<svg style="vertical-align:-4.67647pt;width:64.375px;" id="M1" height="21.1" version="1.1" viewBox="0 0 64.375 21.1" width="64.375" xmlns="http://www.w3.org/2000/svg"><g transform="matrix(1.25,0,0,-1.25,0,21.1)"><g transform="translate(72,-55.12)"><text transform="matrix(1,0,0,-1,-71.95,59.83)"><tspan style="font-size: 17.93px; " x="0" y="0">M</tspan><tspan style="font-size: 17.93px; " x="15.942437" y="0">n</tspan></text><text transform="matrix(1,0,0,-1,-47.04,55.34)"><tspan style="font-size: 12.55px; " x="0" y="0">3</tspan></text><text transform="matrix(1,0,0,-1,-40.27,59.83)"><tspan style="font-size: 17.93px; " x="0" y="0">O</tspan></text><text transform="matrix(1,0,0,-1,-27.32,55.34)"><tspan style="font-size: 12.55px; " x="0" y="0">4</tspan></text></g></g></svg> Nanoparticles: Synthesis, Characterization, and Dielectric Properties

Dhaouadi, Hassouna; Ghodbane, Ouassim; Hosni, Faouzi; Touati, Fathi

doi:https://doi.org/10.5402/2012/706398

International Scholarly Research Notices

On this page

Abstract Introduction Results and Discussion Conclusion References Copyright Related Articles

Research Article | Open Access

Volume 2012 | Article ID 706398 | https://doi.org/10.5402/2012/706398

Nanoparticles: Synthesis, Characterization, and Dielectric Properties

Hassouna Dhaouadi,¹Ouassim Ghodbane,¹Faouzi Hosni,²and Fathi Touati¹

Academic Editor: M. Soylak, J. M. Saniger

Received11 Dec 2011

Accepted02 Jan 2012

Published15 Feb 2012

Abstract

nanoparticles were prepared by a simple chemical route using cetyltetramethylammonium bromide (CTAB) as a template agent. nanocrystals present an octahedral shape, and their crystallite size varies between 20 and 80 nm. They were characterized by XRD, SEM, DTA/TG, and IR spectroscopy. XRD studies confirm the presence of a highly crystalline phase. The Rietveld refinement of the X-ray diffraction data confirms that nanoparticles crystallize in the tetragonal system with space group I41/amd. DTA/TG and XRD measurements demonstrate the phase transition toward a spinel structure between 25 and . The electrical conductivity increases between 80 and , suggesting a semiconducting behaviour of . Both dielectric dispersion (ε′) and dielectric loss (ε′′) were investigated from 80 and in the frequency range of 10 Hz–13 MHz. The dielectric properties showed typical dielectric dispersion based on the Maxwell-Wagner model.

1. Introduction

Metal oxide nanocrystals are widely applied in catalysis, energy storage, magnetic data storage, sensors, and ferrofluids [1–4]. Tetramanganese oxides (Mn₃O₄) are particularly used as main sources of ferrite materials [5] and applied in numerous industrial fields such as magnetic [6], electrochemical [7], and catalysis [8, 9]. The particle size and morphology may be controlled by using various methods including solvothermal/hydrothermal [10, 11], vapor phase growth [12], vacuum calcining precursors [13], thermal decomposition [14], ultrasonic, gamma, and microwave irradiation [15–17], and chemical liquid homogeneous precipitation [18]. Therefore, Mn₃O₄ compounds show distinct shapes including nanoparticles [19], nanorods [20], nanowires [21], and tetragonal particles [22].

The electrical and magnetic properties of numerous nanomaterials are completely different from those of their bulk counterparts. Changes in dielectric properties were attributed to changes in particle size, shape, and boundaries [23, 24]. The modified dielectric properties were used as capacitors, electronic memories, and optical filters. Materials exhibiting a giant dielectric constant were already reported elsewhere [25–27]. The high dielectric permittivity and the low loss factors over a wide frequency range are always of a great interest [28]. In a previous work, we synthesized Mn₃O₄ nanomaterials with lozenge morphology under hydrothermal treatment [29]. The temperature dependence of the conductivity between 25 and 220°C obeys the Arrhenius law with activation energy of 0.48 eV. However, the present work describes the preparation of Mn₃O₄ nanomaterials with octahedral shape at room temperature by using a precipitation method. The magnetic properties of the Mn₃O₄ nanocrystals are also studied by the electron paramagnetic resonance (EPR) technique. To the best of our knowledge, only a limited number of studies of the dielectric properties of nanostructured Mn₃O₄ were reported [30–32]. The scope of the present work is to study the dielectric properties of nanostructured Mn₃O₄ nanoparticles as a function of the frequency and the temperature.

