Performance of PRP Associated with Porous Chitosan as a Composite Scaffold for Regenerative Medicine

Shimojo, Andréa Arruda Martins; Perez, Amanda Gomes Marcelino; Galdames, Sofia Elisa Moraga; Brissac, Isabela Cambraia de Souza; Santana, Maria Helena Andrade

doi:https://doi.org/10.1155/2015/396131

The Scientific World Journal

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2015 | Article ID 396131 | https://doi.org/10.1155/2015/396131

Performance of PRP Associated with Porous Chitosan as a Composite Scaffold for Regenerative Medicine

Andréa Arruda Martins Shimojo,¹Amanda Gomes Marcelino Perez,¹Sofia Elisa Moraga Galdames,¹Isabela Cambraia de Souza Brissac,¹and Maria Helena Andrade Santana¹

Academic Editor: Faik Oktar

Received30 Nov 2014

Accepted08 Jan 2015

Published02 Mar 2015

Abstract

This study aimed to evaluate the in vitro performance of activated platelet-rich plasma associated with porous sponges of chitosan as a composite scaffold for proliferation and osteogenic differentiation of human adipose tissue-derived mesenchymal stem cells. The sponges were prepared by controlled freezing (−20, −80, or −196°C) and lyophilization of chitosan solutions (1, 2, or 3% w/v). The platelet-rich plasma was obtained from controlled centrifugation of whole blood and activated with calcium and autologous serum. The composite scaffolds were prepared by embedding the sponges with the activated platelet-rich plasma. The results showed the performance of the scaffolds was superior to that of activated platelet-rich plasma alone, in terms of delaying the release of growth factors and increased proliferation of the stem cells. The best preparation conditions of chitosan composite scaffolds that coordinated the physicochemical and mechanical properties and cell proliferation were 3% (w/v) chitosan and a −20°C freezing temperature, while −196°C favored osteogenic differentiation. Although the composite scaffolds are promising for regenerative medicine, the structures require stabilization to prevent the collapse observed after five days.

1. Introduction

In tissue engineering, a scaffold is a three-dimensional matrix for the stimulation of cell proliferation and the formation of new tissue. To achieve this goal, scaffolds must meet some specific requirements such as mimicking the native extracellular matrix (ECM) of the target tissue; allowing cell attachment, migration, proliferation, and differentiation to and maintenance of the target phenotype; promoting vascularization and nutrient delivery; and having a biodegradation rate and mechanical properties that are adequate to support the formation of the new tissue [1, 2].

According to Crane and Everts, tissue regeneration is based on a proliferation triangle composed of the three fundamental elements of cells, growth factors (GFs), and scaffolds, which are in a close relationship through their capabilities. Thus, scaffolds provide the conductive matrix for supporting the genic capability of progenitor cells mediated by the inductive capability of GFs [3]. Optimal conditions for tissue regeneration must come from the interaction of the properties of those elements.

The cell responses to the surface chemistry of scaffolds depend on their hydrophobicity, protein adsorption, surface charge, and roughness, softness, and stiffness. Additionally, the porous architecture characterized by the pore size, porosity, connectivity, and tortuosity plays important roles, as described and discussed by Chang and Wang [4]. Therefore, bringing together all these properties in solid scaffolds is an enormous technological challenge.

The fibrin matrix is the natural scaffold formed from the coagulation cascade in the healing process. Under injury, thrombin cleaves the soluble plasma protein fibrinogen into peptide fragments, yielding insoluble fibrin peptides that aggregate and form fibrils. A fibrin network is then formed, which entraps platelets and other blood components [5, 6]. Calcium acts as a cofactor of thrombin, modulates the elongation of fibers during polymerization by promoting lateral branching, and functions in clot stability [7, 8]. Calcium and thrombin also activate platelets, allowing the release of GFs and cytokines. Therefore, the fibrin matrix provides an optimized medium for cell proliferation and healing.

Based on these features, platelet-rich plasma (PRP) has been widely used in regenerative medicine. PRP is an autologous product prepared from whole blood by separating the red blood cells and concentrating the platelets and other components of plasma. However, although viscoelastic, the fibrin matrix alone lacks stability to be efficient when regenerative medicine is the goal.

To mimic the natural healing process and improve the stability of the fibrin matrix, we propose in this work the use of the fibrin network from activated PRP with porous chitosan as a composite scaffold for tissue regeneration.

Our hypothesis is that the chemical nature of the chitosan surface supports the fibrin network by electrostatic attachment, thus prolonging its stability, without changing the paracrine affinity of mesenchymal cells to fibrin fibers. As a consequence, the composite scaffold must improve cell proliferation and tissue differentiation compared to PRP alone.

Related works showed the effects of chitosan on blood coagulation through the strong adhesion of platelets to the surface of chitosan particles, as well as chitosan (0.1–1 mg/mL) incorporated with PRP to enhance the release of PDGF-AB and TGF-β1 from platelets [9, 10]. Shen et al. demonstrated that chitosan could be an appropriate substitute for thrombin, as an agonist in PRP preparation [11]. Chang et al. showed that growth factors could sustain release until 12 h at approximately 1 ng/mL from chitosan/CaSO₄/PRP microspheres after activation with thrombin [12]. Kutlu et al. showed that scaffolds prepared by the freeze-drying of PRP added to chitosan gel (2% w/v) were more effective than chitosan sponges soaked with PRP on controlled GF release [13]. Oktay et al. applied PRP-embedded chitosan sponges to defects and showed a histological tendency toward increased bone formation [14]. Mathews et al. demonstrated that chitosan enhanced mineralization by upregulating the genes associated with mineralization and calcium-binding proteins [15].

Chitosan is a polysaccharide derived from chitin (copolymers β-(14)-2-amino-2-deoxy-D-glucose and β-(14)-2-acetamido 2-deoxy-D-glucose) found in the shells of marine crustaceans and insects and the cell walls of some fungi [16, 17].

In the last ten years, considerable attention has been given to chitosan-based materials in the field of tissue engineering [18, 19]. The beneficial properties of chitosan have been proven, such as biodegradability [20, 21], biocompatibility [22, 23], antibacterial activity [24, 25], cell adhesion [26, 27], and wound healing properties [28, 29]. Moreover, the chemical nature of chitosan gives many possibilities for ionic and covalent modifications that allow for the modulation of the mechanical and biological properties of biomaterials [30, 31].

