The Core/Shell Structure of CdSe/ZnS Quantum Dots Characterized by X-Ray Absorption Fine Spectroscopy

Wei, Huijing; Zhou, Jing; Zhang, Linjuan; Wang, Fang; Wang, Jianqiang; Jin, Chan

doi:https://doi.org/10.1155/2015/764712

Journal of Nanomaterials

On this page

Abstract Introduction Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Special Issue

Quantum Dots and Nanoparticles in Light Emitting Diodes, Displays, and Optoelectronic Devices

View this Special Issue

Research Article | Open Access

Volume 2015 | Article ID 764712 | https://doi.org/10.1155/2015/764712

The Core/Shell Structure of CdSe/ZnS Quantum Dots Characterized by X-Ray Absorption Fine Spectroscopy

Huijing Wei,^1,2Jing Zhou,²Linjuan Zhang,²Fang Wang,¹Jianqiang Wang,²and Chan Jin²

Academic Editor: Hsueh-Shih Chen

Received15 Dec 2014

Revised09 Feb 2015

Accepted17 Feb 2015

Published27 Aug 2015

Abstract

Understanding the chemical and physical properties of core/shell nanocrystal quantum dots (QDs) is key for their use in light-emission applications. In this paper, a single-step injection-free scalable synthetic method is applied to prepare high-quality core/shell QDs with emission wavelengths of 544 nm, 601 nm, and 634 nm. X-ray absorption fine structure spectra are used to determine the core/shell structure of CdSe/ZnS quantum dots. Moreover, theoretical XANES spectra calculated by FEFF.8.20 are used to determine the structure of Se and S compounds. The QD samples displayed nearly spherical shapes with diameters of approximately 3.4 ± 0.5 nm (634 nm), 4.5 ± 0.4 nm (601 nm), and 5.5 ± 0.5 nm (544 nm). With XANES results and MS calculations, it is indicated that sphalerite ZnS capped with organic sulfur ligands should be the shell structure. Wurtzite CdSe is the main core structure with a Cd-Se bond length of 2.3 Å without phase shift. This means that different emission wavelengths are only due to the crystal size with single-step injection-free synthesis. Therefore, single-step injection-free synthesis could generate a nearly ideal core/shell structure of CdSe/ZnS QDs capped with an organic sulfur ligand.

1. Introduction

Over the last 30 years, a significant amount of research has been reported regarding quantum dot (QD) synthesis. The fundamental physical properties and potential applications of quantum dots include multiplexed labeling and tracking of cells or molecules in a biological environment, downshifting light for color engineering in solid-state lighting, illumination and displays, and single-photon sources. Among various semiconductor materials, CdSe has been most extensively studied because its size-dependent photoluminescence is tunable across the visible spectrum [1–5], but it is insufficiently stable and is sensitive to the processing conditions and the environment [6, 7]. To address these disadvantages, scientists have focused on the development of core/shell QDs, which incorporate a shell of wider band gap semiconductor materials around the QD cores [8–13]. These core/shell QDs have been shown to be generally more robust against chemical degradation and photooxidation [14–17].

Knowledge of the chemical and physical properties of semiconductor nanocrystals is a key issue in understanding the mechanisms of the dots formation and their position correlations. Many techniques have been used to determine information on their structural properties and ordering phenomena [18–21]. Element sensitive transmission electron microscopy (TEM) studies have provided information about the CdSe core structure and the surrounding ZnSe shells [22]. The CdSe/ZnS core/shell structure was elucidated using high-resolution TEM/STEM [20, 23]. The structure of core/shell/shell CdSe/ZnSe/ZnS QDs was also studied using photoluminescence spectroscopy [24]. Recently, the structural evolution of the interfaces in CdSe/CdS and CdSe/Cd_0.5Zn_0.5S colloidal QDs was investigated using surface-enhanced Raman spectroscopy [25]. However, not all of these techniques can reveal structural properties. Because of the small scattering volume of CdSe/ZnS QDs, it is not possible to obtain any information using high-resolution X-ray diffraction (HRXRD). Therefore, the understanding of the local structure of these QDs and their environments is still rudimentary.