2. Experimental Procedure

2.1. Sample Preparation

The synthesis of Mn₃O₄ nanoparticles was performed at room temperature, using the precipitation route [18]. 0.22 mol of MnCl₂·6H₂O (Aldrich) was added to 0.44 mol of NaOH (Fluka) aqueous solution. Then 1.37 mmol cetyltetramethylammonium bromide (CTAB) (Sigma) was dispersed and homogenized under slowly magnetic stirring during 24 hours. The precipitate was filtered and carefully washed with distilled water for several times. The resulting product was dried in the oven at 80°C for 24 hours.

The formation of Mn₃O₄ compound in the alkaline aqueous solution may be formulated by the following reactions:

Manganese ions are firstly reduced in alkaline media to Mn(OH)₂ and then decomposed into MnO (see (2) and (3)). Finally, MnO is oxidized to Mn₃O₄ by the atmospheric oxygen.

2.2. Characterisation Techniques

X-ray powder diffraction (XRD) measurements were performed using a Panalytical XPERT PRO MPD diffractometer operating with Cu Kα radiation (). Crystallographic data (lattice parameters, space group) were determined by using the Highscore software. The XRD pattern was analyzed by the Fullprof program [33] based on the Rietveld method [34] in order to calculate the cell parameters.

Infrared (IR) spectra were recorded in the wavenumber range of 4000–400 cm⁻¹ with a “Nicolet 380 Spectrometer.” The samples were dispersed in pure KBr pellets. Thermal analyses were performed by using the “SetaramSetsys 1750” operating from 25 to 800°C at a heating rate of 5°C·min⁻¹ under air atmosphere. Scanning electron microscopy (SEM) images were obtained by a Zeiss Stereoscan 440 instrument. Conductivity measurements were carried out from 80 to 240°C with 5–20°C steps by checking the complex impedance spectroscopy with a Hewlett Packard 4129A impedance analyzer. The signal frequency ranged from 10 to 13 MHz.

3. Results and Discussion

3.1. Crystal Structure, Size, and Morphology

Figure 1 shows XRD patterns of as-prepared Mn₃O₄ nanoparticles. The diffraction peaks correspond to the tetragonal Mn₃O₄ single phase (JCPDS Card 01-080-0382). The Rietveld refinement procedure was performed for the investigation of the crystalline structure of as-prepared nanocrystallites. Figure 1 presents the experimental and calculated patterns together with the differential one, deduced from the Rietveld refinement. Mn₃O₄ X-ray data were refined in the tetragonal system (space group I41/amd). An excellent agreement between experimental and calculated patterns is obtained (). The refined cell parameters of Mn₃O₄ structure are Å, Å, and Å³. The structure was refined according to these parameters: , , , and .

The crystallite sizes were calculated from the major (211) diffraction peak using the Debye Scherrer approximation [35] and are about 50 nm. The morphology of Mn₃O₄ nanoparticles is shown in Figure 2. The formation of Mn₃O₄ nanoparticles is confirmed. Aggregated nanoparticles with octahedral shapes are observed, and their diameter varies between 20 and 80 nm. The SEM results of the Mn₃O₄ nanoparticles agree with the XRD data.

(a)

(b)

3.2. IR Absorption Spectroscopy

The IR absorption spectra of the pure CTAB and Mn₃O₄ nanopowders calcinated at different temperatures for 2 h are shown in Figure 3. The IR spectrum of as-prepared Mn₃O₄ nanoparticles without any thermal treatment displays three significant absorption bands in the range of 400–650 cm⁻¹ (Figure 3(b)). The vibration frequency located at 629 cm⁻¹ is characteristic of Mn–O stretching modes in tetrahedral sites, whereas the vibration frequency located at 510 cm⁻¹ corresponds to the distortion vibration of Mn–O in an octahedral environment. The third vibration band, located at 410 cm⁻¹, can be attributed to the vibration of manganese species (Mn³⁺–O) in the octahedral site of Mn₃O₄ [36–39]. Moreover, the broad band at 3436 cm⁻¹ and the narrow one at 1646 cm⁻¹ correspond to the O–H vibrating mode of the adsorbed water. The two intense adsorption bands located at 2920 and 2840 cm⁻¹ are assigned to the symmetric and asymmetric stretching modes of the –CH₂ group of the CTAB surfactant bounded to the surface of Mn₃O₄, respectively. A comparison of the IR spectrum for pure CTAB (Figure 3(a)) and the spectra relative to the Mn₃O₄ nanoparticles (Figures 3(b), 3(c), and 3(d)) shows invariant frequency positions at 2920, 2840 cm⁻¹, suggesting the absence of intermolecular interactions (C–H⋯O) between oxygen atoms of Mn₃O₄ nanoparticles and the –CH₂ groups belonging to the CTAB surfactant. The difference between symmetric and asymmetric scissoring vibrations of (CH₃)₃–N⁺ group of the pure CTAB (1482 cm⁻¹) and CTAB capped on the Mn₃O₄ nanoparticles surface (1429 cm⁻¹) reveals that CTAB adsorbed on the nanoparticle surface interacts strongly with oxygen atoms of Mn₃O₄ (Figure 3(b)). The single band located at 960 cm⁻¹ on CTAB spectrum (Figure 3(a)) and the narrow one at 955 cm⁻¹ (Figure 3(b)) for bounded CTAB may be assigned to the (C–N⁺) stretching mode. The frequency shift may be caused by the interaction between (CH₃)₃–N⁺ group and the oxidized metal surface [40]. This type of interaction was also observed between the polymer hydroxypropyl cellulose (HPC) used as capping agent and the silver metal surface [41].