Regarding the technological aspects, chitosan can be easily processed in diverse forms in the absence of toxic solvents, such as films [32], sponges [33, 34], fibers [35], beads [36], hydrogels [37], and microparticles/nanoparticles [38]. Furthermore, chitosan supports sterilization [39], is abundant in nature, and requires only low-cost processing in nonaggressive ecological conditions before being used as a raw material [17].

Freeze-drying is the most common and simplest method to produce porous chitosan scaffolds. The freezing process provides the nucleation of ice crystals from solution and further growth along the lines of thermal gradients. Exclusion of the chitosan acetate salt from the ice crystal phase and subsequent ice removal by lyophilization generate a porous material [40, 41].

Madihally and Matthew reported that the pore size of chitosan scaffolds produced by lyophilization can be controlled within the range of 1–250 μm [33]. A more uniform and interconnected pore structure can be obtained when lower freezing temperatures are used. Furthermore, the pore orientation is related to the geometry of the moldings used and can also be controlled by changing thermal gradients during freezing [42].

The microstructure, crystallinity, and mechanical strength of the porous chitosan matrix also can be controlled by the chitosan concentration, molecular weight, and deacetylation degree [33, 43].

In this work, the effects of PRP association were studied regarding the porous structure of solid sponges, which were produced by varying chitosan concentration and freezing conditions. The biological performance of association was evaluated in terms of growth factor release kinetics, proliferation, and osteogenic differentiation of seeded human adipose tissue-derived mesenchymal stem cells (h-AdMSCs).

2. Experimental

2.1. Materials

Chitosan (average molecular weight [Mw] = 4 × 10⁵ Da, degree of deacetylation = %) was purchased from Polymar (Fortaleza, CE, Brazil) and purified according to the protocol described by Nasti et al. [44]. Other chemicals were of reagent grade and were used without any further purification. All biological experiments were performed with human adipose tissue-derived stem mesenchymal cells (h-AdMSCs) and approved by the Ethics Committee of the Medical Sciences School of the University of Campinas (UNICAMP; CAAE: 0972.0.146.000-11). The donors were healthy individuals aged between 30 and 40 years old who were previously assessed through clinical examinations.

2.2. Methods

2.2.1. Preparation of Porous Chitosan Scaffolds (PCHTs)

PCHTs were prepared by freezing at a controlled temperature of a chitosan solution previously poured in 24-well culture plates (TPP, polystyrene, diameter = 15.4 mm) to give them a cylindrical shape, followed by lyophilizing in lyophilizer L101 (Liobras, São Carlos, SP, Brazil) at a temperature of approximately −30°C for 48 hours.

Effects of Chitosan Concentration. Chitosan solutions with concentrations of 1, 2, or 3% (w/v) were prepared by dissolution in 0.2 mol L⁻¹ acetic acid for 24 hours at room temperature. The solutions were frozen at −20°C for 24 hours and lyophilized.

Effects of Freezing Conditions. Chitosan solution (3% w/v) was prepared as previously described. The solution was frozen at −20°C in a freezer for 24 hours; −80°C in an ultrafreezer for 24 hours; or −196°C by immersion in liquid N₂; and lyophilized.

2.2.2. Characterization of Porous Chitosan Scaffolds (PCHTs)

Morphology and Pore Size. The morphology of PCHTs was evaluated by scanning electron microscopy (SEM) using an LEO 440i Electron Microscopy/Oxford (Cambridge, England) operated at 5 kV accelerating voltage. The scaffolds were gold-coated using a sputter coater POLARON SC7620, VG Microtech (Uckfield, England) for 180 s at a current of 3 mA. Pore size () was measured using software Image J 1.47t.

Mechanical Properties. Mechanical compression tests of PCHTs () were performed using a Universal Testing Machine, MTS model 810-Flex Test 40 (MTS Systems Corporation, Eden Prairie, MN, USA) up to 60% strain, according to Correia et al. [45]. The testing machine was equipped with a 1.5 kN load cell, and the loading rate was 5 mm/min. Young’s modulus was calculated in the initial linear section of the stress-strain curve, when the strain was lower than 10%.

Degradation in PBS. The degradation profile of the PCHTs in PBS at 37°C was performed by the gravimetric method described by Tang and Spector through measurements of remaining weight [46].

Water Sorption. The water sorption was determined by swelling of PCHTs (previously weighted) in PBS (LB Laborclin, Pinhais, PR, Brazil) at pH 7.4 for 24 hours at 37°C. The swollen PCHTs were weighed after the removal of excess water by keeping the surfaces on a filter paper. The swelling ratio (SR) was also calculated using where and are the weights of the scaffolds in the swelled state and the dry state, respectively.

Porosity. The porosity () of the PCHTs was determined according to the protocol used by Wang et al. and calculated by [47] where is the total volume of PCHTs (cm³), is the density of nonporous CHT (1.342 g/cm³), and is the weight of sponge (g). Values are expressed as the means ± standard deviation ().

Cell Compatibility. The compatibility was carried out by exposing PCHTs to h-AdMSCs followed by cultivation at 37°C for 24 hours and evaluation by MTT assay (3-[4,5-dimethyl-thiazol-2-yl]-2,5-diphenyltetrazolium bromide) (MTT, Molecular Probes) according to a modified Mosmann method [48]. The MTT assay is a colorimetric test based on the reduction of yellow tetrazolium salt into a purple formazan product in presence of cells [49].

2.2.3. PRP Preparations

PRP Concentration. P-PRP (plasma rich in platelets and poor in leukocytes) was prepared according to Perez et al. [50]. Briefly, whole blood (WB) was collected into 3.5 mL vacuum tubes (Vacuette, Campinas, SP, Brazil) containing sodium citrate 3.2% (w/v) as an anticoagulant. WB was initially centrifuged in a Rotina 380R centrifuge (Hettich Zentrifugen, Tuttlingen, Germany) at 100 ×g for 10 minutes at 25°C. After the formation of three layers (a bottom layer composed mainly of red blood cells (RBCs); an upper layer composed of plasma, platelets, and some WB cells; and an intermediate layer, or buffy coat, composed mostly of WB cells), only the upper layer was collected to obtain P-PRP. The concentration of platelets, WB cells, and RBCs in WB and P-PRP were determined using the ABX Micros ES 60 hematology analyzer (HORIBA ABX Diagnostics, Montpellier, France).

