Growth of ZnO Nanorods on Stainless Steel Wire Using Chemical Vapour Deposition and Their Photocatalytic Activity

Abd Aziz, Siti Nor Qurratu Aini; Pung, Swee-Yong; Ramli, Nurul Najiah; Lockman, Zainovia

doi:https://doi.org/10.1155/2014/252851

The Scientific World Journal

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 252851 | https://doi.org/10.1155/2014/252851

Growth of ZnO Nanorods on Stainless Steel Wire Using Chemical Vapour Deposition and Their Photocatalytic Activity

Siti Nor Qurratu Aini Abd Aziz,^1,2Swee-Yong Pung,¹Nurul Najiah Ramli,¹and Zainovia Lockman^1,2

Academic Editor: A. Monopoli, B. Kim, C.-s. Wu, S. Sun

Received25 Aug 2013

Accepted14 Nov 2013

Published22 Jan 2014

Abstract

The photodegradation efficiency of ZnO nanoparticles in removal of organic pollutants deteriorates over time as a high percentage of the nanoparticles can be drained away by water during the wastewater treatment. This problem can be solved by growing the ZnO nanorods on stainless steel wire. In this work, ZnO nanorods were successfully grown on stainless steel wire by chemical vapour deposition. The SAED analysis indicates that ZnO nanorod is a single crystal and is preferentially grown in [0001] direction. The deconvoluted O 1s peak at 531.5 eV in XPS analysis is associated with oxygen deficient, revealing that the ZnO nanorods contain many oxygen vacancies. This observation is further supported by the finding of the small ratio, that is, ~1 in the photoluminescence analysis. The growth of ZnO nanorods on stainless steel wire was governed by vapour-solid mechanism as there were no Fe particles observed at the tips of the nanorods. The photodegradation of Rhodamine B solution by ZnO nanorods followed the first-order kinetics.

1. Introduction

Zinc oxide (ZnO) is a semiconductor material with a wide bandgap energy (3.37 eV) and large exciton binding energy (60 meV) at room temperature. Attributed to these unique properties, ZnO nanostructures such as nanorods (NRs) [1], nanofibres (NFs) [2], and nanobelts (NBs) [3] have lately been the focus of research activities. These ZnO nanostructures can be used for applications in light-emitting diodes [4] solar cells [5], nanogenerators [6], gas sensors [7], photodetectors [8], and UV lasers [9]. Different techniques have been developed for growing these ZnO nanostructures, which includes chemical vapour deposition (CVD) [10], physical vapour deposition (PVD) [11], molecular beam epitaxy (MBE) [12], pulsed laser deposition (PLD) [13], sol-gel method [14], and electrochemical deposition [15]. Generally, the low growth temperature in solution route (typically under 100°C) affects the crystalline quality of the ZnO nanostructures. The crystal quality of these nanostructures could be improved by carrying out postannealing under certain conditions [16].

The use of wide bandgap semiconductor photocatalysts such as ZnO [17] and TiO₂ [18] to degrade organic pollutants is another rapid developing research field. Approximately one million tons of synthetic organic dyes are produced every year for applications in textile, paint, cosmetic, and food industries [19]. A significant amount of these organic dyes end as wastewater and are discharged into rivers and seas. The removal of these effluents is critical for the environmental sustainability. Thus, the degradation of organic pollutants by semiconductor photocatalysts is one of the most promising technologies to reduce the adverse effects. It can be considered as the “green” technology for the treatment of environment pollutants with solar energy. The by-products of this technology such as water and CO₂ are less harmful to the environment. However, usage of these semiconductor photocatalysts in powder form can cause secondary pollution as they can be easily drained away by water. This also results in the efficiency for degradation of organic pollutants to deteriorate over time. In addition, the semiconductor photocatalysts need to be separated from the reaction medium. This exercise is not only time consuming but also costly. The limitations of using semiconductor photocatalysts in powder form can be resolved by growing them onto a rigid substrate such as stainless steel wire. The stainless steel wire functions as a support to the photocatalyst which reduces the incidence of the photocatalyst being easily washed away by the flowing water during the waste water treatment process.