During the heat treatment of Mn₃O₄, the progressive removal of the organic surfactant is well demonstrated by the IR spectra (Figure 3(b)–(f)) recorded at different temperatures. After two hours of thermal treatment at 500°C, vibration bands corresponding to the surfactant molecules were not observed on IR spectra, indicating that all organic groups were removed. During the heating process, a clear difference is observed in the IR spectra, in the range 700–400 cm⁻¹, corresponding of the stretching bands of Mn–O. This change in the position bands between 300 and 700°C can be related to the phase transformation of Mn₃O₄. This result is in a good agreement with X-ray diffraction data.

3.3. Thermal Analyses

In order to examine the thermal stability of Mn₃O₄ nanoparticles, thermal gravimetric (TG) and differential thermal analyses (DTA) were carried out between 25 and 800°C (Figure 4). In the temperature range of 25–250°C, the weight loss of 9.15% can be related to the release of weakly adsorbed water molecules and to the removal of the organic entities of CTAB surfactant. The broad exothermic peak at about 350°C, associated with the mass gain, is about 0.4% (Figure 4). As confirmed by earlier studies [42–44], this thermal event can be corroborated by the fact that Mn₃0₄ (, ) can be transformed into Mn₅O₈ (, ) in the temperature range of 300–450°C [45]. The new (Mn₅O₈) phase is formed according to the following reaction:

Mn₅O₈ phase is isostructural with Cd₂Mn₃O₈ and crystallizes in the monoclinic system (C2/m) [46]. Mn₅O₈ was observed during the decomposition of manganese oxalate [47] as well as in the transformation of hydrohausmannite into anhydrous hausmannite [46, 48]. The oxidation of Mn³⁺ to Mn⁴⁺ in the temperature range of 300–450°C leads to the crystallization of the Mn₅O₈ phase. After the exothermic peak at 350°C the mass remains relatively constant.

The endothermic event at 575°C, associated with the weight loss of 2.02% (calculated weight loss 1.98%), are related to the consequent release of oxygen due to the reduction of Mn₅O₈ to Mn₂O₃. The reaction scheme can be written as follows:

The weight loss is still constant at temperature higher than 700°C, indicating the completion of the thermal decomposition of the intermediate phase (Mn₅O₈) and the beginning of the crystallization of Mn₂O₃ as a new phase.

In order to give a plausible interpretation of the thermal phenomena, we also performed an investigation by X-ray diffraction analysis at different calcination temperatures for 2 h. Several samples of Mn₃O₄ nanoparticles were heated in electric oven (under air atmosphere) at different temperatures: 25, 300, 500, and 700°C, and they are immediately submitted to X-ray diffraction measurements (Figure 5). The X-ray diffraction of the product treated at 300°C is similar to that of the bare sample. This means that Mn₃O₄ nanoparticles are stable up to 300°C. In the temperature range of 25–300°C, XRD peaks gradually become sharper and higher, indicating an improved crystallinity. The X-ray diffraction spectrum at 500°C shows some additional peaks (Figure 5(c)). These diffraction peaks cannot be attributed to Mn₂O₃, and they are distinguishable from those of Mn₃O₄. They are observed at 21.741, 31.916, 35.400, 39.250, 47.801, and 66.190° and indexed to (−201), (020), (−401), (002), (−421), and (−223) Bragg peaks, respectively. The corresponding phase is identified as Mn₅O₈ (JCPDS card no. 00-039-1218) [44]. It was already established that Mn₅O₈ is stable up to 550°C and transforms to Mn₂O₃ and Mn₃O₄ phases [49]. In the present case, after calcination at 700°C, the XRD spectrum (Figure 5(d)) shows that all diffraction peaks of Mn₅O₈ and Mn₃O₄ phases disappear. In the same way, a new phase Mn₂O₃ appears (JCPDS card no. 00-41-1442) with typical peaks at 19.02, 23.28, 33.07, 35.87, 38.49, 55.44, and 65.92°. These peaks are indexed to (200), (211), (222), (321), (400), (440), and (622), respectively.