X-ray absorption near edge structure (XANES) [26–28] and extended X-ray absorption fine structure (EXAFS) [29, 30] are sensitive to the oxidation state/site symmetry of elements and to the local structure around a selected atom. Recently, the core/shell structure of CdSe_xS_1−x QDs was explored using XANES and EXAFS [31]. The local structure of CdSe/ZnSe QDs was analyzed using EXAFS and diffraction anomalous fine structure (DAFS). XANES is largely a fingerprint for the oxidation state and site symmetry of an element. Meanwhile, theoretical XANES spectra were calculated using the ab initio multiple-scattering code FEFF8.20 [32, 33]. Comparing the theoretical spectra with the experimental spectra can reveal detailed structural information about QDs. Therefore, we use both XAFS experimental data and XANES theoretical calculations to probe the fine structure of QDs obtained from a single-step injection-free synthesis.

In the previous work [12], we developed a single-step injection-free synthesis of high-quality core/shell QDs. We considered the QDs structure to be CdSe/Zn_xCd_1−xS. However, it is difficult to collect detailed structural information using conventional test methods. In this paper, the structural information of QDs is confirmed using EXAFS and XANES with MS calculations.

2. Experiment Section

2.1. Chemicals

Cadmium oxide (CdO, 99.99%), selenium powder (Se, 100 mesh, 99.5%), zinc nitrate hexahydrate (Zn(NO₃)₂·6H₂O, 98%), zinc acetate (Zn(OAc)₂, 99.99%), sulfur powder (S, 99.98%), stearic acid (SA, 95%), and 1-octadecene (ODE, 90%) were purchased from Aldrich.

2.2. QD Synthesis

The QDs were synthesized using a modification of Zhang’s method [12]. First, CdO (0.205 g, 1.6 mmol), Zn(NO₃)₂·6H₂O (0.238 g, 0.8 mmol), Se (0.032 g, 0.4 mmol), and S (0.026 g, 0.8 mmol) were added to a solution of TOP and SA in 20 mL of 1-octadecene (ODE) in a 100-mL three-necked flask, which was fitted with a heating mantle, a condenser, and a temperature probe. Then, the mixture was heated to 250°C at a heating rate of 20–40°C/min under a nitrogen atmosphere.

QDs with an emission wavelength of 544 nm were obtained by adding 0.3 mL TOP and 1.14 g (4 mmol) SA. QDs with an emission wavelength of 601 nm were obtained by adding 0.4 mL TOP and 1.71 g (6 mmol) SA. QDs with an emission wavelength of 534 nm were obtained by adding 3.0 mL TOP and 0.99 g (3.5 mmol) SA and substituting Zn(NO₃)₂ with Zn(OAc)₂.

2.3. Characterization

Photoluminescence spectra (PL spectra) were obtained using an LS-45 (PerkinElmer) fluorescence spectrophotometer. Transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) images were acquired using a field emission TEM (a FEI Tecnai G2 F20 S-Twin, 200 kV).

X-ray absorption fine spectroscopy (XAFS) data for the Se and Cd K-edge were collected on Beamline BL14W1 at the Shanghai Synchrotron Radiation Facility (SSRF). The incident radiation was filtered using a Si (311) double-crystal monochromator with a suppression mirror system for focusing and harmonic rejection. All data were taken in transmission mode using an Oxford ion gas chamber. The Se K-edge spectra were calibrated by defining the zero crossing point of the second derivative of the XANES spectra for the Se reference foils as 12658 eV, and the Cd K-edge spectra were calibrated by defining the zero crossing point of the second derivative of the XANES spectra for the Cd reference foil as 26711 eV. The S K-edge X-ray absorption near edge structure (XANES) spectra were collected on Beamline 4B7A at the Beijing Synchronization Radiation Facility (BSRF). The sulfur K-edge spectrum of the QDs was obtained using a double-crystal monochromator (DCM) and recorded in X-ray fluorescence yield (XFY) mode. The XAFS and XANES data were analyzed using the IFEFFIT software [34], and the cluster size dependence was determined using the ab initio multiple-scattering code FEFF8.20 [32, 33].

