Synthesis and Characterization of Nanocrystalline Ni₅₀Al_50−xMo_x (x = 0–5) Intermetallic Compound during Mechanical Alloying Process

Figure 6

Changes of NiAl lattice parameter after 128 h of milling for the 5 samples with 0, 0.5, 1, 2.5, and 5 at.% Mo.