Research Article
Optimization of Conductive Thin Film Epoxy Composites Properties Using Desirability Optimization Methodology
Table 2
The experimental design and actual responses of MWCNTs/epoxy thin film composites.
| Run number | Variables in decoded levels | Actual responses | Sonication duration (min)
| Filler loadings (vol%)
| Tensile strength (MPa)
| Elastic modulus (MPa)
| Elongation at break (%)
| Thermal conductivity (W/mK)
| Electrical conductivity (ohm−1 m−1)
|
| 1 | 35 | 1.0 | 48.31 | 2140.80 | 2.91 | 0.05995 | 2.75 × 10−10 | 2 | 35 | 1.5 | 53.42 | 2221.40 | 2.90 | 0.06345 | 3.94 × 10−10 | 3 | 5 | 1.0 | 22.74 | 1217.66 | 2.41 | 0.05518 | 2.15 × 10−8 | 4 | 20 | 1.0 | 40.65 | 1779.00 | 2.88 | 0.05669 | 7.62 × 10−6 | 5 | 5 | 2.0 | 20.36 | 1163.40 | 2.19 | 0.09750 | 4.71 × 10−8 | 6 | 35 | 2.0 | 35.79 | 2240.00 | 2.45 | 0.07189 | 8.26 × 10−10 | 7 | 5 | 1.5 | 36.71 | 1800.00 | 2.42 | 0.08550 | 2.96 × 10−8 | 8 | 20 | 1.5 | 52.24 | 2202.40 | 2.83 | 0.08732 | 6.35 × 10−6 | 9 | 20 | 2.0 | 50.96 | 2493.40 | 2.79 | 0.10050 | 1.11 × 10−5 |
|
|