spectro Co., Germany). Their microstructure was observed by SEM (scanning electron microscopy, S-3000N, Hitachi, Japan). The specific area was measured by BET (Brunauer-Emmett-Teller, Model-ASAP 2012, Micromeritics, USA).

2.3. Adsorption and Photocatalytic Degradation

The adsorption and photocatalytic reaction were carried out by mixing 1 L of a FBL dye solution with 5 g of magnetic Mn-Zn ferrite/TiO₂ photocatalysts inside a 2 L photoreactor beaker, using a teflon agitator under dark and under solar irradiation for 8 hrs, respectively. The structure of the FBL dye was shown in [8]. The initial dye concentrations were COD = 100, 200, 300, and 400 mg/L for each experiment. To prepare COD = 100 mg/L, 0.0956 g of FBL dye was measured to make 1 L solution. The sampling time was 0 to 480 min with interval of 40 min, and each sample was taken under mixture condition. After filtration by 0.45 μm MFS, the TOC (total organic carbon, Model 1010, O.I. Analytical, USA) and ADMI (American Dye Manufacturers Institute, Model DR/4000V, HACH, USA) were measured for each sample. COD was determined by the potassium dichromate titration method as described in standard methods [35]. Solar intensities were measured by a radiometer (Lutron Co., Taiwan). All solar intensities at 0.5, 1, 2, 3, 4, 5, 6, 7, and 8 hours were measured and averaged and expressed as (mW/cm²).

3. Results and Discussion

3.1. Characterization of Magnetic Photocatalyst of Mn-Zn Ferrite/TiO₂

The XRF analysis of Mn-Zn ferrite powder and Mn-Zn ferrite/TiO₂ is shown in Table 1. It is clear that the experimental values of magnetic powder from waste are close to the quantity used by predetermined value. The designed molar ratio would be ZnO : MnO : Fe₂O₃ = 12.5 : 35 : 52.5. By SEM micrographs, the particle size for the magnetic Mn-Zn ferrite powder is around 0.24 μm and agglomerates into a secondary particle size of approximately 2 μm [36]. TiO₂ is precipitated on the surface of the secondary particle and its size is approximately 2.5 μm (Figure 3). The EDX diagram for the Mn-Zn ferrite powder and the Mn-Zn ferrite/TiO₂ photocatalyst indicates the presence of Mn, Zn, Fe, and titanium as shown in Figure 4. The minor Zn amount existed in the magnetic photocatalysts causing the absence of Zn in Figure 4(b). The X-ray diffraction patterns of the Mn-Zn ferrite powder, sintered Mn-Zn ferrite, and magnetic photocatalysts in Figure 5 revealed that the spinel cubic ferrites and the anatase form of TiO₂ exist. All the peaks in the pattern match well with the Joint Committee of Powder Diffraction Standard (JCDDS). The sintered Mn-Zn ferrite at 1200°C (N₂) in Figure 5(b) showed the only existence of the spinel cubic structure which can be used directly in the magnetic industry. A small amount of hematite also existed in the specimens. The surface area of Mn-Zn ferrite powder by BET measurement was 8.24 m²/g and that of Mn-Zn ferrite/TiO₂ is increased to 84.98 m²/g which shows more active sites for photoreaction.

(a)

(b)

(a)

(b)

(a)

(b)

(c)

3.2. Magnetic Property

The magnetic properties of Mn-Zn ferrite powder, Mn-Zn ferrite, and Mn-Zn ferrite/TiO₂ are presented by magnetic hysteresis loops using SQUID as shown in Figure 6. The saturation magnetizations (Ms) of Mn-Zn ferrite powder (with and without calcinations) and Mn-Zn ferrite/TiO₂ are 63.15, 99.37, and 14.33 emu/g, respectively. The corresponding coercive forces () are 7.66, 4.60, and 6.13 Oe, respectively. Due to the minimal hysteresis and small , the prepared magnetic materials are all soft-magnetic materials. The magnetic property of the magnetic photocatalysts prepared from waste allows its recovery by the applied magnetic field.