3. Results and Discussion

3.1. Optical Properties

The nanocrystal quantum dots (QDs) were synthesized using the single-step injection-free approach, as shown in Figure 1(a), which produced high-quality core/shell QDs [12]. The detailed procedures are described in the materials and methods. Briefly, CdO, Zn(NO₃)₂, Se, and S were combined in an ODE solution containing TOP and SA at room temperature and then heated to 250°C under stirring. As shown in Figures 1(b)-1(c), the three samples have different colors under a UV lamp with emission wavelengths of 544 nm (green), 601 nm (yellow), and 634 nm (red). The symmetric and narrow band edge PL emission peak in the PL spectra indicates that the particle sizes and shapes are nearly uniform [12].

3.2. Morphology of Obtained QDs

The characterization of QD samples with three different emission wavelengths was performed using TEM and HRTEM, as shown in Figure 2. At different growth stages, the QD samples displayed nearly spherical shapes with diameters of approximately nm (634 nm), nm (601 nm), and nm (544 nm).

(a)

(b)

(c)

3.3. Structural Characterization of the QDs

To understand the relationship between the structure and the variation in the optical properties of the three QDs samples, X-ray absorption spectroscopy (XAS) was employed. X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) data reduction was conducted using standard procedures [35]. XANES is largely a fingerprint for the oxidation state and site symmetry of the elements.

The S K-edge XANES spectra were collected to determine the S compounds in the QD samples. Figure 3(a) shows the S K-edge XANES spectra of the three QDs with emission wavelengths of 544 nm, 601 nm, and 634 nm. Two strong peaks are observed in the S K-edge spectra of the three samples. The first peak (A) is at approximately 2472 eV with two small shoulder peaks (2474 eV and 2476 eV), and the second peak (D) is at approximately 2482 eV. This strong peak, indicated by the white line, arises from the 1s to 3p transition. The white-line energy shift is closely related to the oxidation state of sulfur. The energy shift of the white line in the S K-edge XANES spectra shows a nearly linear dependence on the oxidation state and varies by approximately 12.0 eV from S⁻² to S⁺⁶ [36]. Thus, the first peak (A) in our samples might incorporate contributions from S⁻², while the second peak (D) comes from S⁺⁴ or S⁺⁶. The possible sulfur compounds in S⁻² are ZnS, CdS, and Zn_xCd_1−xS, but it is difficult to distinguish these three sulfur compounds in the S K-edge XANES spectra. Additionally, organic sulfur ligands with sulfur in the S⁺⁴ or S⁺⁶ state cap the QDs.

(a)

(b)

(c)

To distinguish the structure of S in the obtained QD samples, we performed MS calculations of the S K-edge XANES in sphalerite ZnS (Figure 3(b)) and CdS (Figure 3(c)) using different clusters [37]. For ZnS, using a central sulfur atom, the first shell contains only four coordinated zinc atoms and makes only a small contribution to the features of the spectrum. The 17-atom cluster gives rise to the white-line peak A, demonstrating the influence of the relatively strong backscattering of the S⁻² ions [38]. Features B and C were reproduced using clusters larger than 99 atoms, which include atoms up to 6 from the central sulfur atom, indicating that these peaks arise from “medium-range” contributions. There is a white peak A and a shoulder peak B/C in the S K-edge XANES spectra, which indicates that ZnS should be a major component of the samples. The zinc-blend structure of CdS is stable at room temperature but transforms to the wurtzite phase above °C [31]. Therefore, we performed MS calculations of the S K-edge XANES in the wurtzite phase of CdS. For CdS, with a central sulfur atom, the first shell contains only four coordinated cadmium atoms and only makes a small contribution to the features of the spectrum. Prepeak A, the white-line peak B, and shoulder peak C were produced in clusters larger than 92 atoms. Therefore, no prepeak A or shoulder peak C was observed in the S K-edge XANES spectra of the QD samples. Additionally, the white-line peak in CdS is in almost the same position as ZnS. Thus, we suggest that no CdS compounds exist in the obtained samples.

