A Green Approach to Synthesize Silver Nanoparticles in Starch-co-Poly(acrylamide) Hydrogels by <i>Tridax procumbens</i> Leaf Extract and Their Antibacterial Activity

Shaik, Siraj; Kummara, Madhusudana Rao; Poluru, Sudhakar; Allu, Chandrababu; Gooty, Jaffer Mohiddin; Kashayi, Chowdoji Rao; Subha, Marata Chinna Subbarao

doi:https://doi.org/10.1155/2013/539636

International Journal of Carbohydrate Chemistry

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2013 | Article ID 539636 | https://doi.org/10.1155/2013/539636

A Green Approach to Synthesize Silver Nanoparticles in Starch-co-Poly(acrylamide) Hydrogels by Tridax procumbens Leaf Extract and Their Antibacterial Activity

Siraj Shaik,¹Madhusudana Rao Kummara,²Sudhakar Poluru,¹Chandrababu Allu,¹Jaffer Mohiddin Gooty,³Chowdoji Rao Kashayi,⁴and Marata Chinna Subbarao Subha¹

Academic Editor: Roland J. Pieters

Received31 Aug 2013

Accepted13 Nov 2013

Published24 Dec 2013

Abstract

A series of starch-co-poly(acrylamide) (starch-co-PAAm) hydrogels were synthesized by employing free radical redox polymerization. A novel green approach, Tridax procumbens (TD) leaf extract, was used for reduction of silver ions (Ag⁺) into silver nanoparticles in the starch-co-PAAm hydrogel network. The formation of silver nanoparticles was confirmed by UV-visible spectroscopy (UV-Vis), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (X-RD) studies. 22% of weight loss difference between hydrogel and silver nanocomposite hydrogel (SNCH) clearly indicates the formation of silver nanoparticles by TGA. TEM images indicate the successful incorporation of silver nanoparticles ranging from 5 to 10 nm in size and spherical in shape with a narrow size distribution. These developed SNCHs were used to study the antibacterial activity by inhibition zone method against gram-positive and gram-negative bacteria such as Bacillus and Escherichia coli. The results indicated that these SNCHs can be used potentially for biomedical applications.

1. Introduction

Hydrogels have three-dimensional polymeric networks that are fabricated from polymers stabilized through physical or chemical crosslinking. They absorb large quantities of water without losing their structural integrity [1]. Since they mimic body tissues and respond to external stimuli, they are made important and promising forms of biomaterials for various applications including tissue engineering, controlled drug release devices, biosensors, and mechanical actuators [2–4]. Due to the presence of water solubilizing groups, such as –OH, –COOH, –CONH₂, –CONH–, and –SO₃H, these hydrogels show higher hydrophilicity. The three-dimensional network of hydrogel provides relative stability to its structure. Their swollen state results from a balance between the dispersing forces acting on hydrated chains and cohesive forces that do not prevent the penetration of water through the network [5]. Based on these properties the hydrogels have been used recently as templates for production of metallic nanoparticles. Hence the design and development of metal nanoparticles dispersed in polymer matrix have attracted potential applications in various fields like electrical, optical, or mechanical properties [6, 7] making them valuable for applications in areas like optics [8], photo imaging and patterning [9], electronic devices [10], sensors and biosensors [11–13], catalysis [14, 15], and antibacterial and antimicrobial coatings [16]. Silver nanoparticles (Ag NPs) have attracted considerable interest in biological studies because of their ease of preparation, good biocompatibility, and relatively large surface area [17, 18]. Ag NPs have many important applications in biomedical fields, sensors, and filters [19]. Additionally, silver is a potential antibacterial agent [20] and is thus used as a sterilizer for removing bacteria from drinking water [21, 22]. For economic and efficient use of silver, silver nanoparticle composites have been developed and tested for antimicrobial activity.

Starch is one of the natural, renewable, and biodegradable polymers produced by many plants as a source of stored energy. Starch consists of two types of molecules: amylose (normally 20–30%) and amylopectin (normally 70–80%). The relative proportion of amylose to amylopectin depends on the source of starch. It is versatile and cheap and has many uses as thickener, water binder, emulsion stabilizer, and gelling agent [23]. Starch granules are insoluble in cold water but imbibe water reversibly and swell slightly [24]. Maleic acid (MA) is a nontoxic and biodegradable hydrophilic substance which is used as a type of food additive in processing industry. The modification of starch with MA increases its hydrophilicity by converting it into ester form by the reaction between starch and MA to form starch macromonomer [25]. The chemical modification of starch with MA and tartaric acid improves its properties without sacrificing its biodegradability and biocompatibility [25–27]. Several reports are present on acrylamide (AAm) hydrogels that were developed because of their hydrophilic and inert nature that makes them suitable for applications in medicine and pharmacy [28, 29]. Polyacrylamide has been used in contact lenses for a long time, and it has well been evaluated as a sustained-release wound-dressing material [30].