In this paper, ZnO NRs were grown on stainless steel wire using CVD. By controlling the amount of Zn powder, both nano- and micro-ZnO rods could be synthesized on the stainless steel wire. The growth mechanism of ZnO NRs on stainless steel wires was discussed. The photodegradation efficiency of ZnO NRs on removal of organic dye (RhB) under ultraviolet (UV) irradiation was also investigated.

2. Materials and Methods

The stainless steel wire (: 0.05 mm) was used as substrate for the growth of ZnO NRs. The wire was first immersed in acetone and then ultrasonic-cleaned for 10 min. Subsequently, the wire was rinsed with deionized water thoroughly and was left to dry naturally. High purity of Zn powder (99.99%) was used as Zn source. Different amount of Zn powder at 0.3 g, 0.5 g, 1.0 g, 1.5 g, and 2.0 g, respectively, was used to grow the ZnO NRs. As illustrated in Figure 1, the alumina boat was placed in the middle of a horizontal tube furnace. The stainless steel wire was kept at the downstream of the furnace. During the synthesis process, the temperature of the furnace was kept at 650°C with pressure of 1 mbar. A trace amount of oxygen gas (2~3 sccm) was flowed into the furnace for the growth of ZnO NRs. The O₂ gas was turned off after 30 min and the temperature of the furnace was ramped down to room temperature.

The morphology of the as-synthesized nanostructures was studied by Zeiss Supra 35 VP field emission scanning electron microscope (FESEM) and Tecnai G2 20 S-Twin transmission electron microscope (TEM). The phase and crystallinity of the nanostructures were characterized using Philip PW 1729 X-ray diffractor (Cu Kα, λ = 0.154 nm) (XRD). The photoluminescence property of the nanostructures was characterized by PL Spectrophotometer (Horiba JobinYvon Spectrometer HR 550, 450 W, Xe lamp, 325 nm). The X-ray photoelectron spectroscopy (Omicron Nanotechnology, ELS 5000, MgKα radiation) was used to examine the chemical bonds of the sample.

The photocatalytic performance of ZnO was evaluated using RhB dye to represent organic pollutants. The RhB solution with initial concentration of 1 × 10⁻⁵M was prepared using a magnetic stirrer in the dark room. Subsequently, the RhB solution with the ZnO samples was placed together in the reaction cylinder and was irradiated with UV light (360 W lamp, 254 nm) for a period of time. The UV-Vis spectrometer (Cary 50, 553 nm) was used to evaluate the photodegradation of RhB solutions.

3. Results and Discussion

3.1. Structural and Optical Properties

The crystal phase of the as-grown sample (650°C, 2 sccm O₂, and 0.3 g Zn powder) was analysed by XRD as shown in Figure 2. The diffraction peaks of 31.91°, 34.56°, 36.29°, 56.83°, and 62.94° correspond to (100), (002), (101), (110), and (103) crystal planes, respectively. These diffraction peaks could be indexed as wurtzite ZnO (JSPDS Card no. 01-089-1397) with lattice constants of Å and Å. In addition, the diffraction peaks at 35.18°, 36.90°, and 56.53° which represent the crystal planes of (310), (222), and (510), respectively, are contributed from ZnFe₂O₄. It is possible that Fe was unintentionally doped into ZnO NRs during the synthesis process as the NRs were grown on the stainless steel wire.

As shown in Figure 3(a), ZnO NRs were successfully grown on stainless steel wire using CVD (0.3 g Zn powder and 2 sccm O₂). The EDS analysis in Figure 3(b) indicates that the ZnO NRs contain Zn (59.49 At%), O (38.50 At%), and Fe (2.01 At%). The Fe element was contributed from the stainless steel wire. Figure 4 shows the histograms of length, diameter and aspect ratio of ZnO NRs that are grown on the stainless steel wire. The length, diameter, and aspect ratio of these ZnO NRs are μm, μm, and , respectively. The areal density of this ZnO sample is NRs/μm².