The Cd K-edge XANES spectra were also collected to determine the Cd compounds in the QD samples. Figure 4 shows the Fourier transform (FT) magnitudes of the -weighted χ(k) function using a Kaiser-Bessel window and the k-range of 2.8–10.5 for all samples. There are two peaks at approximately 1.7 Å and 2.3 Å without a phase shift. Based on previous results [21, 31, 39–41], the Cd-Se bond has a peak between 2.0 and 3.2 Å in the Cd K-edge RSF function. In our results, there is a peak at approximately 2.3 Å without a phase shift, which was confirmed to be from the Cd-Se bond. Furthermore, there is a strong peak at approximately 1.7 Å without a phase shift, which can be ascribed to the Cd-O bond of TOPO-Cd [42]. In the case of the Cd : Se = 4 : 1 system, the extra Cd atoms cap the CdSe with TOPO attached to both free Cd and CdSe. Meanwhile, as the concentrations of TOP and SA increase, the Cd-O peak intensity decreases gradually, and the Cd-Se peak intensity simultaneously increases, which implies that higher TOP and SA concentrations facilitate the conversion of TOPO-Cd into CdSe. Based on the above results, the CdSe is considered the core of the obtained QDs and has a wurtzite structure. The Cd atoms are located at the tetrahedral sites of a face-centered cubic structure that consists of Se atoms.

The white lines and intensities in the Se K-edge XANES spectra of the QD samples (Figure 5(a)) are similar, indicating that the Se compounds in the three samples are nearly identical. With previous work [8, 43–45], we considered that CdSe was the only compound for element Se in the QD samples. To distinguish the scattering contributions from the different coordination shells of CdSe, which has a wurtzite structure above °C [46], MS calculations of the Se K-edge XANES spectra were performed using different clusters, as shown in Figure 5(b). The results indicate that the XANES spectra for the 5-atom and 17-atom clusters with one and two shells are significantly different from the 29-atom cluster and larger clusters with more than three shells. Compared with the XANES spectra of three samples, the results indicate that the QDs samples have more than 47 atoms, and the small clusters are in wurtzite structures.

(a)

(b)

Three QD samples with different emission wavelengths were obtained using the single-step injection-free synthesis. CdSe compounds with the narrowest band gap of 2.25 eV [47, 48] exist in the center of the QD samples as the core structures. Meanwhile, ZnS compounds comprised the shell structures. Furthermore, the CdSe core structure has a wurtzite structure with a Cd-Se bond length of 2.3 Å without phase shift, and the ZnS has a sphalerite structure. The core structure and shell structure are almost identical for the three different QD samples, which might be caused by the reaction stages. The single-step injection-free synthesis method combines all of the reactants in an ODE solution, which is then heated to 250°C with stirring. When the temperature is greater than °C, CdSe exists only in the wurtzite phase. Based on this synthetic method, it can be concluded that the change in the QD emission wavelength is only caused by the size change due to the TOP and SA concentrations. Therefore, the single-step injection-free synthesis can generate a nearly ideal core/shell structure of CdSe/ZnS QDs capped with sulfur organic ligands, and it can tune the emission wavelength from violet to near infrared.

