Preparation and Properties of PTFE-PMMA Core-Shell Nanoparticles and Nanocomposites
Table 3
Dynamic storage modulus in the glassy (50°C) and rubbery (200°C) state and glass transition temperatures from the maximum in the peak.
| Sample | glassy state 50°C (GPa) | rubbery state 200°C (MPa) |
(°C) |
| PMMA | 2.6 | 4.3 | 142 | BPM4 (3%) | 2.8 | 6.9 | 146 | BPM5 (6%) | 2.8 | 8.8 | 148 | BPM6 (12%) | 3.0 | 9.0 | 148 | BPM7 (18%) | 3.3 | 9.4 | 149 | BPM8 (30%) | 3.4 | 12.6 | 148 | BPM9 (40%) | 2.8 | 14.3 | 149 | BPM10 (50%) | 2.9 | 15.9 | 149 | BPM11 (60%) | 3.1 | 18.9 | 146 |
|
|