Paramagnetic properties of Mn₃O₄ nanoparticles calcined at different temperatures (25°C, 300°C, and 500°C) and cooled at room temperature were studied by the EPR technique (Figure 6). The paramagnetic properties were used in order to study the valence state changes of manganese element as a function of the temperature. Figures 6(a) and 6(b) indicate that the spectra mainly consist in one resonance line centered at that characterizes the unique paramagnetic center (Mn²⁺) at each resonance feature. The broad EPR line seems to be originating from the electrostatic and dipolar interactions between the manganese ions with mixed valence states. Figure 6(c) shows two resonance peaks corresponding to the paramagnetic centers Mn²⁺ and Mn⁴⁺, respectively. This indicates the presence of two Mn₅O₈ (, ) and Mn₃O₄ (, ) phases around 500°C. Such a result is in good agreement with the XRD and thermal data and confirms the presence of two phases Mn₃O₄ and Mn₅O₈ around 500°C.

(a)

(b)

(c)

3.4. Conductivity Study

The temperature variation of the electrical conductivity between 80 and 300°C is represented in Figure 7 in the form of Ln (σT) versus 10⁴/T. The electrical conductivity increases with increasing temperature. In the temperature range 80–140°C, the electrical conductivity approximately presents an Arrhenius-type behavior with an activation energy of . Around 140°C, a break in the curve is observed, accompanied by an increase of the activation energy (). This behaviour may be related to the removal of water molecules, residual ions, and organic surfactant capped on the surface of Mn₃O₄ particles. This probably affects the conductivity mechanism. It was reported elsewhere that the change in the slope does not occur for Mn₃O₄ nanoplatelet preliminarily heated at 300°C before being used in the conductivity study [29]. Larson and Arnott have measured the electrical conductivity of Mn₃O₄ bulk materials in the range 0–200°C. The obtained activation energy is 0.75 eV [50].

3.5. Dielectric Analysis

The complex dielectric permittivity is represented by ε* = ε′− iε′′, where ε′ is the real part of the dielectric permittivity that describes the stored energy, while ε′′ is the imaginary part of dielectric permittivity related to the dissipation energy (or loss of energy) within the medium [51]. Figure 8(a) shows that the dielectric constant (ε′) decreases continuously at lower frequencies and remains constant at higher frequencies giving rise to a plateau. The monotonous decrease in the value of dielectric constant on increasing frequency may be attributed to a combined contribution due to electronic, ionic, and interfacial polarization at low frequencies [52]. The observed dielectric dispersion at low frequencies can be explained on the basis of the Maxwell-Wagner theory of interfacial polarization [53]. According to the Maxwell-Wagner model, the dielectric structure of ferrites consists in two layers. The first layer represents a large number of grains that act as conducting layer at higher frequencies and the other layer consists in grain boundaries that act as highly resistive medium at lower frequencies. Similar results were observed for ferrite nanoparticles (Mn_0.2Ni_0.8Fe₂O₄) [54] as well as in bulk SrNb₂O₆ material [55]. At low frequencies, the polarization process in Mn₃O₄ nanoparticles is explained as a local displacement of electrons by hopping mechanism between Mn²⁺ and Mn³⁺ and an orientation of electric dipole in the direction of the applied field. With increasing the frequency, electric dipoles, and the Mn²⁺/Mn³⁺ electron transfer, the net displacement of charge in one direction decreases and then the dielectric constant decreases. The high dielectric values of the Mn₃O₄ nanoparticles are observed for other compounds such as ZnO nanotubes [56] and Mn_0.2Ni_0.8Fe₂O₄ nanoparticles [54] and for the bulk Mn-Mg spinel ferrite [57]. The large value of dielectric constant is due to the fact that Mn₃O₄ acts as a nanodipole under electric fields. The small-size particles involve large number of particles per unit volume resulting in an increase of the dipole moment per unit volume and the high dielectric constant.

(a)

(b)

(c)

(d)

The temperature dependence of dielectric permittivity (ε′) at selected frequencies is represented in Figure 8(b). The dielectric permittivity increases gradually with the temperature until reaching a maximum value of . On the other hand, relaxor ferroelectrics show a broad peak for the permittivity variation with the temperature at large frequency dispersion [58]. In the present case, a broad peak was observed in the temperature range of 90–120°C at low frequencies (Figure 8(b)). Other compounds show relaxor dielectric response such as CrTiNbO₆ [59] and FeTiNbO₆ [59]. The relatively insignificant variation of dielectric permittivity with the temperature observed at higher frequencies is attributed to atomic and electronic polarizations.

The imaginary part of the dielectric permittivity ε′′ shows higher values that decrease rapidly with the frequency and increase as the temperature rises (Figure 8(c)). For nanometer-sized particles, the contribution of the interfacial loss and the loss from electrical conductivity is dominant at lower frequencies, but at high frequencies these losses are negligible. This may explain the decrease in dielectric constant (ε′′) observed at high frequencies. The large value of the dielectric constant ε′′ at lower frequency is due to the predominance of Mn²⁺ ions, oxygen vacancies, and grain boundary defects [60, 61]. Figure 8(d) indicates that the imaginary part ε′′ is fluctuating and increasing as a function of the temperature at higher frequencies. This suggests that the temperature dependency of the imaginary part is strongly dependent on the frequency range.