(a)

(b)

(a)

(b)

(c)

Figure 5 shows the ZnO NRs grown on stainless steel wire using different amount of Zn powder, that is, 0.3 g, 0.5 g, 1.0 g, 1.5 g, and 2.0 g, respectively. It can be seen in Figure 5 that the ZnO NRs have hexagonal cross sections , which is a typical characteristic of ZnO NRs grown in the direction. As shown in Figure 6(a), the length of the ZnO NRs increases with the increase of Zn powder used in the synthesis, that is, from μm, μm, μm, μm, and μm. The diameter of ZnO NRs also increases from μm, μm, μm, μm, and μm. It was also found that as the amount of Zn powder increased, the ZnO structures grew from nanorods to microrods.

(a)

(b)

(c)

(d)

(e)

(a)

(b)

(c)

As shown in Figure 6(b), the aspect ratio of ZnO NRs increases from , , , , and , respectively, with the increase of Zn powder. This is one of the evidence of anisotropic growth of ZnO with the highest growth rate in direction. However, the areal density of ZnO NRs decreased with the increase of Zn powder as shown in Figure 6(c). The areal density is /μm², NRs/μm², /μm², /μm², and /μm² when the amount of Zn powder used was 0.3 g, 0.5 g, 1.0 g, 1.5 g, and 2.0 g, respectively. This result shows that the NRs were not only grow vertically (length) but also laterally (diameter) with the increase of Zn powder. Some of the adjacent NRs merged together (highlighted in circles in Figure 5(e)) and formed microrods, causing a reduction in areal density. In other words, as the amount of Zn powder increased, more Zn vapour was generated during the synthesis process. This promoted the growth of ZnO from nanorods to microrods with reduction in areal density.

Figure 7(a) shows the TEM image of ZnO NRs with uniform diameter (96 nm) and flat tips. The selected electron area diffraction (SAED) analysis in Figure 7(b) shows that the ZnO NR is single crystal.

(a)

(b)

Figure 8(a) shows the XPS wide scan analysis of the ZnO NRs grown on stainless steel wire. The binding energies of the spectra have been calibrated by taking the carbon C 1s peak (285 eV) as reference. The carbon peak is due to the unavoidable air exposure during inserting the sample in the XPS chamber. The presence of Zn LMN Auger peak at 497.0 eV and O 1s peak at 532.7 eV indicates that the nanostructures were ZnO as the peaks match well with the references in the Handbook of X-ray photoelectron spectroscopy [20]. In addition, the Zn 2p spectra of the ZnO NRs, which is shown in Figure 8(b), have the binding energies of 1021.1 eV and 1042.1 eV. These peaks can be identified as Zn 2p_3/2 and Zn 2p_1/2 lines, respectively. The spin-orbital-splitting energy between the two lines is 21 eV, which is well lying within the standard reference value of Zn (2p) in ZnO [21]. The O 1s peak is prominently identified at approximately 532.7 eV as shown in Figure 8(c). The O 1s XPS is asymmetric, indicating that at least two oxygen species are present in this region. Thus, the peak can be further deconvoluted into two Gaussian peaks, which are located at 530.3 eV and 531.5 eV. The first peak on the low binding energy (530.3 eV) is attributed to the O²⁻ ions on the wurtzite structure of hexagonal Zn²⁺ ion array, which are surrounded by Zn atoms [22]. The second peak (531.5 eV) is associated with oxygen deficient regions within the matrix of ZnO [23]. Figure 8(d) shows that the Fe 2p spectrum comprises two peaks at 710.3 eV and 724.2 eV, which correspond to the Fe 2p_3/2 and Fe 2p_1/2, respectively. According to Patil et al. [24], these two peaks are consistent with the bulk α-Fe₂O₃ peak at 710.8 eV and 724.80 eV. The energy difference between these two peaks is 13.9 eV. This value is the characteristic of Fe³⁺ state, indicating the formation of Fe₂O₃. The ZnO NRs were unintentionally doped with Fe from stainless steel wire during the synthesis process.

