A Numerical Formula for General Prediction of Interface Bonding between Alumina and Aluminum-Containing Alloys
Table 2
Values of oxide formation enthalpy and calculated adsorption energy of oxygen on various metals (M) and related values.
| | | kJ/mol | kJ/mol-M | kJ/mol-O | kJ/mol-O | Energy difference (kJ/mol) |
| Mg | MgO | 601.6 | 601.6 | 601.6 | 664.14 | 419.61 | Al | Al2O3 | 1675.7 | 837.85 | 558.5667 | 833.06 | 588.53 | Si | SiO2 | 910.7 | 910.7 | 455.35 | 885.15 | 640.62 | Ti | TiO2 | 944 | 944 | 472 | 908.96 | 664.43 | V | V2O5 | 1550.6 | 775.3 | 310.12 | 788.34 | 543.81 | Cr | Cr2O3 | 1139.7 | 569.85 | 379.9 | 641.44 | 396.91 | Mn | MnO2 | 520 | 520 | 260 | 605.80 | 361.27 | Fe | Fe2O3 | 824.2 | 412.1 | 274.7333 | 528.65 | 284.12 | CO |
CO3O4 | 891 | 297 | 222.75 | 446.36 | 201.83 | Ni | Ni2O3 | 489.5 | 244.75 | 163.1667 | 409.00 | 164.47 | Cu | CuO | 157.3 | 157.3 | 157.3 | 346.47 | 101.94 | Zn | ZnO | 350.5 | 350.5 | 350.5 | 484.61 | 240.08 | Ga | Ga2O3 | 1089.1 | 544.55 | 363.0333 | 623.35 | 378.82 | Ge | GeO2 | 580 | 580 | 290 | 648.70 | 404.17 | Zr | ZrO2 | 1094.3 | 1094.324 | 547.162 | 1016.44 | 771.91 | Nb | Nb2O5 | 1899.5 | 949.75 | 379.9 | 913.07 | 668.54 | Mo | MoO3 | 745.1 | 745.1 | 248.3667 | 766.75 | 522.22 | Ru | RuO4 | 239.3 | 239.3 | 59.825 | 405.10 | 160.57 | Rh | Rh2O3 | 343.0 | 171.5 | 114.3333 | 356.62 | 112.09 | Pd | PdO | 85.4 | 85.4 | 85.4 | 295.06 | 50.53 | Ag | Ag2O2 | 24.3 | 12.15 | 12.15 | 242.69 | −1.84 | In | In2O3 | 925.8 | 462.9 | 308.6 | 564.97 | 320.44 | Sn | SnO2 | 577.63 | 577.63 | 288.815 | 647.01 | 402.48 | La | La2O3 | 1793.7 | 896.85 | 597.9 | 875.25 | 630.72 | Hf | HfO2 | 1144.7 | 1144.7 | 572.35 | 1052.46 | 807.93 | Ta | Ta2O5 | 2046 | 1023 | 409.2 | 965.45 | 720.92 | W | WO3 | 842.9 | 842.9 | 280.9667 | 836.67 | 592.14 | Re | Re2O7 | 1240.1 | 620.05 | 177.1571 | 677.34 | 432.81 | Os | OsO4 | 391.248 | 391.248 | 97.812 | 513.74 | 269.21 | Ir | IrO2 | 274.1 | 274.1 | 137.05 | 429.98 | 185.45 | Pt | PtO2 | 133.3 | 133.3 | 66.65 | 329.31 | 84.78 | Au | | <0 | <0 | <0 | <0 | <0 | Hg | HgO | 90.79 | 90.79 | 90.79 | 298.91 | 54.38 | Pb | PbO | 218 | 218 | 218 | 389.87 | 145.34 | Bi | Bi2O3 | 573.9 | 191.3 | 286.95 | 370.78 | 126.25 |
|
|