Stress-Strain Compression of AA6082-T6 Aluminum Alloy at Room Temperature
Table 3
Experimental results summary.
| Specimen | mm | N | Stress MPa | | | | MPa | MPa |
| 1a | 0.078 | 44525 | 227.7 | 0.01750 | 0.01735 | 0.01766 | 13008.2 | 227.7 | 1b | 0.027 | 49714 | 254.2 | 0.01464 | 0.01453 | 0.01475 | 17368.0 | 252.2 | 2a | 0.187 | 56542 | 289.1 | 0.02380 | 0.02352 | 0.02409 | 13323.5 | 245.5 | 2b | 0.198 | 57570 | 294.4 | 0.02341 | 0.02313 | 0.02369 | 17006.2 | 228.7 | 3a | 0.866 | 64384 | 329.2 | 0.04957 | 0.04834 | 0.05084 | 15697.4 | 217.4 | 3b | 0.921 | 70400 | 360.0 | 0.05116 | 0.04985 | 0.05252 | 18178.4 | 250.4 | 4a | 1.753 | 76888 | 393.1 | 0.08245 | 0.07905 | 0.08605 | 16920.9 | 253.0 | 4b | 1.612 | 75526 | 386.2 | 0.07799 | 0.07495 | 0.08120 | 14040.0 | 261.4 | 5a | 3.317 | 77916 | 398.4 | 0.13820 | 0.12865 | 0.14873 | 17049.7 | 239.7 | 5b | 3.012 | 84035 | 429.7 | 0.12996 | 0.12152 | 0.13922 | 15654.3 | 249.2 |
|
|