P-PRP Activation. Activated P-PRP (P-PRP) was obtained by adding autologous serum (Ser) and 10% (w/v) CaCl₂ solution as agonists using the following proportions: agonist/P-PRP = 20% (v/v), Ser/CaCl₂ volumetric ratio = 9. Autologous serum was prepared by collecting 5 mL of WB in tubes without anticoagulant. After 30 minutes to form clots, WB was centrifuged at 2000 ×g for 10 minutes [51].

2.2.4. The Composite Scaffolds (P-PRP/PCHTs)

Preparation. P-PRP/PCHTs was prepared for embedding by dripping P-PRP, immediately after activation, onto PCHTs. The preparation was carried out in 48-well microplates using a ratio of 200 μL of P-PRP to 10–20 mg of PCHTs.

Release of GFs. The release of platelet-derived growth factor AB (PDGF-AB) and transforming growth factor β1 (TGF-β1) was performed after 1 hour of gelation of P-PRP associated with PCHTs in the presence of the culture medium (Dulbecco’s Modified Eagle’s Medium (DMEM-LG) (Gibco, Grand Island, NY, USA) with low glucose concentration). The culture medium (1.5 mL) was added to P-PRP/PCHTs in 48-well microplates, which were maintained in an incubator with 5% CO₂ throughout the assays. The total volume of culture medium was withdrawn at 3, 6, 12, 24, and 72 hours, and the same volume of fresh medium was replaced without removing the hydrogels from the wells. The samples were stored at −80°C for further characterization. The concentrations of the released GFs PDGF-AB and TGF-β1 were measured using enzyme-linked immunosorbent assay (ELISA) kits (R&D Systems, Minneapolis, MN, USA) according to the manufacturer’s instructions and specifications.

h-AdMSCs Proliferation. The cultivation of h-AdMSCs was carried out in 24-well tissue culture plates by adding 1 mL DMEM to the seeded composite scaffolds (). The composite scaffolds seeded were maintained at 37°C for 10 days. Cell proliferation was quantified using the thiazolyl blue tetrazolium bromide (MTT) assay. At 3, 5, 7, and 10 cultivation days, the composite scaffolds were removed and transferred to 24-well plates. MTT (1 mL of 1 mg/mL) was then added, and the cultivation proceeded at 37°C for 4 hours. The MTT solution was then discarded, and 1 mL of DMSO was added to dissolve the purple formazan crystals. The samples were shaken at 120 rpm for 30 min to ensure homogeneous dissolution of the formazan dye, and then 200 μL of each sample was transferred to a 96-well plate. Optical density was measured at 595 nm using a microplate reader (FilterMax F5, Molecular Devices).

The isolation and precultivation of h-AdMSCs as well as the cell seeding were performed as described below.

h-AdMSCs Isolation and Precultivation. Human subcutaneous adipose tissue that was initially acquired from liposuction surgery was washed with sterile PBS, separated into fractions of 10 g, digested with 20 mg of collagenase type 1A and maintained in 20 mL of DMEM-LG containing 10% BSA (bovine serum albumin) and 10 μL of gentamicin for 30 min in a 37°C bath. After complete digestion, the reaction was quenched with 10 mL fetal bovine serum (FBS) and immediately centrifuged for 15 min at 1500 rpm. The supernatant was discarded, and the pellet was suspended in 10 mL DMEM-LG with 10% FBS. After precultivation for 24 h, the culture medium was changed every 3 days; after the fourth passage, the cells were characterized by immunophenotyping (data not shown) using flow cytometry and according to their adipogenic, osteogenic, and chondrogenic differentiation and then used in the subsequent experiments.

h-AdMSCs-Seeding. The precultured h-AdMSCs were trypsinized and resuspended in P-PRP to a final cell concentration of 1 × 10⁴ cells/mL. P-PRP containing h-AdMSCs was activated and immediately embedded to the PCHTs in a 24-well tissue culture plate, using 200 μL of h-AdMSCs + P-PRP per 10–20 mg of PCHTs. The composite scaffolds with h-AdMSCs were kept at room temperature for 45 minutes for consolidation of the fibrin network. Pure PRP was used as control.

2.2.5. Images of the h-AdMSCs-Seeded Composite Scaffolds

The images of the cell-seeded composite scaffolds were obtained by scanning electron microscopy after 5 days of h-AdMSCs proliferation. The cell-seeded composite scaffolds were fixed in a solution of 4% paraformaldehyde and 2.5% glutaraldehyde in phosphate buffer, pH 7.4, for 2 hours. The samples were than dehydrated in ethanol for 15 min intervals in aqueous 50%, 70%, 95%, and 100% ethanol solutions (2x) and dried at the critical point dryer BAL-TEC CPD 030 (Schalksmühle, Germany). After gold coating (Sputter Coater POLARON, SC7620, VG Microtech), the cell-seeded composite scaffolds were visualized with a SEM (Leo440i, LEO) with an accelerating voltage of 20 kV.

2.2.6. Induction of Osteogenic Differentiation

h-AdMSCs-seeded in the composite scaffolds were induced to differentiate into the osteogenic lineage by providing the osteogenic medium containing DMEM-LG supplemented with 10% FBS, 1% β-glycerol-phosphate (Sigma-Aldrich, St. Louis, MO, USA), 1% L-ascorbic acid (Sigma-Aldrich, St. Louis, MO, USA), 1% dexamethasone (Sigma-Aldrich, St. Louis, MO, USA), and 1% penicillin/streptomycin solution (Gibco, Grand Island, NY, USA). The medium was changed every 7 days.

Evaluation of Differentiation. Differentiation was evaluated by measuring the alkaline phosphatase activity (ALP) on day 14. The supernatant (200 μL) was collected and mixed with the same volume of p-nitrophenyl phosphate (SIGMAFAST p-nitrophenyl phosphate tablets, Sigma, Saint Louis, MO, USA) as substrate and incubated at room temperature for 30 minutes. Absorbance was read immediately at 405 nm.

2.2.7. Statistical Analysis

Each experiment was carried out in triplicate unless otherwise specified. All results are presented as the mean ± standard deviation (SD). The experimental data from all the studies were analyzed using Analysis of Variance (ANOVA). Statistical significance was set to value ≤ 0.05.

