Evolution of Microstructure and Residual Stress under Various Vibration Modes in 304 Stainless Steel Welds
Table 3
XRD data of different crystallographic planes after vibration welding.
| Vibration mode | | Intensity | FWHM |
| (111) | 0 Hz | 43.64 | 4378 | 0.168 | TX-VSR (362 Hz) | 43.61 | 2701 | 0.176 | TX-VSR (375 Hz) | 43.66 | 3372 | 0.178 | Meta-Lax (59.3 Hz) | 43.67 | 2823 | 0.174 | Meta-Lax (60.9 Hz) | 43.67 | 2804 | 0.182 |
| (200) | 0 Hz | 50.77 | 867 | 0.212 | TX-VSR (362 Hz) | 50.75 | 931 | 0.223 | TX-VSR (375 Hz) | 50.80 | 819 | 0.233 | Meta-Lax (59.3 Hz) | 50.81 | 1035 | 0.218 | Meta-Lax (60.9 Hz) | 50.81 | 1042 | 0.239 |
| (220) | 0 Hz | 74.71 | 397 | 0.288 | TX-VSR (362 Hz) | 74.70 | 350 | 0.301 | TX-VSR (375 Hz) | 74.74 | 261 | 0.303 | Meta-Lax (59.3 Hz) | 74.76 | 320 | 0.298 | Meta-Lax (60.9 Hz) | 74.76 | 322 | 0.307 |
| (110) | 0 Hz | 44.57 | 100 | 0.170 | TX-VSR (362 Hz) | 44.54 | 132 | 0.203 | TX-VSR (375 Hz) | 44.52 | 192 | 0.210 | Meta-Lax (59.3 Hz) | 44.60 | 128 | 0.185 | Meta-Lax (60.9 Hz) | 44.50 | 118 | 0.197 |
|
|