3.3. Adsorption and Solar Photodegradation

The TOC and color ADMI removal percentage through the adsorption of Mn-Zn ferrite/TiO₂ from FBL simulated dye wastewater, having initial dye COD concentrations of 100, 200, 300, or 400 mg/L and the weight ratio of ferrite powder : TiO₂ maintained at 1 : 1, are shown in Figures 7 and 8. It is clear that adsorption by magnetic photocatalyst is much efficient for diluted solution but shows low efficiency for concentrated dye wastewater.

The photodegradation for simulated FBL dye wastewater with initial COD of 100, 200, 300, and 400 mg/L under solar irradiation by using self-produced magnetic photocatalysts from waste and also TiO₂ prepared is shown in Figures 9 and 10. TiO₂ was also produced by the same coprecipitation method. The degradation efficiency increased as the concentrations of pollutants decreased. For dilute pollution of FBL dye (), the TOC removal can reach 87.85% and color or ADMI removal can reach 96.17%. The treatment efficiency by Mn-Zn ferrite/TiO₂ from waste is very close to that of self-prepared TiO₂ by treating dilute simulated dye wastewater. By using TiO₂ only, TOC removal is 88% and color ADMI removal reached 96%. Both dosages of TiO₂ and magnetic photocatalysts were all 5 g/L.

3.4. Adsorption Isotherm

The Langmuir adsorption isotherm has the following equation [37]: where is the mass adsorbed per mass of adsorbent (mg/g), is the mass of the adsorbed solute required to completely saturate a unit mass of adsorbent or monolayer coverage (mg/g), is the adsorption constant (L/mg), and is the equilibrium TOC concentration of solute dye (mg/L). By plotting against for different dye concentrations, straight line was obtained as shown in Figure 11. Adsorption constants were determined by the -intercepts of the lines and were obtained from the slope. Their values were 11.53 (mg/g) for and 0.1014 (L/mg) for , respectively.

3.5. Langmuir-Hinshelwood Kinetic Model (L-H Model)

The L-H model can be expressed by the following equation [31]:where is the photocatalytic reaction constant [mg/(L-min)], is the apparent degradation rate constant (min⁻¹), and is the dye concentration, TOC (mg/L). Combining zero-order and first-order reactions, the L-H model becomes Let and ; the equation becomesBy plotting against , the straight line was obtained and shown as in Figure 12. From the slope and intercept, the kinetic constants can then be calculated.

The constants obtained from adsorption isotherm and L-H model were summarized in Table 2. The adsorption constants for both isotherm and L-H model were very close. It means that adsorption by magnetic photocatalysts occurred first and then photodegradation followed. The result also shows that the L-H kinetic model fits well for the photodegradation of FBL simulated dye wastewater.

4. Conclusions

Mn-Zn ferrite magnetic powder and the sintered Mn-Zn ferrite were successfully prepared from spent dry batteries and steel picking sulfuric waste acid. The composition obtained is close to the designed value as molar ratio of ZnO : MnO : Fe₂O₃ = 12.5 : 35 : 52.5. The sintered Mn-Zn ferrite can be used directly in magnetic industry. The magnetic photocatalyst of Mn-Zn ferrite/TiO₂ was also successfully produced by using magnetic powder, titanium sulfate, and urea as raw material and then followed by simple coprecipitation method. Comparing with JCPDS data, the XRD patterns of the photocatalyst contain Mn-Zn ferrite, anatase TiO₂, and a small amount of hematite. The magnetic photocatalyst falls into the category of soft-magnetic materials by SQUID study which can be recycled by the application of magnetic field. The treatment efficiency by magnetic photocatalyst of Mn-Zn ferrite/TiO₂ for dilute simulated FBL dye wastewater can reach 87.85% of TOC removal and 96.17% of color removal and is very close to the efficiency of using TiO₂ alone. The Mn-Zn ferrite and magnetic photocatalyst produced from waste not only solve the pollution problems but also create the possibility of the benefits for the commercial applications. Both the Langmuir adsorption isotherm and L-H model fit well for the prepared magnetic photocatalyst and can be used successfully in AOP.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This project was supported by the Ministry of Education, Taiwan, and Rui Da Hung Technology Materials Co., Ltd., Taiwan, under Contract no. 99G-39-03. The authors express sincere gratitude to the financial support for this research.