3. Results and Discussion

3.1. Experimental Design

In this study, we prepared novel composite scaffolds by association of PRP with the 3D-porous structure of chitosan. First, different 3D-porous structures of chitosan (PCHTs) were prepared by freeze-drying by varying the CHT concentration and freezing conditions (temperature and freezing rate). Second, the microstructure and mechanical properties of the PCHTs were characterized and evaluated for cell compatibility. The surface chemistry, hydrophilicity, and positive charge of –NH₂ groups in acidic medium were maintained unaltered.

The composite scaffolds (P-PRP/PCHTs) were obtained by embedding the PCHTs with immediately activated P-PRP in a 24-well microplate. The release of the GFs (PDGF-AB and TGF-β1) from the composite scaffolds was evaluated in DMEM culture medium. Afterwards, precultured h-AdMSCs were added to PRP before activation in order to obtain cell-seeded composite scaffolds. In vitro examination of h-AdMSCs proliferation kinetics was performed over 10 days by using the cell-seeded composite scaffolds in DMEM. Additionally, osteogenic differentiation was evaluated by ALP activity measurements after 14 days.

Thus, we verified the correlation between the structure and function of PCHTs by controlling the concentration and freezing conditions of chitosan solution.

3.2. Effects of Freezing Conditions and Chitosan Concentration on PCHTs

3.2.1. Images of Porous Structure

Figures 1(a)–1(c) show images of the porous structure from controlled freezing at −20°C by varying the concentration of the chitosan solution (1, 2, or 3%) and subsequent lyophilization. The images show highly porous structures with rounded pores that are uniformly distributed, radially oriented, and visually interconnected, regardless of CHT concentration. Differences in chitosan molecular weight, deacetylation degree, and purity make difficult comparisons even for similar treatment. Madihally and Matthew, showed a higher pore interconnectivity degree and more open pores for 1% (w/w) chitosan concentration for a similar deacetylation degree, but other properties were not characterized [33].

(a)

(b)

(c)

(d)

(e)

Freezing conditions produced a more prominent effect on the morphology of the pores (Figures 1(d)-1(e)) attributed the variations in the freezing rate used to achieve the temperatures evaluated. In contrast with rounded pores at −20°C (3% CHT) (Figure 1(c)), we observed pores with leaf structure at −80°C (Figure 1(d)), while smaller and elongated open pores were produced at −196°C (Figure 1(e)). In all cases, the pores were uniformly distributed and radially oriented and had a high degree of interconnectivity.

The pore structures allow uniform cell spatial distribution throughout the scaffold, facilitating homogeneous tissue formation. Moreover, the differences in pore morphologies obtained are suitable to several cell linage and type of tissue to be regenerated.

3.2.2. Characterization of PCHTs

Physicochemical and Mechanical Properties. Table 1 shows physicochemical characterization of the PCHTs. At −20°C, the mean diameter of rounded pores could be controlled around the 300–400 μm, regardless of the CHT concentration, although there is a large distribution.

However, the elongated pores from Figures 1(d)-1(e) were markedly decreased with freezing conditions from 2615 μm (−80°C) to 280 μm (−196°C) because crystal growth and hence pore size are functions of both heat and mass transfer rates, determined by the temperature and freezing rate. At −80°C, the observed differences in pore shape and size suggest parallel ice crystal growth, which in turn was caused by the strongly one-dimensional nature of the thermal gradients established during freezing, as discussed by Madihally and Matthew [33].

The diverse nature of tissue architectures requires scaffolds with optimal pore sizes, such as 5 μm for neovascularization [52], 5–15 μm for fibroblast ingrowth [53], 20 μm for the ingrowth of hepatocytes [54], 200–900 μm for osteoconduction [55], and 20–125 μm for regeneration of adult mammalian skin [56].

According to these data, the rounded pores obtained at −20°C or elongated at −196°C are adequate for bone tissue, although other properties could also influence the choice. Moreover, because human adipose tissue-derived mesenchymal stem cells (h-AdMSCs) exhibit a spindle-like shape and are 80–100 μm in diameter and ~200 μm in length [57], the range of pore sizes in our PCHTs allows cells to migrate freely into the scaffolds, favoring the formation of a new tissue.

The porosity is also an important aspect of cell migration and proliferation, guiding and promoting the formation of new tissue. Porosity is defined as the percentage of void space in a solid and is a morphological property independent of material [58]. A porosity higher than 90% and pore interconnectivity are basic requirements for scaffolds in tissue engineering because they affect the diffusion of physiological nutrients and gases to and the removal of metabolic waste and byproducts from cells that have penetrated the scaffold [59, 60]. Moreover, the porosity often compromises the mechanical and structural stability of the scaffolds and must be evaluated in accordance with the application and degradation rate of materials utilized [61].

The porosity values of PCHTs scaffolds ranged from 91.0 to 97.0%, which are adequate for TE, independent of CHT concentration or freezing conditions. However, the porosity decreased with increasing chitosan concentration. The highest porosity was provided from 1% chitosan solution, but there was not a direct relationship with freezing conditions. The PCHTs prepared at −80°C showed a significantly lower porosity even with higher pore size, probably due to their leaf structure (Table 1).

To guide tissue regeneration, scaffolds should also have sufficient mechanical strength during in vitro culturing to maintain the spaces required for cell in-growth and matrix elaboration [59]. Moreover, their mechanical properties should be similar to the properties of tissues generated to provide an adequate structural support in the stage of healing [62].

Scaffolds for the regeneration of hard tissue must exhibit a mechanical modulus in the range of 10–1,500 MPa, while scaffolds for soft tissues must exhibit a mechanical modulus in the range of 0.4–350 MPa [63].

In this work, we observed a drastic decrease in Young’s modulus (Table 1) with a decrease in CHT concentration. Better mechanical properties were found for a CHT concentration of 3%.

The PCHTs 3% (w/v) prepared at −80°C showed lower mechanical strength than those prepared at −20°C and −196°C with the same CHT concentration, which could be attributed to its leaf structure and pore size. There was no significant difference () in mechanical properties for PCHTs 3% (w/v) frozen at −20°C or −196°C. Thus, the range of Young’s moduli found for PCHTs suggests their application for soft tissue engineering. For hard tissues, these scaffolds must be crosslinked and/or reinforced by the addition of fillers.

The water absorption capacity (swelling property) of the scaffolds affects cell growth indirectly [64]. The hydration of the scaffolds is a necessary step for cell incorporation and proliferation.