In continuation of our work [31] on usage of polymers in biomedical applications, the present research paper explores a simple and facile method to synthesize starch-co-poly(acrylamide) (starch-co-PAAm) hydrogels and silver nanocomposite hydrogels (SNCHs) by using a green process in which the Ag⁺ ions are successfully reduced by Tridax procumbens (TD) leaf extract. Starch, MA, and AAm were chosen on the basis of their significant characteristics in biomedical fields. The most popular way used for the direct synthesis of metal ions into nanoparticles is through chemical reduction method by using several reagents such as sodium borohydride, sodium hypophosphite, and sodium citrate. Several reports are presented for the development of Ag NPs by using such reducing agents [32, 33]. But these reducing agents may have environmental problems due to their toxicity, so a considerable interest to use nontoxic materials for reduction of Ag NPs is growing rapidly these days. In order to avoid such type of toxic reagents, recently plant extracts have been used for production of Ag NPs due to their cost-effective nature and also ambient conditions for reduction [34–37]. Therefore, the development of metal nanoparticles based on natural extracts is considered the most appropriate method. Recently Tridax procumbens (TD) leaf extract was used as reducing agent for preparation of Ag NPs by direct synthesis. TD contains several flavonoids, alkyl esters, terpenes, sterols, fatty acids, and polysaccharides. Due to the presence of these constituents, TD has several potential therapeutic activities like antiviral, antioxidant, and antibiotic efficacies; wound-healing activity; insecticidal and anti-inflammatory activity [38]. Now we have used this extract for production of Ag NPs in starch-co-PAAm hydrogel networks due to its natural reduction property and high biological activity. The developed SNCHs may be biodegradable and nontoxic and were potential materials to be used for biomedical applications.

2. Experimental

2.1. Materials

AR grade soluble starch (potato), silver nitrate (AgNO₃), potassium persulfate (KPS), maleic acid (MA), and sodium hydroxide (NaOH) were purchased from SD Fine Chemicals, Mumbai, India. Acrylamide (AAm), N,N¹-methylenebisacrylamide (MBA), and N,N,N¹,N¹¹-tetramethylethylenediamine (TEMED) were purchased from Aldrich Chemical Company Inc. (Milwaukee, WI, USA). All chemicals were used without further purification. Double-distilled (DD) water is used throughout the experiment.

2.2. Preparation of Tridax procumbens (TD) Leaf Extract

Leaf extracts were prepared by a green process technique, using the standard procedure described by Prasad et al. [39]. Tridax procumbens leaves were collected from Tridax procumbens plants at our university campus in Sri Krishnadevaraya University (Anantapur, Andhra Pradesh, India), thoroughly washed with DD water to remove the dust particles, and then dried in sun to remove the residual moisture. From this 20 g leaves were chopped finely and boiled in a 250 mL glass beaker along with 200 mL of sterile DD water for 10 min in order to extract the contents of the leaves. After boiling the colour, the aqueous solution changed from watery to yellow colour. The aqueous extract was separated by filtration with 2.5 μm Whatman filter paper (Sigma-Aldrich, USA) and then stored at room temperature.

2.3. Synthesis of Starch-co-PAAm Hydrogels and Their Silver Nanocomposite Hydrogels (SNCHs)

Gelatinized starch solution was prepared by mixing a quantitative amount of starch powder in 10.0 mL of DD water and 1.0 mL of 0.5 M sodium hydroxide (NaOH) solution, and the mixture was heated in a water bath at 90°C for 10 min with continuous magnetic stirring. A predetermined amount of MA was then added to the gelatinized starch solution and the resulting mixture was further heated in a water bath at 80°C for 4 h [25]. Subsequently, a quantitative amount of acrylamide was added and stirred for half an hour at 50°C, after that cross-linker (MBA) and initiator (KPS) were added according to the formulations mentioned in the Table 1. Finally, an aqueous solution of TEMED was added to the solution and the same temperature was maintained for another 10 min. After completion of free radical polymerization, the synthesized copolymeric hydrogel was taken out and immersed in double-distilled water at room temperature for 24 h to remove the excess of unreacted monomers and reagents present in the hydrogel network. During this period, DD water was refreshed for every 12 h in order to leach out the residue effectively. Finally, the hydrogel was dried at ambient temperature for 48 h. Similarly, other hydrogels were prepared by the above procedure according to their feed compositions as per Table 1.

