Research Article
Fabrication of Surface Level Cu/SiCp Nanocomposites by Friction Stir Processing Route
Figure 6
Optical micrographs of nanocomposites at (a–c) the interface between SZ and BM and (d–f) SZ region at different parameter combinations.
(a) 500 rpm/20 mm/min/1° |
(b) 750 rpm/50 mm/min/0° |
(c) 1000 rpm/20 mm/min/1° |
(d) 500 rpm/20 mm/min/1° |
(e) 750 rpm/20 mm/min/2° |
(f) 1000 rpm/20 mm/min/1° |