PCHTs scaffolds showed a high swelling capacity in PBS (pH 7.2) regardless of chitosan concentration and freezing conditions, allowing for rapid hydration when culture medium was added.

Degradation in PBS. Scaffold degradation is also an important parameter for the formation of new tissue. The scaffold degradation rate must be tuned appropriately with the growth rate of the new tissue in such a way that by the time the injury site is completely regenerated, the scaffold is completely degraded [55]. Degradation can occur through mechanisms that involve physical or chemical processes and/or biological processes that are mediated by biological agents, such as enzymes [1].

Here, we evaluated in vitro the profile degradation of PCHTs in PBS (pH 7.2) at 37°C; we supposed that degradation occurred by solubilization due to the presence of residual acetate molecules.

Figure 2 shows the degradation profile of PCHTs.

We observed the highest weight loss, approximately 45%, for PCHT 1% (−20°C) after 7 days, while for PCHTs 2% (−20°C), 3% (−20°C), and 3% (−196°C) weight loss was approximately 35% after 3 days. The PCHTs 3% (−80°C) showed the lowest weight loss, probably due to their leaf structure retaining lower concentration of acetate molecules.

Our results suggest that the PCHTs need further stabilization, to ensure the balance between tissue regeneration and degradation rate of the scaffold.

3.2.3. Cell Compatibility

Figure 3 shows the cell compatibility of h-AdMSCs cultured in the presence of PCHTs, as assayed by MTT. The results revealed no potential cytotoxicity in 24 hours for the scaffolds according to the standard values (PTC).

However, we observed lower proliferation of h-AdMSCs on PCHTs prepared with chitosan concentration of 3% (w/v) compared to the negative control.

Nevertheless, the PCHTs are potentially useful for in vivo applications regardless of CHT concentration and freezing conditions.

3.3. Characterization of the Composite Scaffolds

3.3.1. Images of the Cell-Seeded P-PRP/PCHTs

SEM characterization (Figure 4) of the P-PRP/PCHTs on the 5th day of culture showed fibrin networks covering the pores and surface of PCHTs, as a consequence of the interaction of fibrin fibers and CHT. This interaction supported cell proliferation by improving the mechanical strength of the fibrin network, in addition to providing additional surface area to cell adhesion, proliferation, and differentiation.

(a)

(b)

(c)

(d)

(e)

(f)

3.3.2. Growth Factor Release

Figure 5 shows PDGF-AB and TGF-β1 release kinetics from P-PCHTs determined by ELISA.

(a)

(b)

(c)

(d)

Figure 5

Release profiles of growth factors from P-PRP in porous chitosan scaffolds as a function of ((a), (b)) chitosan concentrations and ((c), (d)) freezing conditions. (■) PCHTs 1% (−20°C); (●) PCHTs 2% (−20°C); (▲) PCHTs 3% (−20°C); (□) PCHTs 3% (−80°C), (O) PCHTs 3% (−196°C), and () P-PRP activated with Ca⁺²/thrombin (used as control); TGF-β1 ((a), (c)); and PDGF-AB ((b), (d)). The concentration of platelets in P-PRP was 472,250 pq/mm³. Activated P-PRP alone was used as control.

The curves show diffusion profiles, indicating no collapse of the porous structure of chitosan scaffolds during the course of the assays, regardless of the CHT concentration and freezing conditions.

PDGF-AB released from PCHTs ended within 24 hours of incubation, whereas TGF-β1 tended to continue after 72 hours.

A controlled release of TGF-β1 and PDGF-AB was achieved for all CHT concentrations, related to the scaffolds of activated P-PRP only. The slowest release was observed for a chitosan concentration of 3%.

In contrast, for the PCHTs 3% freezing at −80°C and −196°C, we observed a controlled release of TGF-β1, but a strong burst release of PDGF-AB.

Thus, PCHTs prepared with 3% CHT at −20°C provided a controlled release of PDGF-AB and TGF-β1 and can be an efficient vehicle for release of GFs from PRP.

3.3.3. h-AdMSCs-Seeded Proliferation

Figure 6 shows the proliferation profile of h-AdMSCs cultured in P-PRP/PCHTs.

(a)

(b)

The cell number per well determined after 3 days exceeded the number of seeded cells (1.4 × 10⁴ cells/well) in all the P-PRP/PCHTs, meaning that the cells kept in the matrices retained their viability, regardless of the CHT concentration and freezing conditions.

The cell number per well of P-PRP/PCHTs prepared with 1, 2, and 3% (w/v) of chitosan (Figure 6(a)) showed significant differences () compared to control (P-PRP). Therefore, PCHTs should have stabilized fibrin networks as we initially hypothesized.

However, regarding freezing condition, no significant variations for P-PRP/PCHTs prepared at −80°C or −196°C and P-PRP were observed (Figure 6(b)). In all cases, cell viability decreased after 7 days, probably due to collapse of the structure.

We also observed that the exponential phase of the cultures (Figure 6(a)) started after the maximum release of GFs (Figure 5), and the decline phase matched the largest weight loss of the PCHTs (Figure 2).

3.3.4. Induction of Osteogenic Differentiation

Osteogenic differentiation of h-AdMSCs was investigated 14 days after cell seeding. ALP, an early marker of osteogenic differentiation, was determined, and the results are shown in Figure 7. The expression of ALP activity showed no significant difference () with CHT concentration. However, higher osteogenic differentiation was obtained with P-PRP/PCHTs 3% (−196°C).

4. Conclusions

Composite scaffolds were prepared with porous chitosan and -PRP. The performance of the composite scaffolds was superior to P-PRP alone, indicating that the porous chitosan stabilized the fibrin network, supporting our initial hypothesis.

Chitosan concentration and freezing conditions influenced the physicochemical and biological properties of the scaffolds. On the average, physicochemical, mechanical, and h-AdMSCs proliferation improved by the use of 3% (w/v) chitosan and −20°C freezing temperature, while −196°C favored osteogenic differentiation. Additional stabilization of the porous structure is needed for applications in regenerative medicine.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors acknowledge the financial support from the National Council of Technological and Scientific Development (CNPq, Brazil). They also thank Dr. William Dias Belangero and Dr. Ana Amélia Rodrigues of the Faculty of Medical Sciences (University of Campinas) for the MTT results and Dr. Ângela Cristina Malheiros Luzo of the Haematology and Hemotherapy Center (University of Campinas) for the donation of h-AdMSCs.