4. Conclusion

Mn₃O₄ nanoparticles were successfully prepared by using the precipitation method at room temperature in the presence of CTAB, as a template agent. X-ray structural analyses confirmed that Mn₃O₄ nanoparticles crystallize in the tetragonal system. From XRD and SEM results, Mn₃O₄ nanoparticles exhibit a crystallite size between 20 and 80 nm. XRD and DTA/TG analyses show the apparition of the metastable Mn₅O₈ phase at about 350°C. The paramagnetic properties of Mn₃O₄ samples were studied by the EPR technique in order to study the valence state changes with the temperature and to confirm the presence of the metastable Mn₅O₈ phase around 350°C. Dielectric measurement results show that ε′ and ε′′ decrease as the frequency increases. The dielectric dispersion ε′ and the dielectric absorption ε′′ of Mn₃O₄ nanoparticles are found to be slightly temperature dependent at higher frequency. These results indicate that the dielectric properties showed a usual dielectric dispersion explained on the basis of the Maxwell-Wagner model.

References

A. J. Zarur and J. V. Ying, “Reverse microemulsion synthesis of nanostructured complex oxides for catalytic combustion,” Nature, vol. 403, no. 6765, pp. 65–67, 2000.
View at: Publisher Site | Google Scholar
S. A. Majetich and Y. Jin, “Magnetization directions of individual nanoparticles,” Science, vol. 284, no. 5413, pp. 470–473, 1999.
View at: Publisher Site | Google Scholar
C. Nayral, E. Viala, P. Fau et al., “Synthesis of tin and tin oxide nanoparticles of low size dispersity for application in gas sensing,” Chemistry. A European Journal, vol. 6, no. 22, pp. 4082–4090, 2000.
View at: Google Scholar
K. Raj and R. Moskowits, “Commercial applications of Ferro fluids,” Journal of Magnetism and Magnetic Materials, vol. 685, p. 233, 1990.
View at: Google Scholar
G. R. Mohan, D. Ravinder, A. V. Ramana Reddy, and B. S. Boyanov, “Dielectric properties of polycrystalline mixed nickel-zinc ferrites,” Materials Letters, vol. 40, no. 1, pp. 39–45, 1999.
View at: Publisher Site | Google Scholar
A. Buckelew, J. R. Galán-Mascarós, and K. R. Dunbar, “Facile conversion of the face-centered cubic prussian-blue material K₂[Mn₂(CN)₆] into the spinel oxide Mn₃O₄ at the solid/water interface,” Advanced Materials, vol. 14, no. 22, pp. 1646–1648, 2002.
View at: Publisher Site | Google Scholar
S. T. Myung, S. Komaba, and N. Kumagai, “Hydrothermal synthesis and electrochemical behavior of orthorhombic LiMnO₂,” Electrochimica Acta, vol. 47, no. 20, pp. 3287–3295, 2002.
View at: Publisher Site | Google Scholar
E. J. Grootendorst, Y. Verbeek, and V. Ponec, “The role of the mars and van krevelen mechanism in the selective oxidation of nitrosobenzene and the deoxygenation of nitrobenzene on oxidic catalysts,” Journal of Catalysis, vol. 157, no. 2, pp. 706–712, 1995.
View at: Publisher Site | Google Scholar
E. R. Stobbe, B. A. De Boer, and J. W. Geus, “The reduction and oxidation behaviour of manganese oxides,” Catalysis Today, vol. 47, no. 1–4, pp. 161–167, 1999.
View at: Google Scholar
Y. C. Zhang, T. Qiao, and X. Ya Hu, “Preparation of Mn₃O₄ nanocrystallites by low-temperature solvothermal treatment of γ-MnOOH nanowires,” Journal of Solid State Chemistry, vol. 177, no. 11, pp. 4093–4097, 2004.
View at: Publisher Site | Google Scholar
W. Zhang, Z. Yang, Y. Liu, S. Tang, X. Han, and M. Chen, “Controlled synthesis of Mn₃O₄ nanocrystallites and MnOOH nanorods by a solvothermal method,” Journal of Crystal Growth, vol. 263, no. 1-4, pp. 394–399, 2004.
View at: Publisher Site | Google Scholar
Y. Q. Chang, D. P. Yu, Y. Long, J. Xu, X. H. Luo, and R. C. Ye, “Large-scale fabrication of single-crystalline Mn₃O₄ nanowires via vapor phase growth,” Journal of Crystal Growth, vol. 279, no. 1-2, pp. 88–92, 2005.
View at: Publisher Site | Google Scholar