References

S. H. Lin and M. L. Chen, “Combined ozonation and ion exchange treatments of textile wastewater effluents,” Journal of Environmental Science and Health A, vol. 23, no. 7, pp. 1000–2010, 1997.
View at: Google Scholar
I. Arslan, I. A. Balcioglu, T. Tuhkanen, and D. Bahnemann, “H₂O₂/UV-C and Fe²⁺/H₂O₂/UV-C versus TiO₂/UV-A treatment for reactive dye wastewater,” Journal of Environmental Engineering, vol. 126, no. 10, pp. 903–911, 2000.
View at: Publisher Site | Google Scholar
D. Tomova, V. Iliev, S. Rakovsky, M. Anachkov, A. Eliyas, and G. L. Puma, “Photocatalytic oxidation of 2,4,6-trinitrotoluene in the presence of ozone under irradiation with UV and visible light,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 231, no. 1, pp. 1–8, 2012.
View at: Publisher Site | Google Scholar
Y. Nakamura, F. Kobayashi, M. Daidai, and A. Kurosumi, “Purification of seawater contaminated with undegradable aromatic ring compounds using ozonolysis followed by titanium dioxide treatment,” Marine Pollution Bulletin, vol. 57, no. 1–5, pp. 53–58, 2008.
View at: Publisher Site | Google Scholar
F. Gozzi, A. Machulek Jr., V. S. Ferreira et al., “Investigation of chlorimuron-ethyl degradation by Fenton, photo-Fenton and ozonation processes,” Chemical Engineering Journal, vol. 210, pp. 444–450, 2012.
View at: Publisher Site | Google Scholar
M. Karatas, Y. A. Argun, and M. E. Argun, “Decolorization of antraquinonic dye, Reactive Blue 114 from synthetic wastewater by Fenton process: kinetics and thermodynamics,” Journal of Industrial and Engineering Chemistry, vol. 18, no. 3, pp. 1058–1062, 2012.
View at: Publisher Site | Google Scholar
S. Karthikeyan, A. Titus, A. Gnanamani, A. B. Mandal, and G. Sekaran, “Treatment of textile wastewater by homogeneous and heterogeneous Fenton oxidation processes,” Desalination, vol. 281, no. 1, pp. 438–445, 2011.
View at: Publisher Site | Google Scholar
R. Liu, H. M. Chiu, C.-S. Shiau, R. Y.-L. Yeh, and Y.-T. Hung, “Degradation and sludge production of textile dyes by Fenton and photo-Fenton processes,” Dyes and Pigments, vol. 73, no. 1, pp. 1–6, 2007.
View at: Publisher Site | Google Scholar
S. S. Abu Amr and H. A. Aziz, “New treatment of stabilized leachate by ozone/Fenton in the advanced oxidation process,” Waste Management, vol. 32, no. 9, pp. 1693–1698, 2012.
View at: Publisher Site | Google Scholar
M. Čaplovičová, P. Billik, Ľ. Čaplovič et al., “On the true morphology of highly photoactive anatase TiO₂ nanocrystals,” Applied Catalysis B: Environmental, vol. 117-118, pp. 224–235, 2012.
View at: Publisher Site | Google Scholar
S. Bagwasi, B. Tian, J. Zhang, and M. Nasir, “Synthesis, characterization and application of bismuth and boron Co-doped TiO₂: a visible light active photocatalyst,” Chemical Engineering Journal, vol. 217, pp. 108–118, 2013.
View at: Publisher Site | Google Scholar
M. Khraisheh, L. Wu, A. H. Al-Muhtaseb, A. B. Albadarin, and G. M. Walker, “Phenol degradation by powdered metal ion modified titanium dioxide photocatalysts,” Chemical Engineering Journal, vol. 213, pp. 125–134, 2012.
View at: Publisher Site | Google Scholar
R. Liu, H. S. Wu, R. Yeh, C. Y. Lee, and Y. T. Hung, “Synthesis and bactericidal ability of TiO₂ and Ag-TiO₂ prepared by coprecipitation method,” International Journal of Photoenergy, vol. 2012, Article ID 640487, 7 pages, 2012.
View at: Publisher Site | Google Scholar