References

R. Langer and J. P. Vacanti, “Tissue engineering,” Science, vol. 260, no. 5110, pp. 920–926, 1993.
View at: Publisher Site | Google Scholar
G. Chen, T. Ushida, and T. Tateishi, “Scaffold design for tissue engineering,” Macromolecular Bioscience, vol. 2, no. 2, pp. 67–77, 2002.
View at: Publisher Site | Google Scholar
D. Crane and P. A. M. Everts, “Platelet rich plasma (PRP) matrix grafts,” Practical Pain Management, vol. 8, pp. 12–27, 2008.
View at: Google Scholar
H.-I. Chang and Y. Wang, “Cell responses to surface and architecture of tissue engineering scaffolds,” in Regenerative Medicine and Tissue Engineering—Cells and Biomaterials, D. Eberli, Ed., chapter 27, pp. 569–588, InTech, Rijeka, Croatia, 2011.
View at: Google Scholar
W. Bensaïd, J. T. Triffitt, C. Blanchat, K. Oudina, L. Sedel, and H. Petite, “A biodegradable fibrin scaffold for mesenchymal stem cell transplantation,” Biomaterials, vol. 24, no. 14, pp. 2497–2502, 2003.
View at: Publisher Site | Google Scholar
J. W. Weisel and C. Nagaswami, “Computer modeling of fibrin polymerization kinetics correlated with electron microscope and turbidity observations: clot structure and assembly are kinetically controlled,” Biophysical Journal, vol. 63, no. 1, pp. 111–128, 1992.
View at: Publisher Site | Google Scholar
M. R. Falvo, O. V. Gorkun, and S. T. Lord, “The molecular origins of the mechanical properties of fibrin,” Biophysical Chemistry, vol. 152, no. 1–3, pp. 15–20, 2010.
View at: Publisher Site | Google Scholar
E. A. Ryan, L. F. Mockros, J. W. Weisel, and L. Lorand, “Structural origins of fibrin clot rheology,” Biophysical Journal, vol. 77, no. 5, pp. 2813–2826, 1999.
View at: Publisher Site | Google Scholar
K. Kojima, Y. Okamoto, K. Miyatake, H. Fujise, Y. Shigemasa, and S. Minami, “Effects of chitin and chitosan on collagen synthesis in wound healing,” Journal of Veterinary Medical Science, vol. 66, no. 12, pp. 1595–1598, 2004.
View at: Publisher Site | Google Scholar
Y. Okamoto, R. Yano, K. Miyatake, I. Tomohiro, Y. Shigemasa, and S. Minami, “Effects of chitin and chitosan on blood coagulation,” Carbohydrate Polymers, vol. 53, no. 3, pp. 337–342, 2003.
View at: Publisher Site | Google Scholar
E.-C. Shen, T.-C. Chou, C.-H. Gau, H.-P. Tu, Y.-T. Chen, and E. Fu, “Releasing growth factors from activated human platelets after chitosan stimulation: a possible bio-material for platelet-rich plasma preparation,” Clinical Oral Implants Research, vol. 17, no. 5, pp. 572–578, 2006.
View at: Publisher Site | Google Scholar
S. J. Chang, S. M. Kuo, C.-W. Lan, I. Manousakas, and P. H. Tsai, “Evaluation of chitosan/CaSO₄/platelet-rich plasma microsphere composites as alveolus osteogenesis material,” Biomedical Engineering: Applications, Basis and Communications, vol. 21, no. 2, pp. 115–122, 2009.
View at: Publisher Site | Google Scholar
B. Kutlu, R. S. T. Aydin, A. C. Akman, M. Gümüşderelioglu, and R. M. Nohutcu, “Platelet-rich plasma-loaded chitosan scaffolds: preparation and growth factor release kinetics,” Journal of Biomedical Materials Research Part B: Applied Biomaterials, vol. 101, no. 1, pp. 28–35, 2013.
View at: Publisher Site | Google Scholar
E. O. Oktay, B. Demiralp, S. Senel, A. Cevdet Akman, K. Eratalay, and H. Akincibay, “Effects of platelet-rich plasma and chitosan combination on bone regeneration in experimental rabbit cranial defects,” The Journal of Oral Implantology, vol. 36, no. 3, pp. 175–184, 2010.
View at: Publisher Site | Google Scholar
S. Mathews, R. Bhonde, P. K. Gupta, and S. Totey, “A novel tripolymer coating demonstrating the synergistic effect of chitosan, collagen type 1 and hyaluronic acid on osteogenic differentiation of human bone marrow derived mesenchymal stem cells,” Biochemical and Biophysical Research Communications, vol. 414, no. 1, pp. 270–276, 2011.
View at: Publisher Site | Google Scholar
R. Muzzarelli, “Chitosan,” in Natural Chelating Polymers, R. Muzzarelli, Ed., pp. 144–176, Pergamon Press, Oxford, UK, 1973.
View at: Google Scholar
J. Berger, M. Reist, J. M. Mayer, O. Felt, N. A. Peppas, and R. Gurny, “Structure and interactions in covalently and ionically crosslinked chitosan hydrogels for biomedical applications,” European Journal of Pharmaceutics and Biopharmaceutics, vol. 57, no. 1, pp. 19–34, 2004.
View at: Publisher Site | Google Scholar
N. Nwe, T. Furuike, and H. Tamura, “The mechanical and biological properties of chitosan scaffolds for tissue regeneration templates are significantly enhanced by chitosan from Gongronella butleri,” Materials, vol. 2, no. 2, pp. 374–398, 2009.
View at: Publisher Site | Google Scholar
A. M. Martins, G. Eng, S. G. Caridade, J. F. Mano, R. L. Reis, and G. Vunjak-Novakovic, “Electrically conductive chitosan/carbon scaffolds for cardiac tissue engineering,” Biomacromolecules, vol. 15, no. 2, pp. 635–643, 2014.
View at: Publisher Site | Google Scholar
R. J. Nordtveit, K. M. Vårum, and O. Smidsrød, “Degradation of partially N-acetylated chitosans with hen egg white and human lysozyme,” Carbohydrate Polymers, vol. 29, no. 2, pp. 163–167, 1996.
View at: Publisher Site | Google Scholar
D. Koga, “Chitin enzymology—chitinase,” in Advances in Chitin Science, R. Chen and H. C. Chen, Eds., vol. 3, pp. 16–23, 1998.
View at: Google Scholar