4. Conclusions

A single-step injection-free scalable synthetic method was used to prepare core/shell QDs with different emission wavelengths. The core/shell structure of the QDs with three different emission wavelengths (544 nm, 601 nm, and 644 nm) was performed using EXAFS and XANES with MS calculations. The structure of the CdSe (core) and ZnS (shell) in the three QD samples is nearly identical. The XAFS results show that CdSe is the main core component with a wurtzite structure and a Cd-Se bond length of 2.3 Å without phase shift. They also indicate that the ZnS has a sphalerite structure, and the shell structure is capped with organic sulfur ligands with sulfur in the S⁺⁴ or S⁺⁶ state. Based on this synthetic method, it could be concluded that the changes in the QD emission wavelengths are only caused by the size changes of the nanocrystal, due to the TOP and SA concentrations. Therefore, this single-step injection-free synthesis could generate nearly ideal core/shell CdSe/ZnS QDs capped with organic sulfur ligands.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work was financially supported by the National Key Technology R&D Program (31-1122ZCKF), the State Key Development Program for Basic Research of China (2011BAK15B04), Natural Science Foundation of China (11105221), and the State Key Development Program for Basic Research of China (Grant no. 2010CB934501).

References

D. C. Hannah, N. J. Dunn, S. Ithurria et al., “Observation of size-dependent thermalization in CdSe nanocrystals using time-resolved photoluminescence spectroscopy,” Physical Review Letters, vol. 107, no. 17, Article ID 177403, 2011.
View at: Publisher Site | Google Scholar
E. A. Weiss, R. C. Chiechi, S. M. Geyer et al., “Size-dependent charge collection in junctions containing single-size and multi-size arrays of colloidal CdSe quantum dots,” The Journal of the American Chemical Society, vol. 130, no. 1, pp. 74–82, 2008.
View at: Publisher Site | Google Scholar
D. Katz, T. Wizansky, O. Millo, E. Rothenberg, T. Mokari, and U. Banin, “Size-dependent tunneling and optical spectroscopy of CdSe quantum rods,” Physical Review Letters, vol. 89, no. 8, Article ID 086801, 2002.
View at: Publisher Site | Google Scholar
M. E. Schmidt, S. A. Blanton, M. A. Hines, and P. Guyot-Sionnest, “Size-dependent two-photon excitation spectroscopy of CdSe nanocrystals,” Physical Review B: Condensed Matter and Materials Physics, vol. 53, no. 19, pp. 12629–12632, 1996.
View at: Publisher Site | Google Scholar
A. L. Rogach, A. Kornowski, M. Gao, A. Eychmüller, and H. Weller, “Synthesis and characterization of a size series of extremely small thiol-stabilized CdSe nanocrystals,” The Journal of Physical Chemistry B, vol. 103, no. 16, pp. 3065–3069, 1999.
View at: Publisher Site | Google Scholar
P. Reiss, M. Protiere, and L. Li, “Core/shell semiconductor nanocrystals,” Small, vol. 5, no. 2, pp. 154–168, 2009.
View at: Publisher Site | Google Scholar
M. D. Regulacio and M.-Y. Han, “Composition-tunable alloyed semiconductor nanocrystals,” Accounts of Chemical Research, vol. 43, no. 5, pp. 621–630, 2010.
View at: Publisher Site | Google Scholar
W. Zhang, G. Chen, J. Wang, B.-C. Ye, and X. Zhong, “Design and synthesis of highly luminescent near-infrared-emitting water-soluble CdTe/CdSe/ZnS Core/Shell/Shell quantum dots,” Inorganic Chemistry, vol. 48, no. 20, pp. 9723–9731, 2009.
View at: Publisher Site | Google Scholar