A. Charanpahari, S. S. Umare, S. P. Gokhale, V. Sudarsan, B. Sreedhar, and R. Sasikala, “Enhanced photocatalytic activity of multi-doped TiO₂ for the degradation of methyl orange,” Applied Catalysis A: General, vol. 443-444, pp. 96–102, 2012.
View at: Publisher Site | Google Scholar
Z. D. Meng, F. J. Zhang, L. Zhu et al., “Synthesis and characterization of M-fullerene/TiO₂ photocatalysts designed for degradation azo dye,” Materials Science and Engineering C, vol. 32, no. 8, pp. 2175–2182, 2012.
View at: Publisher Site | Google Scholar
S. Yamazaki, Y. Fujiwara, S. Yabuno, K. Adachi, and K. Honda, “Synthesis of porous platinum-ion-doped titanium dioxide and the photocatalytic degradation of 4-chlorophenol under visible light irradiation,” Applied Catalysis B: Environmental, vol. 121-122, pp. 148–153, 2012.
View at: Publisher Site | Google Scholar
B. Neppolian, A. Bruno, C. L. Bianchi, and M. Ashokkumar, “Graphene oxide based Pt-TiO₂ photocatalyst: ultrasound assisted synthesis, characterization and catalytic efficiency,” Ultrasonics Sonochemistry, vol. 19, no. 1, pp. 9–15, 2012.
View at: Publisher Site | Google Scholar
S. R. Shirsath, D. V. Pinjari, P. R. Gogate, S. H. Sonawane, and A. B. Pandit, “Ultrasound assisted synthesis of doped TiO₂ nano-particles: characterization and comparison of effectiveness for photocatalytic oxidation of dyestuff effluent,” Ultrasonics Sonochemistry, vol. 20, no. 1, pp. 277–286, 2013.
View at: Publisher Site | Google Scholar
S. Chakma and V. S. Moholkar, “Physical mechanism of sono-fenton process,” AIChE Journal, vol. 59, no. 11, pp. 4303–4313, 2013.
View at: Publisher Site | Google Scholar
S. Chakma and V. S. Moholkar, “Investigations in synergism of hybrid advanced oxidation processes with combinations of sonolysis + fenton process + UV for degradation of bisphenol A,” Industrial and Engineering Chemistry Research, vol. 53, no. 16, pp. 6855–6865, 2014.
View at: Publisher Site | Google Scholar
P. M. Botta, P. G. Bercoff, E. F. Aglietti, H. R. Bertorello, and J. M. Porto López, “Two alternative synthesis routes for MnZn ferrites using mechanochemical treatments,” Ceramics International, vol. 32, no. 8, pp. 857–863, 2006.
View at: Publisher Site | Google Scholar
A. Angermann, E. Hartmann, and J. Töpfer, “Mixed-metal carbonates as precursors for the synthesis of nanocrystalline MnZn ferrites,” Journal of Magnetism and Magnetic Materials, vol. 322, no. 21, pp. 3455–3459, 2010.
View at: Publisher Site | Google Scholar
B. S. Randhawa, H. S. Dosanjh, and M. Kaur, “Preparation of spinel ferrites from citrate precursor route-a comparative study,” Ceramics International, vol. 35, no. 3, pp. 1045–1049, 2009.
View at: Publisher Site | Google Scholar
R. Gimenes, M. R. Baldissera, M. R. A. Da Silva et al., “Structural and magnetic characterization of Mn_xZn_1−xFe₂O₄ ( $x = 0.2$ ; 0.35; 0.65; 0.8; 1.0) ferrites obtained by the citrate precursor method,” Ceramics International, vol. 38, no. 1, pp. 741–746, 2012.
View at: Publisher Site | Google Scholar
G. Xi, L. Yang, and M. Lu, “Study on preparation of nanocrystalline ferrites using spent alkaline Zn-Mn batteries,” Materials Letters, vol. 60, no. 29-30, pp. 3582–3585, 2006.
View at: Publisher Site | Google Scholar
L. Xiao, T. Zhou, and J. Meng, “Hydrothermal synthesis of Mn-Zn ferrites from spent alkaline Zn-Mn batteries,” Particuology, vol. 7, no. 6, pp. 491–495, 2009.
View at: Publisher Site | Google Scholar
J. Azadmanjiri, “Preparation of Mn-Zn ferrite nanoparticles from chemical sol-gel combustion method and the magnetic properties after sintering,” Journal of Non-Crystalline Solids, vol. 353, no. 44-46, pp. 4170–4173, 2007.