(a)

(b)

(c)

(d)

A sharp near-band-edge (NBE) UV emission at 379 nm and a broad green emission were observed in the room temperature PL measurement on the ZnO NRs grown on stainless steel wire as shown in Figure 9. The UV peak is attributed to the recombination of free exciton. The green emission peak is generally attributed to the deep level defect in ZnO crystals. According to Shetty and Nanda [25], ZnO contains various defects such as oxygen vacancy (), Zn vacancy (), oxygen interstitial (), Zn interstitial (), oxygen antisite (O_Zn), and zinc antisite (Zn_O). One of the possible origins of this strong green emission is related to the large quantity of the surface oxygen vacancies induced by Fe-related defects of the ZnO NRs. This observation is supported by the XPS analysis shown in Figure 8(c) as the large percentage of O 1s peak is contributed from the oxygen deficiency region (531.5 eV). Since the UV peak represents the NBE emission of ZnO and the green emission is defect-related emission, a good crystal quality of ZnO shall have a large / ratio in PL measurement [26]. Thus, the poor / ratio of PL, that is, ~1, indicates that the ZnO NRs have a relatively poor crystal quality.

3.2. Growth Mechanism

The most common mechanism used to describe the growth of ZnO NRs is vapour-liquid-solid (VLS) mechanism. One of the unique characteristics of nanorods grown under VLS mechanism is the presence of metal alloy nanoparticles at the tips of the nanorods. However, the growth of ZnO NRs on stainless steel wire is concluded to follow vapour-solid (VS) mechanism as no metal particles could be observed at the tips of the NRs (Figure 3(a)). As illustrated in Figures 10(a) and 10(b), zinc and oxygen vapours condense on the surface of stainless steel wire to form ZnO nucleus during the synthesis process. The surface energy of crystal planes of ZnO nucleus contributes to the effectiveness of capturing the subsequent adsorbed Zn and O atoms. This energy also affects the growth rate and the proportion of crystallographic planes of the nanostructures [25]. In the case of ZnO, the (002) plane has the lowest surface free energy, followed by the planes. Thus, ZnO NRs have the highest growth rate in direction, resulting in anisotropic growth of nanorods (Figure 8(c)). Eventually, ZnO NRs are formed towards the end of the synthesis process (Figure 10(d)).

(a)

(b)

(c)

(d)

3.3. Photocatalytic Study

The effectiveness of ZnO NRs grown on stainless steel wire as photocatalyst to degrade RhB solution under UV light (254 nm) was studied. The ZnO in Figure 11 shows the photodegradation of RhB solution by ZnO NRs as photocatalysts over a period of UV irradiation time. The RhB solution decolourized gradually. The degradation of the RhB solution was monitored by the deterioration of absorbance at 553 nm. Figure 12 shows the absorbance peak of RhB solution that degraded by ZnO NRs. It decreased from the initial absorbance of 0.853 (a.u.) to 0.537 (a.u.) after 30 min of UV irradiation. After 120 min, the RhB absorbance peak decreased to 0.194 (a.u.).

It is known that the absorption of solution () is proportional to the concentration () of the absorbing species as stated in Beer-Lambert Law [27]. Thus, the absorbance data is plotted as ln () of the time-dependent normalized dye concentrations (which is the ratio between the initial concentration and the concentration upon reaction) as shown in Figure 13. The linear plots in Figure 13 indicate that the degradation of RhB solution by ZnO NRs follows pseudo-first-order kinetics. The rate constant of ZnO NRs is min⁻¹.

The above observation can be explained as follows. The electrons and holes are generated in the ZnO upon UV irradiation as the UV light has the energy greater than the bandgap of ZnO. These charge carriers need to travel to the surface of ZnO rods for the formation of free radicals. In this case, oxygen acts as an electron acceptor by forming superoxide radical anions whereas holes react with water adhering to the surfaces of semiconductor particles to form highly reactive hydroxyl radicals (). These free radicals are capable of degrading the RhB molecules into less harmful by-products such as water and acids. As these reactions occur on the surface of ZnO exposed to solution, a larger exposed surface allows a more effective charges transfer for the formation of free radicals.

4. Conclusions

ZnO NRs were successfully synthesized on stainless steel wire via CVD. The deconvoluted O1s peak at 531.5 eV in XPS analysis is associated with oxygen deficient defects in ZnO. Thus, ZnO NRs grown on stainless steel wire contained many crystal defects which are mainly related to oxygen vacancies. This observation agrees well with the PL result. The PL spectra of ZnO NRs grown on stainless steel wire show a low / ratio, that is, ~1. This indicates that the ZnO NRs have a relatively poor crystal quality. It is crucial to control the amount of Zn powder used in the synthesis process as it promotes the growth of ZnO from nanorods to microrods. The reduction in areal density of ZnO rods was attributed to the merging of adjacent rods. The growth of ZnO NRs on stainless steel wire was governed by VS mechanism as no foreign catalyst could be observed at the tips of NRs. The photodegradation of RhB solution by the ZnO NRs grown on stainless steel wire under UV irradiation followed the first-order kinetics with rate constant of min⁻¹.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

The financial support of USM short term Grant (304/PBAHAN/60311011) for this project is gratefully acknowledged.