J. van Embden, J. Jasieniak, and P. Mulvaney, “Mapping the optical properties of CdSe/CdS heterostructure nanocrystals: the effects of core size and shell thickness,” Journal of the American Chemical Society, vol. 131, no. 40, pp. 14299–14309, 2009.
View at: Publisher Site | Google Scholar
B. J. Walker, P. M. Allen, and M. G. Bawendi, Abstracts of Papers of the American Chemical Society, American Chemical Society, 2010.
J. R. Dethlefsen and A. Dossing, “Preparation of a ZnS shell on CdSe quantum dots using a single-molecular ZnS precursor,” Nano Letters, vol. 11, no. 5, pp. 1964–1969, 2011.
View at: Publisher Site | Google Scholar
W. Zhang, H. Zhang, Y. Feng, and X. Zhong, “Scalable single-step noninjection synthesis of high-quality core/shell quantum dots with emission tunable from violet to near infrared,” ACS Nano, vol. 6, no. 12, pp. 11066–11073, 2012.
View at: Publisher Site | Google Scholar
W. Zhang, C. Jin, Y. Yang, and X. Zhong, “Noninjection facile synthesis of gram-scale highly luminescent CdSe multipod nanocrystals,” Inorganic Chemistry, vol. 51, no. 1, pp. 531–535, 2012.
View at: Publisher Site | Google Scholar
J. Hensel, G. Wang, Y. Li, and J. Z. Zhang, “Synergistic effect of CdSe quantum dot sensitization and nitrogen doping of TiO₂ nanostructures for photoelectrochemical solar hydrogen generation,” Nano Letters, vol. 10, no. 2, pp. 478–483, 2010.
View at: Publisher Site | Google Scholar
J. Wang, I. Mora-Seró, Z. Pan et al., “Core/shell colloidal quantum dot exciplex states for the development of highly efficient quantum-dot-sensitized solar cells,” Journal of the American Chemical Society, vol. 135, no. 42, pp. 15913–15922, 2013.
View at: Publisher Site | Google Scholar
A. Salant, M. Shalom, I. Hod, A. Faust, A. Zaban, and U. Banin, “Quantum dot sensitized solar cells with improved efficiency prepared using electrophoretic deposition,” ACS Nano, vol. 4, no. 10, pp. 5962–5968, 2010.
View at: Publisher Site | Google Scholar
L. Liu, J. Hensel, R. C. Fizmorris, Y. Li, and J. J. Zhang, “Preparation and photoelectrochemical properties of CdSe/TiO₂ hybrid mesoporous structures,” The Journal of Physical Chemistry Letters, vol. 1, no. 1, pp. 155–160, 2010.
View at: Publisher Site | Google Scholar
T. Schmidt, T. Clausen, J. Falta et al., “Correlated stacks of CdSe/ZnSSe quantum dots,” Applied Physics Letters, vol. 84, no. 22, pp. 4367–4369, 2004.
View at: Publisher Site | Google Scholar
T. Schmidt, E. Roventa, T. Clausen et al., “Ordering mechanism of stacked CdSe Zn/S_xSe_1−x quantum dots: a combined reciprocal-space and real-space approach,” Physical Review B—Condensed Matter and Materials Physics, vol. 72, no. 19, Article ID 195334, 2005.
View at: Publisher Site | Google Scholar
M. A. van Huis, A. van Veen, H. Schut, S. W. H. Eijt, B. J. Kooi, and J. T. M. de Hosson, “Electron microscopy and positron annihilation study of CdSe nanoclusters embedded in MgO,” Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, vol. 218, no. 1–4, pp. 410–415, 2004.
View at: Publisher Site | Google Scholar
A. Demourgues, G. N. Greaves, R. Bilsborrow, G. Baker, A. Sery, and B. Speit, “XAFS study of CdSe quantum dots in a silicate glass,” Nuclear Instruments and Methods in Physics Research B, vol. 97, no. 1–4, pp. 166–168, 1995.
View at: Publisher Site | Google Scholar
D. Litvinov, A. Rosenauer, D. Gerthsen, and N. N. Ledentsov, “Character of the Cd distribution in ultrathin CdSe layers in a ZnSe matrix,” Physical Review B: Condensed Matter and Materials Physics, vol. 61, no. 24, pp. 16819–16826, 2000.
View at: Publisher Site | Google Scholar