Accurately weighed dried starch-co-PAAm hydrogels were equilibrated with DD water for 48 h and immediately transferred to a beaker containing 100 mL of 5 mM AgNO₃ aqueous solution and then allowed to equilibrate for 24 h. During this process, most of the silver ions (Ag⁺) were exchanged from solution into free network spaces of copolymeric hydrogel. The hydrogel with absorbed Ag⁺ ions was finally transferred to a beaker containing 50 mL Tridax procumbens leaf extract aqueous solution and kept for 24 h for reduction of Ag⁺ ions into silver nanoparticles (Ag⁰). After reduction of Ag⁺ ions, the hydrogel was turned into brown colour, which confirms the formation of Ag⁰ nanoparticles in hydrogel matrix [31, 33]. The above procedure was adopted for all other remaining hydrogels to convert them into SNCHs. The formation of hydrogels and silver nanocomposite hydrogels is shown in Scheme 1.

2.4. Swelling Studies

Fully dried copolymeric hydrogels were weighed and equilibrated in DD water at 37°C for three days. The equilibrium swelling capacity () of the hydrogel was calculated by the following equation: where and are the weight of swollen hydrogel and weight of the dry hydrogel, respectively. The data provided is an average value of 3 individual sample readings.

2.5. Characterization Methods

Fourier transform infrared (FT-IR) spectra of hydrogel and SNCH are recorded on Perkin Elmer (model impact 410, Wisconsin, MI, USA) spectrophotometer. The samples were crushed with potassium bromide (KBr) to make pellets under hydraulic pressure of 600 kg and scanned between 4000 and 400 cm⁻¹. UV-visible (UV-Vis) spectra of starch-co-PAAm hydrogel and SNCHs were recorded using UV-Vis spectrophotometer (Perkin Elmer). For this, the grinded samples (10 mg/mL) were stored for 10 days to leach out Ag NPs into water (media) and then the measurements were carried out. X-ray diffraction (X-RD) measurements were carried out using Rikagu diffractometer (Cu radiation, nm) running at 40 kV and 40 mA. TGA curves of hydrogel and SNCH are recorded using TA instrument’s sequential thermal analyser (Model-SDT Q600, USA). The samples were heated from room temperature to 700°C at a heating rate of 10°C per min. Scanning electron microscopy (SEM) images were taken with a high resolution SEM instrument (MIRA LMH, H.S.) at an accelerating voltage of 15 kV. SEM specimens were prepared by the dry hydrogel and SNCHs, coated with a thin layer of palladium and gold alloy, and then studied for morphological variations. The size and shape of Ag⁰ nanoparticles were investigated by transmission electron microscopy (TEM) (FEI Tecnai G² S-Twin 200 kV) at an acceleration voltage of 15 kV. For TEM measurements, the samples were prepared by dropping 5–10 μL of finely grinded SNCH dispersion on a carbon-coated copper grid and dried at room temperature after removing excess moisture using filter paper.

2.6. Antibacterial Activity of Silver Nanocomposite Hydrogels

Antimicrobial activity studies of starch-co-PAAm hydrogel and its SNCHs were carried out by disc diffusion method [40, 41] on bacterial strains, namely, Escherichia coli and Bacillus. Nutrient agar medium was prepared by mixing peptone (5.0 g), beef extract (3.0 g), and sodium chloride (NaCl) (5.0 g) in 1,000 mL distilled water and the pH was adjusted to 7.0. Finally, agar (15.0 g) was added to this solution and this medium was sterilized in an autoclave at a pressure of 15 lbs for 30 min at 121°C. This medium was transferred into sterilized Petri dishes in a laminar air flow chamber. After solidification of the media, Escherichia coli and Bacillus culture (50 μL) was spread on the solid surface of the media. Paper discs (6 mm diameter) were soaked inside the test compounds (20 mg/20 mL) overnight before loading them on culture plates. The plates were incubated at 37°C for 24 h. The inhibition zone appeared around the disc was measured and recorded as the antibacterial effect of Ag NPs.