References

N. A. Hamzah, S. Y. Pung, S. Sreekantan, and S. N. Q. A. Abd Aziz, “Effect of CVD synthesis parameters on the growth of catalyst-free ZnO NRs,” Material Science Forum, vol. 756, pp. 24–30, 2013.
View at: Google Scholar
H. M. Ren, Y. H. Ding, Y. Jiang, F. Xu, Z. Long, and P. Zhang, “Synthesis and properties of ZnO nanofibers prepared by electrospinning,” Journal of Sol-Gel Science and Technology, vol. 52, no. 2, pp. 287–290, 2009.
View at: Publisher Site | Google Scholar
X. Y. Zhang, J. Y. Dai, H. C. Ong, N. Wang, H. L. W. Chan, and C. L. Choy, “Hydrothermal synthesis of oriented ZnO nanobelts and their temperature dependent photoluminescence,” Chemical Physics Letters, vol. 393, no. 1–3, pp. 17–21, 2004.
View at: Publisher Site | Google Scholar
J. H. Na, M. Kitamura, M. Arita, and Y. Arakawa, “Hybrid p-n junction light-emitting diodes based on sputtered ZnO and organic semiconductors,” Applied Physics Letters, vol. 95, no. 25, Article ID 253303, 2009.
View at: Publisher Site | Google Scholar
Z. L. Wang, R. Yang, J. Zhou et al., “Lateral nanowire/nanobelt based nanogenerators, piezotronics and piezo-phototronics,” Materials Science and Engineering R, vol. 70, no. 3–6, pp. 320–329, 2010.
View at: Publisher Site | Google Scholar
P. Sudhagar, R. S. Kumar, J. H. Jung et al., “Facile synthesis of highly branched jacks-like ZnO nanorods and their applications in dye-sensitized solar cells,” Materials Research Bulletin, vol. 46, no. 9, pp. 1473–1479, 2011.
View at: Publisher Site | Google Scholar
J. Xu, J. Han, Y. Zhang, Y. Sun, and B. Xie, “Studies on alcohol sensing mechanism of ZnO based gas sensors,” Sensors and Actuators B, vol. 132, no. 1, pp. 334–339, 2008.
View at: Publisher Site | Google Scholar
C.-Y. Lu, S.-J. Chang, S.-P. Chang et al., “Ultraviolet photodetectors with ZnO nanowires prepared on ZnO: Ga/glass templates,” Applied Physics Letters, vol. 89, no. 15, Article ID 153101, 2006.
View at: Publisher Site | Google Scholar
S. Chu, G. Wang, W. Zhou et al., “Electrically pumped waveguide lasing from ZnO nanowires,” Nature Nanotechnology, vol. 6, no. 8, pp. 506–510, 2011.
View at: Publisher Site | Google Scholar
G. Zhong, A. Kalam, A. S. Al-Shihri, Q. Su, J. Li, and G. Du, “Low-temperature growth of well-aligned ZnO nanorods/nanowires on flexible graphite sheet and their photoluminescence properties,” Materials Research Bulletin, vol. 47, no. 6, pp. 1467–1470, 2012.
View at: Publisher Site | Google Scholar
Y. Zhang, L. Wang, X. Liu, Y. Yan, C. Chen, and J. Zhu, “Synthesis of nano/micro zinc oxide rods and arrays by thermal evaporation approach on cylindrical shape substrate,” Journal of Physical Chemistry B, vol. 109, no. 27, pp. 13091–13093, 2005.
View at: Publisher Site | Google Scholar
J. S. Wang, C. S. Yang, P. I. Chen et al., “Catalyst-free highly vertically aligned ZnO nanoneedle arrays grown by plasma-assisted molecular beam epitaxy,” Applied Physics A, vol. 97, no. 3, pp. 553–557, 2009.
View at: Publisher Site | Google Scholar
L. C. Tien, S. J. Pearton, D. P. Norton, and F. Ren, “Synthesis and microstructure of vertically aligned ZnO nanowires grown by high-pressure-assisted pulsed-laser deposition,” Journal of Materials Science, vol. 43, no. 21, pp. 6925–6932, 2008.
