A Comparative Study of Spin Coated Transparent Conducting Thin Films of Gallium and Aluminum Doped ZnO Nanoparticles

Figure 4

The electrical resistivity, , of spin coated 5 GZO and AZO layers as a function of doping ratio in the dispersed nanopowders; the layers were sintered at 600°C in air and then heated at 400°C for 90 min in reducing gas.