H. Shin, D. Jang, Y. Jang, M. Cho, and K. Park, “High resolution imaging analysis of CdSe/ZnS core-shell quantum dots (QDs) using Cs-corrected HR-TEM/STEM,” Journal of Materials Science: Materials in Electronics, vol. 24, no. 10, pp. 3744–3748, 2013.
View at: Publisher Site | Google Scholar
B. C. Fitzmorris, J. K. Cooper, J. Edberg, S. Gul, J. Guo, and J. Z. Zhang, “Synthesis and structural, optical, and dynamic properties of core/shell/shell CdSe/ZnSe/ZnS quantum dots,” Journal of Physical Chemistry C, vol. 116, no. 47, pp. 25065–25073, 2012.
View at: Publisher Site | Google Scholar
A. M. Kelley, Q. Q. Dai, Z.-J. Jiang, J. A. Baker, and D. F. Kelley, “Resonance Raman spectra of wurtzite and zincblende CdSe nanocrystals,” Chemical Physics, vol. 422, pp. 272–276, 2013.
View at: Publisher Site | Google Scholar
S. Tanaka, M. Kitta, T. Tamura, T. Akita, Y. Maeda, and M. Kohyama, “First-principles calculations of O-K ELNES/XANES of lithium titanate,” Journal of Physics D: Applied Physics, vol. 45, no. 49, Article ID 494004, 2012.
View at: Publisher Site | Google Scholar
H. Murata, K. Shitara, I. Tanaka, A. Nakahira, T. Mizoguchi, and K. Matsunaga, “First-principles calculations of Zn-K XANES in Ca-deficient hydroxyapatite,” Journal of Physics: Condensed Matter, vol. 22, no. 38, Article ID 384213, 2010.
View at: Publisher Site | Google Scholar
D. Cabaret, F. Mauri, and G. S. Henderson, “Oxygen K-edge XANES of germanates investigated using first-principles calculations,” Physical Review B: Condensed Matter and Materials Physics, vol. 75, no. 18, Article ID 184205, 2007.
View at: Publisher Site | Google Scholar
P. H. Citrin, “Basic principles of exafs applied to simple and complex systems,” Bulletin of the American Physical Society, vol. 22, no. 3, p. 359, 1977.
View at: Google Scholar
V. Krishnan, M. P. Feth, E. Wendel, Y. Chen, M. Hanack, and H. Bertagnolli, “EXAFS spectroscopy—fundamentals, measurement techniques, data evaluation and applications in the field of phthalocyanines,” Zeitschrift für Physikalische Chemie, vol. 218, no. 1, pp. 1–15, 2004.
View at: Publisher Site | Google Scholar
L. Y. Chen, C. H. Chen, C. H. Tseng, F. L. Lai, and B. J. Hwang, “Synthesis CdSe_xS_1−x core/shell type quantum dotsvia one injection method,” Chemical Communications, vol. 47, no. 5, pp. 1592–1594, 2011.
View at: Publisher Site | Google Scholar
K. Nakanishi and T. Ohta, “Verification of the FEFF simulations to K-edge XANES spectra of the third row elements,” Journal of Physics: Condensed Matter, vol. 21, no. 10, Article ID 104214, 2009.
View at: Publisher Site | Google Scholar
E. Bosman and J. Thieme, “Modeling of XANES-spectra with the FEFF-program,” in Proceedings of the 9th International Conference on X-Ray Microscopy, vol. 186, Zurich, Switzerland, July 2009.
View at: Google Scholar
M. Newville, “IFEFFIT: interactive XAFS analysis and FEFF fitting,” Journal of Synchrotron Radiation, vol. 8, no. 2, pp. 322–324, 2001.
View at: Publisher Site | Google Scholar
H. L. Bao, J. Li, L. H. Jiang et al., “Structure of PtnNi nanoparticles electrocatalysts investigated by X-ray absorption spectroscopy,” Journal of Physical Chemistry C, vol. 117, no. 40, pp. 20584–20591, 2013.
View at: Publisher Site | Google Scholar
G. P. Huffman, F. E. Huggins, N. Shah et al., “Characterization of fine particulate matter produced by combustion of residual fuel oil,” Journal of the Air and Waste Management Association, vol. 50, no. 7, pp. 1106–1114, 2000.
View at: Publisher Site | Google Scholar