View at: Publisher Site | Google Scholar
Y. L. Chan, S. Y. Pung, and S. Sreekantan, “Degradation of organic dye using ZnO nanorods based continuous flow water purifier,” Journal of Sol-Gel Science and Technology, vol. 66, no. 3, pp. 399–405, 2013.
View at: Publisher Site | Google Scholar
J. Gong, Z. Dou, Q. Ding, Y. Xu, and W. Zhu, “Controlled synthesis of ZnO nanostructures by electrodeposition method,” Journal of Nanomaterials, vol. 2010, Article ID 740628, 6 pages, 2010.
View at: Publisher Site | Google Scholar
A. B. Djurišić and Y. H. Leung, “Optical properties of ZnO nanostructures,” Small, vol. 2, no. 8-9, pp. 944–961, 2006.
View at: Google Scholar
R. Velmurugan and M. Swaminathan, “An efficient nanostructured ZnO for dye sensitized degradation of Reactive Red 120 dye under solar light,” Solar Energy Materials and Solar Cells, vol. 95, no. 3, pp. 942–950, 2011.
View at: Publisher Site | Google Scholar
Z. Liu and M. Misra, “Dye-sensitized photovoltaic wires using highly ordered TiO2 nanotube arrays,” ACS Nano, vol. 4, no. 4, pp. 2196–2200, 2010.
View at: Publisher Site | Google Scholar
F. M. D. Chequer, G. A. R. de Olivera, E. R. A. Ferraz, J. C. Cardoso, M. V. B. Zanoni, and D. P. de Olivera, “Textile dyes: dyeing process and environmental impact,” in Eco-Friendly Textile Dyeing and Finishing, chapter 6, InTech, 2013.
View at: Publisher Site | Google Scholar
J. Chastain and R. C. King, Handbook of X-Ray Photoelectron Spectroscopy: A Reference Book of standard spectra dor identification and interpretAtion of XPS data, Physical Electronics, Eden Prairie, Minn, USA, 1995.
C. Wang, X. Tan, S. Chen et al., “Highly-sensitive cholesterol biosensor based on platinum-gold hybrid functionalized ZnO nanorods,” Talanta, vol. 94, pp. 263–270, 2012.
View at: Publisher Site | Google Scholar
R. D. Shannon, “Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides,” Acta Crystallographica A, vol. 32, no. 5, pp. 751–767, 1976.
View at: Google Scholar
S. Mal, S. Nori, J. Narayan, and J. T. Prater, “Defect-mediated ferromagnetism and controlled switching characteristics in ZnO,” Journal of Materials Research, vol. 26, no. 10, pp. 1298–1308, 2011.
View at: Publisher Site | Google Scholar
D. Patil, V. Patil, and P. Patil, “Highly sensitive and selective LPG sensor based on α-Fe₂O₃ nanorods,” Sensors and Actuators B, vol. 152, no. 2, pp. 299–306, 2011.
View at: Publisher Site | Google Scholar
A. Shetty and K. K. Nanda, “Tunable device properties of free-standing inorganic/organic flexible hybrid structures obtained by exfoliation,” Applied Physics Letters, vol. 100, no. 24, Article ID 242108, 2012.
View at: Google Scholar
S. Y. Pung, K. L. Choy, and X. Hou, “Structural and optical properties of ZnO nanostructures,” ASEAN Engineering Journal, vol. 1, pp. 46–56, 2012.
View at: Google Scholar
S. Xu, C. Lao, B. Weintraub, and Z. L. Wang, “Density-controlled growth of aligned ZnO nanowire arrays by seedles chemical approach on smooth surfaces,” Journal of Materials Research, vol. 23, no. 8, pp. 2072–2077, 2008.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Siti Nor Qurratu Aini Abd Aziz et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1834

Downloads

1196

Citations