A Comprehensive Study on Gamma-Ray Exposure Build-Up Factors and Fast Neutron Removal Cross Sections of Fly-Ash Bricks
Table 3
GP fitting parameters for FAB1 and FAB2.
| Energy (MeV) | | | | | |
| | FAB1 | 0.015 | 1.028 | 0.386 | 0.215 | 14.919 | −0.146 | 0.02 | 1.062 | 0.398 | 0.206 | 15.078 | −0.116 | 0.03 | 1.201 | 0.408 | 0.207 | 14.534 | −0.110 | 0.04 | 1.421 | 0.476 | 0.180 | 14.500 | −0.100 | 0.05 | 1.677 | 0.605 | 0.124 | 15.483 | −0.065 | 0.06 | 1.963 | 0.701 | 0.095 | 14.727 | −0.053 | 0.08 | 2.435 | 0.851 | 0.055 | 14.413 | −0.048 | 0.1 | 2.646 | 1.026 | 0.014 | 13.593 | −0.029 | 0.15 | 2.731 | 1.272 | −0.042 | 10.413 | −0.006 | 0.2 | 2.670 | 1.371 | −0.057 | 7.813 | −0.005 | 0.3 | 2.476 | 1.464 | −0.077 | 17.191 | 0.013 | 0.4 | 2.350 | 1.467 | −0.080 | 16.046 | 0.016 | 0.5 | 2.247 | 1.451 | −0.079 | 16.302 | 0.018 | 0.6 | 2.171 | 1.422 | −0.076 | 18.225 | 0.021 | 0.8 | 2.049 | 1.383 | −0.073 | 15.355 | 0.021 | 1 | 1.976 | 1.323 | −0.063 | 16.064 | 0.019 | 1.5 | 1.864 | 1.232 | −0.048 | 14.866 | 0.017 | 2 | 1.789 | 1.155 | −0.033 | 15.608 | 0.011 | 3 | 1.678 | 1.061 | −0.012 | 13.922 | −0.001 | 4 | 1.602 | 0.995 | 0.005 | 12.945 | −0.009 | 5 | 1.537 | 0.948 | 0.020 | 12.601 | −0.021 | 6 | 1.474 | 0.924 | 0.027 | 11.700 | −0.022 | 8 | 1.406 | 0.902 | 0.033 | 13.689 | −0.027 | 10 | 1.345 | 0.881 | 0.042 | 13.141 | −0.033 | 15 | 1.258 | 0.835 | 0.061 | 14.297 | −0.052 |
| | FAB2 | 0.015 | 1.027 | 0.376 | 0.228 | 14.103 | −0.155 | 0.02 | 1.058 | 0.408 | 0.197 | 15.983 | −0.113 | 0.03 | 1.190 | 0.402 | 0.212 | 14.267 | −0.113 | 0.04 | 1.397 | 0.466 | 0.185 | 14.389 | −0.104 | 0.05 | 1.646 | 0.583 | 0.133 | 15.174 | −0.071 | 0.06 | 1.890 | 0.700 | 0.093 | 15.276 | −0.052 | 0.08 | 2.374 | 0.827 | 0.061 | 14.429 | −0.051 | 0.1 | 2.586 | 1.001 | 0.016 | 13.739 | −0.032 | 0.15 | 2.692 | 1.248 | −0.037 | 10.823 | −0.009 | 0.2 | 2.647 | 1.356 | −0.055 | 8.168 | −0.006 | 0.3 | 2.462 | 1.454 | −0.076 | 17.822 | 0.013 | 0.4 | 2.342 | 1.458 | −0.078 | 16.424 | 0.015 | 0.5 | 2.239 | 1.445 | −0.078 | 16.305 | 0.017 | 0.6 | 2.162 | 1.420 | −0.076 | 17.592 | 0.020 | 0.8 | 2.044 | 1.380 | −0.072 | 15.458 | 0.021 | 1 | 1.970 | 1.323 | −0.063 | 16.408 | 0.019 | 1.5 | 1.862 | 1.232 | −0.048 | 15.186 | 0.017 | 2 | 1.788 | 1.155 | −0.033 | 15.865 | 0.011 | 3 | 1.677 | 1.062 | −0.012 | 14.771 | −0.001 | 4 | 1.601 | 0.995 | 0.005 | 12.967 | −0.009 | 5 | 1.537 | 0.946 | 0.021 | 11.908 | −0.021 | 6 | 1.477 | 0.927 | 0.026 | 11.786 | −0.021 | 8 | 1.405 | 0.902 | 0.034 | 13.732 | −0.028 | 10 | 1.344 | 0.882 | 0.042 | 13.128 | −0.033 | 15 | 1.257 | 0.838 | 0.060 | 14.282 | −0.052 |
|
|