J. Du, Y. Gao, L. Chai, G. Zou, Y. Li, and Y. Qian, “Hausmannite Mn₃O₄ nanorods: synthesis, characterization and magnetic properties,” Nanotechnology, vol. 17, no. 19, article no. 024, pp. 4923–4928, 2006.
View at: Publisher Site | Google Scholar
M. Salavati-Niasari, F. Davar, and M. Mazaheri, “Synthesis of Mn₃O₄ nanoparticles by thermal decomposition of a [bis(salicylidiminato)manganese(II)] complex,” Polyhedron, vol. 27, no. 17, pp. 3467–3471, 2008.
View at: Publisher Site | Google Scholar
I. K. Gopalakrishnan, N. Bagkar, R. Ganguly, and S. K. Kulshreshtha, “Synthesis of superparamagnetic Mn₃O₄ nanocrystallites by ultrasonic irradiation,” Journal of Crystal Growth, vol. 280, no. 3-4, pp. 436–441, 2005.
View at: Publisher Site | Google Scholar
Y. Hu, J. Chen, X. Xue, and T. Li, “Synthesis of monodispersed single-crystal compass-shaped Mn₃O₄ via gamma-ray irradiation,” Materials Letters, vol. 60, no. 3, pp. 383–385, 2006.
View at: Publisher Site | Google Scholar
S. K. Apte, S. D. Naik, R. S. Sonawane et al., “Nanosize Mn₃O₄ (Hausmannite) by microwave irradiation method,” Materials Research Bulletin, vol. 41, no. 3, pp. 647–654, 2006.
View at: Publisher Site | Google Scholar
Z. W. Chen, J. K. L. Lai, and C. H. Shek, “Nucleation site and mechanism leading to growth of bulk-quantity Mn₃O₄ nanorods,” Applied Physics Letters, vol. 86, no. 18, Article ID 181911, pp. 1–3, 2005.
View at: Publisher Site | Google Scholar
A. Vázquez-Olmos, R. Redón, G. Rodríguez-Gattorno et al., “One-step synthesis of Mn₃O₄ nanoparticles: structural and magnetic study,” Journal of Colloid and Interface Science, vol. 291, no. 1, pp. 175–180, 2005.
View at: Publisher Site | Google Scholar
Z. H. Wang, D. Y. Geng, Y. J. Zhang, and Z. D. Zhang, “Morphology, structure and magnetic properties of single-crystal Mn₃O₄ nanorods,” Journal of Crystal Growth, vol. 310, no. 18, pp. 4148–4151, 2008.
View at: Publisher Site | Google Scholar
C. Du, J. Yun, R. K. Dumas et al., “Three-dimensionally intercrossing Mn₃O₄ nanowires,” Acta Materialia, vol. 56, no. 14, pp. 3516–3522, 2008.
View at: Publisher Site | Google Scholar
M. Anilkumar and V. Ravi, “Synthesis of nanocrystalline Mn₃O₄ at $100^{\circ} C$ ,” Materials Research Bulletin, vol. 40, no. 4, pp. 605–609, 2005.
View at: Publisher Site | Google Scholar
E. Veena Gopalan, K. A. Malini, S. Saravanan, D. Sakthi Kumar, Y. Yoshida, and M. R. Anantharaman, “Evidence for polaron conduction in nanostructured manganese ferrite,” Journal of Physics D, vol. 41, no. 18, Article ID 185005, 2008.
View at: Publisher Site | Google Scholar
S. D. Shenoy, P. A. Joy, and M. R. Anantharaman, “Effect of mechanical milling on the structural, magnetic and dielectric properties of coprecipitated ultrafine zinc ferrite,” Journal of Magnetism and Magnetic Materials, vol. 269, no. 2, pp. 217–226, 2004.
View at: Publisher Site | Google Scholar
M. A. Subramanian, D. Li, N. Duan, B. A. Reisner, and A. W. Sleight, “High dielectric constant in ACu₃Ti₄O₁₂ and ACu₃Ti₃FeO₁₂ phases,” Journal of Solid State Chemistry, vol. 151, no. 2, pp. 323–325, 2000.
View at: Publisher Site | Google Scholar
A. P. Ramirez, M. A. Subramanian, M. Gardel et al., “Giant dielectric constant response in a copper-titanate,” Solid State Communications, vol. 115, no. 5, pp. 217–220, 2000.
View at: Publisher Site | Google Scholar
P. Jha, S. Rai, K. V. Ramanujachary, S. E. Lofland, and A. K. Ganguli, “(La_0.4Ba_0.4Ca_0.2)(Mn_0.4Ti _0.6)O₃: a new titano-manganate with a high dielectric constant and antiferromagnetic interactions,” Journal of Solid State Chemistry, vol. 177, no. 8, pp. 2881–2888, 2004.
View at: Publisher Site | Google Scholar
B. V. Prasad, G. Narsinga Rao, J. W. Chen, and D. Suresh Babu, “Abnormal high dielectric constant in SmFeO₃ semiconductor ceramics,” Materials Research Bulletin, vol. 46, no. 10, pp. 1670–1673, 2011.
View at: Publisher Site | Google Scholar
