Abstract

The crystallographic orientation distribution and the geometrical lamellae orientation distribution in lamellar eutectics are, in general, not independent of each other. The combined orientation-lamellae distribution function depends on five angular parameters. X-ray diffraction in such eutectics may exhibit an anisotropic macroscopic absorption factor if the penetration depth of the X-rays is large compared with their planar size. As a consequence, the reflected X-ray intensity may depend on a third angle γ, i.e. a rotation of the sample about the diffraction vector s additionally to the usual pole figure angles α, β which describe the orientation of the diffraction vector s with respect to the sample coordinate system. It is thus necessary to measure three-dimensional generalized pole figures instead of conventional two-dimensional ones.