G. Molinaro, J.-C. Leroux, J. Damas, and A. Adam, “Biocompatibility of thermosensitive chitosan-based hydrogels: an in vivo experimental approach to injectable biomaterials,” Biomaterials, vol. 23, no. 13, pp. 2717–2722, 2002.
View at: Publisher Site | Google Scholar
M. Rücker, M. W. Laschke, D. Junker et al., “Angiogenic and inflammatory response to biodegradable scaffolds in dorsal skinfold chambers of mice,” Biomaterials, vol. 27, no. 29, pp. 5027–5038, 2006.
View at: Publisher Site | Google Scholar
R. Muzzarelli, R. Tarsi, O. Filippini, E. Giovanetti, G. Biagini, and P. E. Varaldo, “Antimicrobial properties of N-carboxybutyl chitosan,” Antimicrobial Agents and Chemotherapy, vol. 34, no. 10, pp. 2019–2023, 1990.
View at: Publisher Site | Google Scholar
X. Li, M. Min, N. Du et al., “Chitin, chitosan, and glycated chitosan regulate immune responses: the novel adjuvants for cancer vaccine,” Clinical and Developmental Immunology, vol. 2013, Article ID 387023, 8 pages, 2013.
View at: Publisher Site | Google Scholar
P. He, S. S. Davis, and L. Illum, “In vitro evaluation of the mucoadhesive properties of chitosan microspheres,” International Journal of Pharmaceutics, vol. 166, no. 1, pp. 75–88, 1998.
View at: Publisher Site | Google Scholar
U. Bertram and R. Bodmeier, “In situ gelling, bioadhesive nasal inserts for extended drug delivery: in vitro characterization of a new nasal dosage form,” European Journal of Pharmaceutical Sciences, vol. 27, no. 1, pp. 62–71, 2006.
View at: Publisher Site | Google Scholar
S. F. Antonov, E. V. Kryzhanovskaya, Y. I. Filippov, S. M. Shinkarev, and M. A. Frolova, “Study of wound-healing properties of chitosan,” Russian Agricultural Sciences, vol. 34, no. 6, pp. 426–427, 2008.
View at: Publisher Site | Google Scholar
T. Dai, M. Tanaka, Y.-Y. Huang, and M. R. Hamblin, “Chitosan preparations for wounds and burns: antimicrobial and wound-healing effects,” Expert Review of Anti-Infective Therapy, vol. 9, no. 7, pp. 857–879, 2011.
View at: Publisher Site | Google Scholar
S. A. Agnihotri, N. N. Mallikarjuna, and T. M. Aminabhavi, “Recent advances on chitosan-based micro- and nanoparticles in drug delivery,” Journal of Controlled Release, vol. 100, no. 1, pp. 5–28, 2004.
View at: Publisher Site | Google Scholar
I. Adekogbe and A. Ghanem, “Fabrication and characterization of DTBP-crosslinked chitosan scaffolds for skin tissue engineering,” Biomaterials, vol. 26, no. 35, pp. 7241–7250, 2005.
View at: Publisher Site | Google Scholar
M. Mucha, I. Michalak, J. Balcerzak, and M. Tylman, “Chitosan scaffolds, films and microgranules for medical application—preparation and drug release studies,” Polimery, vol. 57, no. 10, pp. 714–721, 2012.
View at: Google Scholar
S. V. Madihally and H. W. T. Matthew, “Porous chitosan scaffolds for tissue engineering,” Biomaterials, vol. 20, no. 12, pp. 1133–1142, 1999.
View at: Publisher Site | Google Scholar
F. Amaral, P. Sampaio, and M. A. Barbosa, “Three-dimensional culture of human osteoblastic cells in chitosan sponges: the effect of the degree of acetylation,” Journal of Biomedical Materials Research A, vol. 76, no. 2, pp. 335–346, 2006.
View at: Publisher Site | Google Scholar
T. Majima, T. Irie, N. Sawaguchi et al., “Chitosan-based hyaluronan hybrid polymer fibre scaffold for ligament and tendon tissue engineering,” Proceedings of the Institution of Mechanical Engineers, Part H: Journal of Engineering in Medicine, vol. 221, no. 5, pp. 537–546, 2007.
View at: Publisher Site | Google Scholar
X. Z. Shu and K. J. Zhu, “Controlled drug release properties of ionically cross-linked chitosan beads: the influence of anion structure,” International Journal of Pharmaceutics, vol. 233, no. 1-2, pp. 217–225, 2002.
View at: Publisher Site | Google Scholar
H. P. Tan, C. R. Chu, K. A. Payne, and K. G. Marra, “Injectable in situ forming biodegradable chitosan-hyaluronic acid based hydrogels for cartilage tissue engineering,” Biomaterials, vol. 30, no. 13, pp. 2499–2506, 2009.
View at: Publisher Site | Google Scholar
M. Lavertu, S. Méthot, N. Tran-Khanh, and M. D. Buschmann, “High efficiency gene transfer using chitosan/DNA nanoparticles with specific combinations of molecular weight and degree of deacetylation,” Biomaterials, vol. 27, no. 27, pp. 4815–4824, 2006.
View at: Publisher Site | Google Scholar
S. B. Rao and C. P. Sharma, “Sterilization of chitosan: implications,” Journal of Biomaterials Applications, vol. 10, no. 2, pp. 136–143, 1995.
View at: Google Scholar
S. Cardea, P. Pisanti, and E. Reverchon, “Generation of chitosan nanoporous structures for tissue engineering applications using a supercritical fluid assisted process,” The Journal of Supercritical Fluids, vol. 54, no. 3, pp. 290–295, 2010.
View at: Publisher Site | Google Scholar
A. R. Costa-Pinto, R. L. Reis, and N. M. Neves, “Scaffolds based bone tissue engineering: the role of chitosan,” Tissue Engineering Part B: Reviews, vol. 17, no. 5, pp. 331–347, 2011.
View at: Publisher Site | Google Scholar
F. Shen, Y. L. Cui, L. F. Yang et al., “A study on the fabrication of porous chitosan/gelatin network scaffold for tissue engineering,” Polymer International, vol. 49, no. 12, pp. 1596–1599, 2000.
View at: Publisher Site | Google Scholar
D. L. Nettles, S. H. Elder, and J. A. Gilbert, “Potential use of chitosan as a cell scaffold material for cartilage tissue engineering,” Tissue Engineering, vol. 8, no. 6, pp. 1009–1016, 2002.
View at: Publisher Site | Google Scholar