H. Dhaouadi, A. Madani, and F. Touati, “Synthesis and spectroscopic investigations of Mn₃O₄ nanoparticles,” Materials Letters, vol. 64, no. 21, pp. 2395–2398, 2010.
View at: Publisher Site | Google Scholar
D. Yan, S. Cheng, R. F. Zhuo et al., “Nanoparticles and 3D sponge-like porous networks of manganese oxides and their microwave absorption properties,” Nanotechnology, vol. 20, no. 10, Article ID 105706, 2009.
View at: Publisher Site | Google Scholar
K. Usha and C. K. Mahadevan, “Structure, morphology and electrical properties of Mn₃O₄ nanocrystals,” Archives of Physics Research, vol. 2, p. 75, 2011.
View at: Google Scholar
E. Karaoğlu, H. Deligöz, H. Sözeri, A. Baykal, and M. S. Toprak, “Hydrothermal Synthesis and Characterization of PEG-Mn₃O₄ Nanocomposite,” Nano-Micro Letters, vol. 3, p. 25, 2011.
View at: Google Scholar
C. Rodriguez, “Recent advances in magnetic structure determination by neutron powder diffraction,” Physica B, vol. 192, no. 1-2, pp. 55–69, 1993.
View at: Google Scholar
H. M. Rietveld, “Line profiles of neutron powder-diffraction peaks for structure refinement,” Acta Crystallographica, vol. 22, p. 151, 1967.
View at: Google Scholar
H. P. Klug and L. E. Alexander, X-ray Diffraction Procedures for Polycrystalline and Amorphous Materials, chapter 9, Wiley, New York, NY, USA, 1st edition, 1954.
M. Ishii, M. Nakahira, and T. Yamanaka, “Infrared absorption spectra and cation distributions in (Mn, Fe)₃O₄,” Solid State Communications, vol. 11, no. 1, pp. 209–212, 1972.
View at: Google Scholar
W. Z. Wang, C. K. Xu, G. H. Wang, Y. K. Liu, and C. L. Zheng, “Preparation of smooth single-crystal Mn₃O₄ nanowires,” Advanced Materials, vol. 14, no. 11, pp. 837–840, 2002.
View at: Publisher Site | Google Scholar
N. Gupta, A. Verma, S. C. Kashyap, and D. C. Dube, “Microstructural, dielectric and magnetic behavior of spin-deposited nanocrystalline nickel-zinc ferrite thin films for microwave applications,” Journal of Magnetism and Magnetic Materials, vol. 308, no. 1, pp. 137–142, 2007.
View at: Publisher Site | Google Scholar
S. Lanfredi, P. S. Saia, R. Lebullenger, and A. C. Hernandes, “Electric conductivity and relaxation in fluoride, fluorophosphate and phosphate glasses: analysis by impedance spectroscopy,” Solid State Ionics, vol. 146, no. 3-4, pp. 329–339, 2002.
View at: Publisher Site | Google Scholar
Z. M. Sui, X. Chen, L. Y. Wang et al., “Capping effect of CTAB on positively charged Ag nanoparticles,” Physica E, vol. 33, no. 2, pp. 308–314, 2006.
View at: Publisher Site | Google Scholar
L. Francis, A. Balakrishnan, K. P. Sanosh, and E. Marsano, “Hydroxy propyl cellulose capped silver nanoparticles produced by simple dialysis process,” Materials Research Bulletin, vol. 45, no. 8, pp. 989–992, 2010.
View at: Publisher Site | Google Scholar
P. Tailhades, B. Gillot, and A. Rousset, “Mixed-valence defect ferrites: a new family of fine powders and thin films of spinel ferrites,” Journal De Physique. IV, vol. 2, no. 1, p. 249, 1997.
View at: Google Scholar
T. Gao, P. Norby, F. Krumeich, H. Okamoto, R. Nesper, and H. Fjellvåg, “Synthesis and properties of layered-structured Mn₅O₈ nanorods,” Journal of Physical Chemistry C, vol. 114, no. 2, pp. 922–928, 2010.
View at: Publisher Site | Google Scholar
V. Berbenni and A. Marini, “Oxidation behaviour of mechanically activated Mn₃O₄ by TGA/DSC/XRPD,” Materials Research Bulletin, vol. 38, no. 14, pp. 1859–1866, 2003.
View at: Publisher Site | Google Scholar
H. R. Oswald and M. J. Wanpetich, “Die Kristallstrukturen von Mn₅O₈ und Cd₂Mn₃O₈,” Helvetica Chimica Acta, vol. 50, p. 2023, 1967.
View at: Google Scholar
S. Fritsch, J. Sarrias, A. Rousset, and G. U. Kulkarni, “Low-temperature oxidation of Mn₃O₄ hausmannite,” Materials Research Bulletin, vol. 33, no. 8, pp. 1185–1194, 1998.
View at: Google Scholar