3. Results and Discussion

3.1. Swelling Studies

Water uptake by hydrogels was monitored for an extended period of time till equilibrium was achieved. Swelling characteristics of starch-co-PAAm hydrogels and SNCH systems at 37°C were determined using (1) and are plotted as a function of composition in Figure 1. The hydrogels swelled rapidly in water and attained equilibrium within 12 h. Figure 1 shows the influence of various amounts of starch, MA, acrylamide, and MBA on swelling characteristics of the copolymeric hydrogels and their SNCHs. The order of swelling capacity values of starch-co-PAAm hydrogels and SNCHs is copolymeric SNCHs > pure hydrogels. This pattern of swelling is reasonable because once the Ag⁺ ions loaded hydrogels were treated with TD leaf extract, the reduction of Ag⁺ ions into Ag⁰ nanoparticles takes place which may enhance the overall porosity of the gel and hence promote higher water molecules uptake capacity. The other reason can be that the particles have different sizes and different surface charges in the gel networks that cause absolute expansion of the network.

(a)

(b)

(c)

(d)

It is observed from Figures 1(a), 1(b), and 1(c) as the amount of starch, MA, and AAm increases, the swelling of hydrogels increased. This is due to the increase in hydrophilic groups (–OH, –COOH, –CONH₂) and increase in hydrodynamic free volume to accommodate more of the solvent molecules. As the amount of MBA increased (Figure 1(d)) the swelling has been decreased due to the high crosslinking density, which tightens the polymeric chains thereby making the hydrogels rigid.

3.2. FT-IR Spectral Studies

In Figure 2, the IR spectrum of starch-co-PAAm hydrogel shows the characteristic absorption peaks at 1118 cm⁻¹ and the absorption bands in the range of 2900–3400 cm⁻¹ which are attributed to –C–O and –OH stretching vibrations of starch, respectively. The characteristic absorption peak at 1680 cm⁻¹ results from –C=O stretching vibration of the –CONH₂ group, and a broad absorption band at 3219 cm⁻¹ is related to the –NH asymmetric and –OH symmetric stretching vibrational group; band at 2812 cm⁻¹ is attributed to stretching vibrations of –CH₃ units. The absorption band at 1710 cm⁻¹ is due to asymmetrical stretching for –COOH group of maleic acid. The substitution of MA was also confirmed by the absorption band observed at 1230 cm⁻¹ which indicates the –C–O–O-stretching vibrations of ester. These peaks have shifted to 1110 cm⁻¹, 1214 cm⁻¹, 1669 cm⁻¹, and 2804 cm⁻¹, and 3202 cm⁻¹ in SNCH indicates that Ag⁰ nanoparticles are successfully incorporated in SNCH matrices.

3.3. UV-Visible Spectroscopy

The formation of Ag⁰ nanoparticles in the copolymeric hydrogel networks can be expected in our current strategy because the Ag⁺-loaded starch-co-PAAm hydrogel was readily reduced by TD leaf extract, which immediately turned into brown colour. This change in colour shows that the Ag⁰ nanoparticles are entrapped inside the networks through strong localization and stabilization established by the polymer matrix. The existence of Ag⁰ nanoparticles in the gel networks was estimated by UV-visible spectroscopy analysis. Figure 3 illustrates the absorption peaks of SNCHs in 325–500 nm ranges that are assigned to Ag NPs which arose from the surface plasmon resonance (SPR). A significant improvement in the absorption peak at 420 nm was observed for Ag⁰-loaded hydrogels due to the surface plasmon resonance band [42]. The UV-visible absorption band is not symmetrical for all the formulations, because the formation of nanoparticles and their size depends on the network structure of hydrogels and their functionality. This absorption peak was not observed in the case of starch-co-PAAm hydrogel. No additional absorption peaks around 325–500 nm indicates that SNCH network is protecting the nanoparticles from the aggregation or cluster formation. This analysis confirms the formation of highly dispersed Ag⁰ nanoparticles in the copolymeric hydrogels.

3.4. X-Ray Diffraction

The crystallinity of the hydrogel and SNCH was confirmed by the analysis of X-ray diffraction (X-RD) pattern (Figure 4). The dry powders of hydrogel and SNCH were used for X-RD analysis. In the diffractogram, four diffraction peaks were obtained at an angle, , 49.25, 64.10, and 77.87 which could be attributed to the Brags reflections of (111), (200), (220), and (311) planes of face centred cubic (FCC) structure of Ag NPs. A broad diffraction peak in both samples can be seen at 20° due to the amorphous nature of starch-co-PAAm hydrogel and SNCH. The (200), (220), and (311) peaks were less intense compared to (111) peak. So, in this case, we might conclude that the nanoassemblies were mainly composed of (111) lattice planes. Similar type of observations was found previously in reported work [31, 33].

