The Fission-Based 99Mo Production Process ROMOL-99 and Its Application to PINSTECH Islamabad
Table 2
Optimal parameters for the alumina column process.
| Al2O3 column | About 50 mm × 145 mm, bottom G 3 frit | Al2O3 weak acid material | 250 g, size ~60 m, density 1.25 mL/g, porosity 0.875 | Loading process: | FEED volume ~5.8 L, 0.15 < [H+] < 0.7 M, ~120 min | (1) Wash process | 1000 mL 0.5 M HNO3, time about 15 min | (2) Wash process | 500 mL water, time about 7 min | (3) Wash process | 1000 mL 0.01 M NH3, time about 15 min | Liquid waste volume: | 8300 mL | Elution | 1000 mL 1-2 M NH3, time about 30 min | Alumina column process: | Total time about 3 h. |
|
|