Z. Y. Wu, G. Ouvrard, S. Lemaux et al., “Sulfur K-edge X-ray-absorption study of the charge transfer upon lithium intercalation into titanium disulfide,” Physical Review Letters, vol. 77, no. 10, pp. 2101–2104, 1996.
View at: Publisher Site | Google Scholar
F. E. Huggins, N. Shah, G. P. Huffman, and J. D. Robertson, “XAFS spectroscopic characterization of elements in combustion ash and fine particulate matter,” Fuel Processing Technology, vol. 65, pp. 203–218, 2000.
View at: Publisher Site | Google Scholar
M. Uehara, Z. H. Sun, H. Oyanagi et al., “In situ extended x-ray absorption fine structure study of initial processes in CdSe nanocrystals formation using a microreactor,” Applied Physics Letters, vol. 94, no. 6, Article ID 063104, 2009.
View at: Publisher Site | Google Scholar
Z. H. Sun, H. Oyanagi, M. Uehara et al., “Study on initial kinetics of CdSe nanocrystals by a combination of in situ X-ray absorption fine structure and microfluidic reactor,” The Journal of Physical Chemistry C, vol. 113, no. 43, pp. 18608–18613, 2009.
View at: Publisher Site | Google Scholar
E. Piskorska-Hommel, V. Holý, O. Caha et al., “Complementary information on CdSe/ZnSe quantum dot local structure from extended X-ray absorption fine structure and diffraction anomalous fine structure measurements,” Journal of Alloys and Compounds, vol. 523, pp. 155–160, 2012.
View at: Publisher Site | Google Scholar
S. N. Sharma, H. Sharma, G. Singh, and S. M. Shivaprasad, “Low energy ion induced effects on TOPO capped CdSe nanocrystals probed by XPS depth profiling and optical measurements,” Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms, vol. 244, no. 1, pp. 86–90, 2006.
View at: Publisher Site | Google Scholar
Z. Fang, L. Liu, J. Wang, and X. Zhong, “Depositing a ZnxCd1-xS shell around cdse core nanocrystals via a noninjection approach in aqueous media,” Journal of Physical Chemistry C, vol. 113, no. 11, pp. 4301–4306, 2009.
View at: Publisher Site | Google Scholar
X. H. Zhong, Y. Y. Feng, and Y. L. Zhang, “Facile and reproducible synthesis of red-emitting CdSe nanocrystals in amine with long-term fixation of particle size and size distribution,” The Journal of Physical Chemistry C, vol. 111, no. 2, pp. 526–531, 2007.
View at: Publisher Site | Google Scholar
X. H. Zhong, R. G. Xie, Y. Zhang, T. Basché, and W. Knoll, “High-quality violet- to red-emitting ZnSe/CdSe core/shell nanocrystals,” Chemistry of Materials, vol. 17, no. 16, pp. 4038–4042, 2005.
View at: Publisher Site | Google Scholar
K. B. Subila, G. K. Kumar, S. M. Shivaprasad, and K. G. Thomas, “Luminescence properties of CdSe quantum dots: role of crystal structure and surface composition,” Journal of Physical Chemistry Letters, vol. 4, no. 16, pp. 2774–2779, 2013.
View at: Publisher Site | Google Scholar
K. Tvrdy, P. A. Frantsuzov, and P. V. Kamat, “Photoinduced electron transfer from semiconductor quantum dots to metal oxide nanoparticles,” Proceedings of the National Academy of Sciences of the United States of America, vol. 108, no. 1, pp. 29–34, 2011.
View at: Publisher Site | Google Scholar
Z. Pan, K. Zhao, J. Wang, H. Zhang, Y. Feng, and X. Zhong, “Near infrared absorption of ${C d S e}_{x}$ ${T e}_{1 - x}$ alloyed quantum dot sensitized solar cells with more than 6% efficiency and high stability,” ACS Nano, vol. 7, no. 6, pp. 5215–5222, 2013.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2015 Huijing Wei et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

4789

Downloads

1898

Citations