3.5. SEM Studies

The morphology of starch-co-PAAm hydrogel and SNCH was investigated with SEM. Figure 5 shows the SEM micrographs of the starch-co-PAAm and SNCHs. Figure 5(a) shows a clear surface feature for the pure hydrogel, whereas Ag NPs-loaded starch-co-PAAm hydrogel (Figure 5(b)) exhibits smaller nanoparticles distributed throughout the hydrogel networks. It is worth mentioning that no individual silver particles were observed outside the SNCH, indicating a strong interaction between the polymer matrix and the silver particles.

(a)

(b)

3.6. TEM Studies

Shape and size distribution of the synthesized Ag NPs were characterized by transmission electron microscopic (TEM) analysis. Figures 6(a) and 6(b) are the low magnification images and Figure 6(c) is the high magnification image obtained by transmission electron microscopy at an acceleration voltage of 15 kV. These images indicate that the particles are well defined, spherical in shape with a narrow size distribution, and highly dispersed with an average diameter of 7 nm in size (Figure 6(d)). Moreover, the electron diffraction pattern of Ag⁰ nanoparticles is clearly visible in Figure 6(e) as three diffraction rings and from that pattern it is evident that the nanoparticles are crystalline and have a face centered cubic (FCC) structure.

(a)

(b)

(c)

(d)

(e)

3.7. Thermogravimetrical Analysis

The starch-co-PAAm hydrogel and its SNCHs are characterized by thermogravimetrical analysis to determine the percentage of weight loss of pure hydrogel as well as Ag⁰ nanoparticles loaded hydrogel, as shown in Figure 7. The starch-co-PAAm hydrogel has followed two decomposition steps below 400°C and 82% weight loss occurred below 700°C. However, two decomposition states and only 60% weight loss were observed in the case of SNCH below 700°C. The difference in decomposition between the hydrogel and SNCH is found to be 22%, and it confirms the presence of Ag⁰ nanoparticles in the SNCH network. From these results it is concluded that SNCH showed a higher thermal stability when compared with the starch-co-PAAm hydrogel due to the undecomposed remaining weight of Ag⁰ nanoparticles present in the copolymeric networks.

3.8. Antibacterial Studies

The antimicrobial activity of different molar weight ratios of SNCHs was examined against gram-negative and gram-positive bacteria. All SNCHs proved effective against the tested microorganisms Escherichia coli and Bacillus, but growth inhibitory effects varied from one another as shown in Figures 8(a) and 8(b). The results indicate that starch-co-PAAm-3, starch-co-PAAm-4, starch-co-PAAm-5, starch-co-PAAm-8, and starch-co-PAAm-9 SNCHs exhibited greater reduction of Escherichia coli and Bacillus growth, while the pure hydrogels (c) were generally inefficient as shown in Table 2. The inhibition zone follows the order starch-co-PAAm-3 > starch-co-PAAm-5 > starch-co-PAAm-8 > starch-co-PAAm-4 > starch-co-PAAm-9. These results are expected due to the small sizes of Ag⁰ nanoparticles and the same order is expected for swelling ratio. Ag NPs adhered to the cell wall of bacteria and penetrated through the cell membrane; they kill microorganisms instantly by blocking their respiratory enzyme systems and having no negative effect on human cells.

(a)

(b)

4. Conclusions

In conclusion, we have demonstrated a facile and simple green methodology for preparation of starch-co-PAAm silver nanocomposite hydrogels by free radical polymerization and thereby reducing Ag⁺ into Ag⁰ nanoparticles using Tridax procumbens leaf extract. The main aim of this study was to develop a new antimicrobial/wound-dressing agent. These antimicrobial agents are nontoxic materials which can be used systemically as an alternative to conventional systemic antibiotic, antiviral, and antifungal therapies that do not incur the development of resistance by the target pathogens. The synthesis method adopted here is very simple and can be easily implemented for any kind of scientific as well as industrial application due to its cost-effective nature. A number of SNCHs were formulated with high dispersion rates of Ag⁰ nanoparticles throughout the hydrogel networks by varying the concentrations of carbohydrate polymer, monomers, and crosslinker. The synthesized nanocomposites are confirmed by using various spectral, thermal, and electron microscopy methods. These SNCHs having Ag⁰ nanoparticles concentrations as low as 1 mg/mL showed excellent antibacterial activity against gram-positive and gram-negative bactericide. This resulted into inhibition of bacterial cell growth and multiplication. So these nanocomposites could be used as successful antibacterial agents such as wound-dressing materials.

