Evaluation of Effect of Various Nanofillers on Technological Properties of NBR/NR Blend Vulcanized Using BIAT-CBS System
Table 3
Technological properties of NBR/NR blend mixes containing nano-SCC, -PCS, and CNT.
| | Mixes | TS
MPa | 300% M
MPa | EB
% | TR
N/mm | Hardness
Shore A | AL
mm3 | CS
% | ΔG
J/mol | ΔS
J/mol/K |
| | NBCNT1 | 4.36 | 2.54 | 463 | 21.52 | 37 | 161.13 | 3.85 | −27.08 | 0.0902 | | NBCNT2 | 6.64 | 3.33 | 490 | 28.5 | 41 | 139.76 | 3.91 | −27.96 | 0.0932 | | NBCNT3 | 7.83 | 4.12 | 519 | 36.49 | 43 | 137.12 | 4.08 | −30.0 | 0.100 | | NBCNT4 | 8.45 | 4.76 | 542 | 37.21 | 48 | 135.32 | 4.14 | −31.01 | 0.1034 | | NBCC | 3.86 | 2.21 | 445 | 20.71 | 40 | 175.26 | 3.32 | −26.12 | 0.0871 | | NBCS | 5.81 | 2.60 | 429 | 18.11 | 37 | 179.19 | 3.46 | −26.08 | 0.0869 | |
NB0 | 3.79 | 2.11 | 379 | 14.97 | 34 | 191.09 | 3.95 | −26.54 | 0.0885 |
|
|
TS: tensile strength, M: modulus, EB: elongation at break, TR: tear resistance, CS: compression set, AL: abrasion loss, and SV: swelling value.
|