Research Article
Thermaly Active Structures for Shape Morphing Applications
Table 7
Layer thermomechanical behavior.
| | ρ | c | EL | ET | | | | | α L | α T | λ L | | Units | (Kg·m−3) | (j·kg−1 K−1) | (MPA) | (MPA) | | | (MPA) | (MPA) | (10-5 K−1) | (10−5 K−1) | (W·m−1 K−1) | W.m-1 K−1 |
| UDG | 1610 | 1001 | 25726 | 7291 | 0.3 | 0.3 | 2604 | 2604 | 0.97 | 4.7 | 0.3 | 0.5 | 2DA | 1250 | 1170 | 16209 | 16209 | 0.1 | 0.1 | 1549 | 1549 | 1.2 | 1.2 | 0.16 | 0.16 | AL | 1440 | 990 | 154432 | 5194 | 0.3 | 0.3 | 2138 | 2138 | −6.210−3 | 5.3 | 72 | 0.5 | Glue | 1210 | 1100 | 821 | 821 | 0.4 | 0.4 | Isotropic | 10 | 10 | Fitting |
|
|