A. Nasti, N. M. Zaki, P. de Leonardis et al., “Chitosan/TPP and chitosan/TPP-hyaluronic acid nanoparticles: systematic optimisation of the preparative process and preliminary biological evaluation,” Pharmaceutical Research, vol. 26, no. 8, pp. 1918–1930, 2009.
View at: Publisher Site | Google Scholar
C. R. Correia, L. S. Moreira-Teixeira, L. Moroni et al., “Chitosan scaffolds containing hyaluronic acid for cartilage tissue engineering,” Tissue Engineering—Part C: Methods, vol. 17, no. 7, pp. 717–730, 2011.
View at: Publisher Site | Google Scholar
S. Tang and M. Spector, “Incorporation of hyaluronic acid into collagen scaffolds for the control of chondrocyte-mediated contraction and chondrogenesis,” Biomedical Materials, vol. 2, no. 3, pp. S135–S141, 2007.
View at: Publisher Site | Google Scholar
Y.-C. Wang, M.-C. Lin, D.-M. Wang, and H.-J. Hsieh, “Fabrication of a novel porous PGA-chitosan hybrid matrix for tissue engineering,” Biomaterials, vol. 24, no. 6, pp. 1047–1057, 2003.
View at: Publisher Site | Google Scholar
T. Mosmann, “Rapid colorimetric assay for cellular growth and survival: application to proliferation and cytotoxicity assays,” Journal of Immunological Methods, vol. 65, no. 1-2, pp. 55–63, 1983.
View at: Publisher Site | Google Scholar
M. Gümüdereliolu and S. Aday, “Heparin-functionalized chitosan scaffolds for bone tissue engineering,” Carbohydrate Research, vol. 346, no. 5, pp. 606–613, 2011.
View at: Publisher Site | Google Scholar
A. G. M. Perez, R. Lichy, J. F. S. D. Lana et al., “Prediction and modulation of platelet recovery by discontinuous centrifugation of whole blood for the preparation of pure platelet-rich plasma,” BioResearch Open Access, vol. 2, no. 4, pp. 307–314, 2013.
View at: Publisher Site | Google Scholar
A. G. M. Perez, A. A. Rodrigues, A. C. M. Luzo, J. F. S. D. Lana, W. D. Belangero, and M. H. A. Santana, “Fibrin network architectures in pure platelet-rich plasma as characterized by fiber radius and correlated with clotting time,” Journal of Materials Science: Materials in Medicine, vol. 25, no. 8, pp. 1967–1977, 2014.
View at: Publisher Site | Google Scholar
J. H. Brauker, V. E. Carr-Brendel, L. A. Martinson, J. Crudele, W. D. Johnston, and R. C. Johnson, “Neovascularization of synthetic membranes directed by membrane microarchitecture,” Journal of Biomedical Materials Research, vol. 29, no. 12, pp. 1517–1524, 1995.
View at: Publisher Site | Google Scholar
J. J. Klawitter and S. F. Hulbert, “Application of porous ceramics for the attachment of load-bearing internal orthopedic applications,” Journal of Biomedical Materials Research A Symposium, vol. 5, no. 6, pp. 161–229, 1971.
View at: Publisher Site | Google Scholar
S. Yang, K.-F. Leong, Z. Du, and C.-K. Chua, “The design of scaffolds for use in tissue engineering. Part I. Traditional factors,” Tissue Engineering, vol. 7, no. 6, pp. 679–689, 2001.
View at: Publisher Site | Google Scholar
A. J. Salgado, O. P. Coutinho, and R. L. Reis, “Bone tissue engineering: state of the art and future trends,” Macromolecular Bioscience, vol. 4, no. 8, pp. 743–765, 2004.
View at: Publisher Site | Google Scholar
I. V. Yannas, E. Lee, D. P. Orgill, E. M. Skrabut, and G. F. Murphy, “Synthesis and characterization of a model extracellular matrix that induces partial regeneration of adult mammalian skin,” Proceedings of the National Academy of Sciences of the United States of America, vol. 86, no. 3, pp. 933–937, 1989.
View at: Publisher Site | Google Scholar
C. Chavez-Munoz, K. T. Nguyen, W. Xu, S.-J. Hong, T. A. Mustoe, and R. D. Galiano, “Transdifferentiation of adipose-derived stem cells into keratinocyte-like cells: engineering a stratified epidermis,” PLoS ONE, vol. 8, no. 12, Article ID e80587, 2013.
View at: Publisher Site | Google Scholar
C. A. Léon y León, “New perspectives in mercury porosimetry,” Advances in Colloid and Interface Science, vol. 76-77, pp. 341–372, 1998.
View at: Publisher Site | Google Scholar
K. F. Leong, C. M. Cheah, and C. K. Chua, “Solid freeform fabrication of three-dimensional scaffolds for engineering replacement tissues and organs,” Biomaterials, vol. 24, no. 13, pp. 2363–2378, 2003.
View at: Publisher Site | Google Scholar
X. Liu and P. X. Ma, “Polymeric scaffolds for bone tissue engineering,” Annals of Biomedical Engineering, vol. 32, no. 3, pp. 477–486, 2004.
View at: Publisher Site | Google Scholar
Q. L. Loh and C. Choong, “Three-dimensional scaffolds for tissue engineering applications: role of porosity and pore size,” Tissue Engineering Part B: Reviews, vol. 19, no. 6, pp. 485–503, 2013.
View at: Publisher Site | Google Scholar
H.-Y. Cheung, Q.-T. Lau, T.-P. Lu, and D. Hui, “A critical review on polymer-based bio-engineered materials for scaffold development,” Composites Part B: Engineering, vol. 38, no. 3, pp. 291–300, 2007.
View at: Publisher Site | Google Scholar
S. J. Hollister, “Porous scaffold design for tissue engineering,” Nature Materials, vol. 4, no. 7, pp. 518–524, 2005.
View at: Publisher Site | Google Scholar
J. Enrione, F. Osorio, D. López et al., “Characterization of a Gelatin/chitosan/hyaluronan scaffold-polymer,” Electronic Journal of Biotechnology, vol. 13, no. 5, pp. 1–11, 2010.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2015 Andréa Arruda Martins Shimojo et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1900

Downloads

1524

Citations