Acknowledgments

The authors thank University Grants Commission (UGC), New Delhi (India), for providing financial support to one of the authors (Siraj Shaik) under UGC-RFSMS (Letter no. F.7-290/2009 (BSR)/10-01/2009). The authors are thankful to Professor T. P. Radhakrishnan, School of Chemistry, University of Hyderabad, Hyderabad, Andhra Pradesh, for helping them in obtaining TEM images.

References

K. Y. Lee and D. J. Mooney, “Hydrogels for tissue engineering,” Chemical Reviews, vol. 101, no. 7, pp. 1869–1879, 2001.
View at: Publisher Site | Google Scholar
N. A. Peppas, P. Bures, W. Leobandung, and H. Ichikawa, “Hydrogels in pharmaceutical formulations,” European Journal of Pharmaceutics and Biopharmaceutics, vol. 50, no. 1, pp. 27–46, 2000.
View at: Publisher Site | Google Scholar
J. Kim, I. S. Kim, T. H. Cho et al., “Bone regeneration using hyaluronic acid-based hydrogel with bone morphogenic protein-2 and human mesenchymal stem cells,” Biomaterials, vol. 28, no. 10, pp. 1830–1837, 2007.
View at: Publisher Site | Google Scholar
N. A. Peppas, J. Z. Hilt, A. Khademhosseini, and R. Langer, “Hydrogels in biology and medicine: from molecular principles to bionanotechnology,” Advanced Materials, vol. 18, no. 11, pp. 1345–1360, 2006.
View at: Publisher Site | Google Scholar
H. F. Mark, N. M. Bikals, C. G. Overberger, and J. I. Kroschwitz, Encyclopedia of Polymer Science and Engineering, Wiley-Interscience, New York, NY, USA, 1986.
Y. Xia, P. Yang, Y. Sun et al., “One-dimensional nanostructures: synthesis, characterization, and applications,” Advanced Materials, vol. 15, no. 5, pp. 353–389, 2003.
View at: Publisher Site | Google Scholar
W. Caseri, “Nanocomposites of polymers and metals or semiconductors: historical background and optical properties,” Macromolecular Rapid Communications, vol. 21, no. 11, pp. 705–722, 2000.
View at: Google Scholar
M. José-Yacamán, R. Pérez, P. Santiago, M. Benaissa, K. Gonsalves, and G. Carlson, “Microscopic structure of gold particles in a metal polymer composite film,” Applied Physics Letters, vol. 69, no. 7, pp. 913–915, 1996.
View at: Google Scholar
F. Stellacci, C. A. Bauer, T. M. Friedrichsen et al., “Laser and electron-beam induced growth of nanoparticles for 2D and 3D metal patterning,” Advanced Materials, vol. 14, no. 3, pp. 194–198, 2002.
View at: Google Scholar
S. Pothukuchi, Y. Li, and C. P. Wong, “Development of a novel polymer-metal nanocomposite obtained through the route of in situ reduction for integral capacitor application,” Journal of Applied Polymer Science, vol. 93, no. 4, pp. 1531–1538, 2004.
View at: Publisher Site | Google Scholar
D. N. Muraviev, J. Macanás, M. J. Esplandiu, M. Farre, M. Muñoz, and S. Alegret, “Simple route for intermatrix synthesis of polymer stabilized core-shell metal nanoparticles for sensor applications,” Physica Status Solidi (A), vol. 204, no. 6, pp. 1686–1692, 2007.
View at: Publisher Site | Google Scholar
J. Macanás, M. Farre, M. Muñoz, S. Alegret, and D. N. Muraviev, “Preparation and characterization of polymer-stabilized metal nanoparticles for sensor applications,” Physica Status Solidi (A), vol. 203, no. 6, pp. 1194–1200, 2006.
View at: Publisher Site | Google Scholar
F. P. Zamborini, M. C. Leopold, J. F. Hicks, P. J. Kulesza, M. A. Malik, and R. W. Murray, “Electron hopping conductivity and vapor sensing properties of flexible network polymer films of metal nanoparticles,” Journal of the American Chemical Society, vol. 124, no. 30, pp. 8958–8964, 2002.
View at: Publisher Site | Google Scholar
