Research Article
Surface Characteristics and High Cycle Fatigue Performance of Shot Peened Magnesium Alloy ZK60
Figure 11
Fatigue fractures of ZK60-T5 alloy after SP: (a) overall fracture surface and (b) crack initiation site, EP, 160 MPa; (c) overall fracture surface and (d) crack initiation site, 0.05 mmN, 200 MPa; (e) overall fracture surface and (f) crack initiation site, 0.30 mmN, 185 MPa.