J. A. Lee, C. E. Newnham, F. S. Stone, and F. L. Tye, “Thermal decomposition of managanese oxyhydroxide,” Journal of Solid State Chemistry, vol. 31, no. 1, pp. 81–93, 1980.
View at: Google Scholar
J. H. Rask and P. R. Buseck, “Topotactic relations among pyrolusite, manganite, and Mn₅O₈: a high-resolution transmission electron microscopy investigation,” American Mineralogist, vol. 71, no. 5-6, pp. 805–814, 1986.
View at: Google Scholar
C. B. Azzoni, M. C. Mozzati, P. Galinetto et al., “Thermal stability and structural transition of metastable Mn₅O₈: in situ micro-Raman study,” Solid State Communications, vol. 112, no. 7, pp. 375–378, 1999.
View at: Publisher Site | Google Scholar
E. G. Larson, R. J. Arnott, and D. G. Wickham, “Preparation, semiconduction and low-temperature magnetization of the system Ni_1-xMn_2+xO₄,” Journal of Physics and Chemistry of Solids, vol. 23, no. 12, pp. 1771–1781, 1962.
View at: Google Scholar
A. M. M. Farea, S. Kumar, K. M. Batoo, A. Yousef, C. G. Lee, and Alimuddin, “Structure and electrical properties of Co_0.5Cd_x ${Fe}_{2.5 - x}$ O₄ ferrites,” Journal of Alloys and Compounds, vol. 464, no. 1-2, pp. 361–369, 2008.
View at: Publisher Site | Google Scholar
A. Kumar, B. P. Singh, R. N. P. Choudhary, and A. K. Thakur, “Characterization of electrical properties of Pb-modified BaSnO₃ using impedance spectroscopy,” Materials Chemistry and Physics, vol. 99, no. 1, pp. 150–159, 2006.
View at: Publisher Site | Google Scholar
K. W. Wagner, “Electricity and magnetism,” Annals of Physics, vol. 40, p. 817, 1913.
View at: Google Scholar
Y. Köseoǧlu, M. Bay, M. Tan et al., “Magnetic and dielectric properties of Mn_0.2Ni_0.8Fe₂O₄ nanoparticles synthesized by PEG-assisted hydrothermal method,” Journal of Nanoparticle Research, vol. 13, no. 5, pp. 2235–2244, 2011.
View at: Publisher Site | Google Scholar
M. Pastor, S. Goenka, S. Maiti, K. Biswas, and I. Manna, “Phase evolution, dielectric and impedance spectroscopic study of SrNb₂O₆ columbite phase,” Ceramics International, vol. 36, no. 3, pp. 1041–1045, 2010.
View at: Publisher Site | Google Scholar
T. Ramana, K. Akhilesh, B. Chandrahas, and T. P. Sinha, “Charge transport and dielectric response in ZnO nanotubes,” Current Applied Physics, vol. 10, p. 676, 2010.
View at: Google Scholar
S. F. Mansour and M. A. Elkestawy, “A comparative study of electric properties of nano-structured and bulk Mn-Mg spinel ferrite,” Ceramics International, vol. 37, no. 4, pp. 1175–1180, 2011.
View at: Publisher Site | Google Scholar
L. E. Cross, “The contribution of structural disorder to diffuse phase transitions in ferroelectrics,” Ferroelectrics, vol. 76, p. 241, 1987.
View at: Google Scholar
R. Mani, S. N. Achary, K. R. Chakraborty et al., “Dielectric properties of some MM0₄ and MTiM0O₆ (M0 $1 / 4$ Cr, Fe,Ga; M0 $1 / 4$ Nb, Ta,Sb) rutile-type oxides,” Journal of Solid State Chemistry, vol. 183, no. 6, pp. 1380–1387, 2010.
View at: Publisher Site | Google Scholar
J. C. Maxwell, Electricity and Magnetism, Oxford University Press, New York, NY, USA, 1973.
Z. Durmus, A. Baykal, H. Kavas, and H. Sozeri, “Preparation and characterization of polyaniline (PANI)-Mn₃O₄ nanocomposite,” Physica B, vol. 406, p. 1114, 2011.
View at: Google Scholar

Copyright

Copyright © 2012 Hassouna Dhaouadi et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

8023

Downloads

11613

Citations

International Scholarly Research Notices

Mn3O4 Nanoparticles: Synthesis, Characterization, and Dielectric Properties

Abstract

1. Introduction

2. Experimental Procedure

2.1. Sample Preparation

2.2. Characterisation Techniques

3. Results and Discussion

3.1. Crystal Structure, Size, and Morphology

3.2. IR Absorption Spectroscopy

3.3. Thermal Analyses

3.4. Conductivity Study

3.5. Dielectric Analysis

4. Conclusion

References

Copyright

Nanoparticles: Synthesis, Characterization, and Dielectric Properties