D. N. Muraviev, J. Macanás, P. Ruiz, and M. Munoz, “Synthesis, stability and electrocatalytic activity of polymer-stabilized monometallic Pt and bimetallic Pt/Cu core-shell nanoparticles,” Physica Status Solidi (A), vol. 205, no. 6, pp. 1460–1464, 2008.
View at: Publisher Site | Google Scholar
T. Yao, C. Wang, J. Wu et al., “Preparation of raspberry-like polypyrrole composites with applications in catalysis,” Journal of Colloid and Interface Science, vol. 338, no. 2, pp. 573–577, 2009.
View at: Publisher Site | Google Scholar
K. Varaprasad, Y. Murali Mohan, S. Ravindra et al., “Hydrogel–silver nanoparticle composites: a new generation of antimicrobials,” Journal of Applied Polymer Science, vol. 115, no. 2, pp. 1199–1207, 2010.
View at: Publisher Site | Google Scholar
Y. Mo, I. Mörke, and P. Wachter, “Surface enhanced Raman scattering of pyridine on silver surfaces of different roughness,” Surface Science, vol. 133, no. 1, pp. L452–L458, 1983.
View at: Google Scholar
Y.-C. Chung, I.-H. Chen, and C.-J. Chen, “The surface modification of silver nanoparticles by phosphoryl disulfides for improved biocompatibility and intracellular uptake,” Biomaterials, vol. 29, no. 12, pp. 1807–1816, 2008.
View at: Publisher Site | Google Scholar
G. Cao, Nanostructures and Nanomaterials: Synthesis, Properties and Applications, Imperial College Press, London, UK, 2004.
N. Grier, Disinfection, Sterilization and Preservation, S. S. Block, Ed., Lea & Febiger, Philadelphia, Pa, USA, 3rd edition, 1983.
J. Kusnetsov, E. Iivanainen, N. Elomaa, O. Zacheus, and P. J. Martikainen, “Copper and silver ions more effective against Legionellae than against mycobacteria in a hospital warm water system,” Water Research, vol. 35, no. 17, pp. 4217–4225, 2001.
View at: Publisher Site | Google Scholar
J. Keleher, J. Bashant, N. Heldt, L. Johnson, and Y. Li, “Photo-catalytic preparation of silver-coated TiO₂ particles for antibacterial applications,” World Journal of Microbiology and Biotechnology, vol. 18, no. 2, pp. 133–139, 2002.
View at: Publisher Site | Google Scholar
J.-Y. Li and A.-I. Yeh, “Relationships between thermal, rheological characteristics and swelling power for various starches,” Journal of Food Engineering, vol. 50, no. 3, pp. 141–148, 2001.
View at: Publisher Site | Google Scholar
H. Mark and O. Kirk, Encyclopedia of Chemical Technology, John Willy & Sons, New York, NY, USA, 3rd edition, 1986.
S. C. Pang, S. F. Chin, S. H. Tay, and F. M. Tchong, “Starch–maleate–polyvinyl alcohol hydrogels with controllable swelling behaviors,” Carbohydrate Polymers, vol. 84, no. 1, pp. 424–429, 2011.
View at: Publisher Site | Google Scholar
A. Biswas, R. L. Shogren, G. Selling, J. Salch, J. L. Willett, and C. M. Buchanan, “Rapid and environmentally friendly preparation of starch esters,” Carbohydrate Polymers, vol. 74, no. 1, pp. 137–141, 2008.
View at: Publisher Site | Google Scholar
S. F. Chin, S. C. Pang, and L. S. Lim, “Synthesis and characterization of novel water soluble starch tartarate nanoparticles,” ISRN Materials Science, vol. 2012, Article ID 723686, 5 pages, 2012.
View at: Publisher Site | Google Scholar
B. Singh, N. Chauhan, S. Kumar, and R. Bala, “Psyllium and copolymers of 2-hydroxylethylmethacrylate and acrylamide-based novel devices for the use in colon specific antibiotic drug delivery,” International Journal of Pharmaceutics, vol. 352, no. 1-2, pp. 74–80, 2008.
View at: Publisher Site | Google Scholar
B. Singh and R. Bala, “Design of dietary polysaccharide and binary monomer mixture of acrylamide and 2-acrylamido-2-methylpropane sulphonic acid based antiviral drug delivery devices,” Chemical Engineering Research and Design, vol. 90, no. 3, pp. 346–358, 2012.
View at: Publisher Site | Google Scholar
