Review Article
Zero Spatial Frequency Limit: Method to Characterize Photopolymers as Optical Recording Material
Table 1
Solution compositions and thicknesses.
| Composition type | A | B | C | D | E | F | G |
| NaAO (g) | 0.75 | 1.5 | 0.75 | 1.5 | 0.75 | — | — | H2O (mL) | 12.5 | 12.5 | 12.5 | 12.5 | 12.5 | 14.5 | 14.5 | TEA (mL) | 1.25 | 1.5 | 1.5 | 3 | 3 | 1.25 | 2.3 | PVA (mL) (15% w/v) | 12.5 | 12.5 | 12.5 | 12.5 | 12.5 | 12.5 | 12.5 | YE (0.8% w/v) (mL) | 0.6 | 0.6 | 0.6 | 0.6 | — | 0.6 | 0.6 | PRF (g) | — | — | — | — | 0.14 | — | — | BMA (g) | — | 0.1 | 0.2 | — | — | — | 0.25 | AA (g) | — | — | — | — | — | 0.96 | 0.84 | Thickness ± 4 (μm) | 105 | 100 | 97 | 107 | 106 | 100 | 102 |
|
|