Fabrication of Surface Level Cu/SiCp Nanocomposites by Friction Stir Processing Route
Figure 4
(a) Temperature distribution profile for sample at 750 rpm/20 mm/min/2° and (b) peak temperature history during FSP runs in advancing and retreating side.