J. Rosiak, K. Burozak, and W. Pȩkala, “Polyacrylamide hydrogels as sustained release drug delivery dressing materials,” Radiation Physics and Chemistry, vol. 22, no. 3–5, pp. 907–915, 1983.
View at: Google Scholar
A. C. Babu, M. N. Prabhakar, A. S. Babu, B. Mallikarjuna, M. C. S. Subha, and K. C. Rao, “Development and characterization of semi-IPN silver nanocomposite hydrogels for antibacterial applications,” International Journal of Carbohydrate Chemistry, vol. 2013, Article ID 243695, 8 pages, 2013.
View at: Publisher Site | Google Scholar
P. S. K. Murthy, Y. M. Mohan, K. Varaprasad, B. Sreedhar, and K. M. Raju, “First successful design of semi-IPN hydrogel–silver nanocomposites: a facile approach for antibacterial application,” Journal of Colloid and Interface Science, vol. 318, no. 2, pp. 217–224, 2008.
View at: Publisher Site | Google Scholar
V. R. Babu, C. Kim, S. Kim, C. Ahn, and Y.-I. Lee, “Development of semi-interpenetrating carbohydrate polymeric hydrogels embedded silver nanoparticles and its facile studies on E. coli,” Carbohydrate Polymers, vol. 81, no. 2, pp. 196–202, 2010.
View at: Publisher Site | Google Scholar
S. Ravindra, Y. M. Mohan, N. N. Reddy, and K. M. Raju, “Fabrication of antibacterial cotton fibres loaded with silver nanoparticles via ‘Green Approach’,” Colloids and Surfaces A, vol. 367, no. 1–3, pp. 31–40, 2010.
View at: Publisher Site | Google Scholar
S. Barua, R. Konwarh, S. S. Bhattacharya et al., “Non-hazardous anticancerous and antibacterial colloidal “green”silver nanoparticles,” Colloids and Surfaces B, vol. 105, pp. 37–42, 2013.
View at: Publisher Site | Google Scholar
C. Dipankar and S. Murugan, “The green synthesis, characterization and evaluation of the biological activities of silver nanoparticles synthesized from Iresine herbstii leaf aqueous extracts,” Colloids and Surfaces B, vol. 98, pp. 112–119, 2012.
View at: Publisher Site | Google Scholar
V. S. Kotakadi, Y. S. Rao, S. A. Gaddam, T. N. V. K. Prasad, A. V. Reddy, and D. V. R. S. Gopai, “Simple and rapid biosynthesis of stable silver nanoparticles using dried leaves of Catharanthus roseus. Linn. G. Donn and its antimicrobial activity,” Colloids and Surfaces B, vol. 105, pp. 194–198, 2013.
View at: Publisher Site | Google Scholar
L. Suseela, A. Sarsvathy, and P. Brindha, “Pharmacognostic studies on Tridax procumbens L. (Asteraceae),” Journal of Phytological Research, vol. 15, no. 2, pp. 141–147, 2002.
View at: Google Scholar
M. H. Prasad, C. Rameshz, N. Jayakumar, V. Ragunathan, and D. Kalpana, “Biosynthesis of bimetallic Ag/Cu₂O nanocomposites using Tridax procumbens leaf extract,” Advanced Science, Engineering and Medicine, vol. 4, no. 1, pp. 85–88, 2012.
View at: Publisher Site | Google Scholar
H. Acharya, J. Sung, H.-I. Shin, S.-Y. Park, B. G. Min, and C. Park, “Deposition of silver nanoparticles on single wall carbon nanotubes via a self assembled block copolymer micelles,” Reactive and Functional Polymers, vol. 69, no. 7, pp. 552–557, 2009.
View at: Publisher Site | Google Scholar
K. B. Holt and A. J. Bard, “Interaction of silver(I) ions with the respiratory chain of Escherichia coli: an electrochemical and scanning electrochemical microscopy study of the antimicrobial mechanism of micromolar Ag⁺,” Biochemistry, vol. 44, no. 39, pp. 13214–13223, 2005.
View at: Publisher Site | Google Scholar
C.-N. Lok, C.-M. Ho, R. Chen et al., “Proteomic analysis of the mode of antibacterial action of silver nanoparticles,” Journal of Proteome Research, vol. 5, no. 4, pp. 916–924, 2006.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2013 Siraj Shaik et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3859

Downloads

1671

Citations