View at: Publisher Site | Google Scholar
X. Cao, G. Liu, Y. Wang, J. Li, and R. Hong, “Preparation of octahedral shaped Mn_0.8Zn_0.2Fe₂O₄ ferrites via co-precipitation,” Journal of Alloys and Compounds, vol. 497, no. 1-2, pp. L9–L12, 2010.
View at: Publisher Site | Google Scholar
P. P. Goswami, H. A. Choudhury, S. Chakma, and V. S. Moholkar, “Sonochemical synthesis of cobalt ferrite nanoparticles,” International Journal of Chemical Engineering, vol. 2013, Article ID 934234, 6 pages, 2013.
View at: Publisher Site | Google Scholar
P. P. Goswami, H. A. Choudhury, S. Chakma, and V. S. Moholkar, “Sonochemical synthesis and characterization of manganese ferrite nanoparticles,” Industrial & Engineering Chemistry Research, vol. 52, no. 50, pp. 17848–17855, 2013.
View at: Publisher Site | Google Scholar
M. Ma, Y. Zhang, X. Li, D. Fu, H. Zhang, and N. Gu, “Synthesis and characterization of titania-coated Mn-Zn ferrite nanoparticles,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 224, no. 1–3, pp. 207–212, 2003.
View at: Publisher Site | Google Scholar
F. Chen and J. Zhao, “Preparation and photocatalytic properties of a novel kind of loaded photocatalyst of TiO₂/SiO₂/γ-Fe₂O₃,” Catalysis Letters, vol. 58, no. 4, pp. 245–247, 1999.
View at: Publisher Site | Google Scholar
Y. Gao, B. Chen, H. Li, and Y. Ma, “Preparation and characterization of a magnetically separated photocatalyst and its catalytic properties,” Materials Chemistry and Physics, vol. 80, no. 1, pp. 348–355, 2003.
View at: Publisher Site | Google Scholar
Y.-P. Fu, W.-K. Chang, H.-C. Wang, C.-W. Liu, and C.-H. Lin, “Synthesis and characterization of anatase TiO₂ nanolayer coating on Ni-Cu-Zn ferrite powders for magnetic photocatalyst,” Journal of Materials Research, vol. 25, no. 1, pp. 134–140, 2010.
View at: Publisher Site | Google Scholar
APHA, Standard Methods for the Examination of Water and Wastewater, American Public Health Association/American Water Works Association/Water Environment Federation, Washington, DC, USA, 21th edition, 2003.
C. F. Wu, Preparation characterization and application of Mn-Zn ferrite powders and magnetic titanium dioxide from used dry batteries and spent steel pickling liquids [M.S. thesis], Department of Chemical and Materials Engineering, Minghsin University of Science and Technology, Hsinchu, Taiwan, 2012.
R. Y. L. Yeh and A. Thomas, “Color removal from dye wastewaters by adsorption using powdered activated carbon: mass transfer studies,” Journal of Chemical Technology and Biotechnology, vol. 63, no. 1, pp. 48–54, 1995.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2015 Robert Liu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1372

Downloads

1627

Citations

Journal of Nanomaterials

Degradation of FBL Dye Wastewater by Magnetic Photocatalysts from Scraps

Abstract

1. Introduction

2. Materials and Methods

2.1. Preparation of Magnetic Mn-Zn Ferrite Powder and Magnetic Photocatalyst

2.2. Characterization

2.3. Adsorption and Photocatalytic Degradation

3. Results and Discussion

3.1. Characterization of Magnetic Photocatalyst of Mn-Zn Ferrite/TiO2

3.2. Magnetic Property

3.3. Adsorption and Solar Photodegradation

3.4. Adsorption Isotherm

3.5. Langmuir-Hinshelwood Kinetic Model (L-H Model)

4. Conclusions

Conflict of Interests

Acknowledgments

References

Copyright

3.1. Characterization of Magnetic Photocatalyst of Mn-Zn Ferrite/TiO₂