Adsorption of Hexavalent Chromium from Aqueous Solution Using Chemically Activated Carbon Prepared from Locally Available Waste of Bamboo (<i>Oxytenanthera abyssinica</i>)

Dula, Tamirat; Siraj, Khalid; Kitte, Shimeles Addisu

doi:https://doi.org/10.1155/2014/438245

International Scholarly Research Notices

On this page

Abstract Introduction Materials Discussion Conclusion References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 438245 | https://doi.org/10.1155/2014/438245

Adsorption of Hexavalent Chromium from Aqueous Solution Using Chemically Activated Carbon Prepared from Locally Available Waste of Bamboo (Oxytenanthera abyssinica)

Tamirat Dula,¹Khalid Siraj,¹and Shimeles Addisu Kitte¹

Academic Editor: S.-H. Kim, Q. Zhou, C. Stalikas

Received12 Dec 2013

Accepted09 Jan 2014

Published23 Feb 2014

Abstract

This study reports on the adsorption of Hexavalent Chromium from aqueous solutions using activated carbon prepared from bamboo (Oxytenanthera abyssinica) waste by KOH activation heating in an electrical furnace at 1073 K for 3 hrs. Batch adsorption experiments were also carried out as a function of pH, contact time, initial concentration of the adsorbate, adsorbent dosage, and temperature of the solution. Kinetic studies of the data showed that the adsorption follows the pseudo-second-order kinetic model. Thermodynamic parameters showed that adsorption on the surface of BWAC was feasible, spontaneous in nature, and exothermic between temperatures of 298 and 318 K. The equilibrium data better fitted the Freundlich isotherm model for studying the adsorption behavior of Hexavalent Chromium by BWAC. IR spectrum for loaded and unloaded BWAC was obtained using FT-IR spectrophotometer. Adsorption efficiency and capacity of Hexavalent Chromium were found to be 98.28% at pH 2 and 59.23 mg/g at 300 K.

1. Introduction

Out of the various toxic pollutants chromium and its compounds are considered as the most dangerous inorganic water pollutants. Chromium compounds present in the effluents as a result of electroplating, metal finishing, magnetic tapes, wood preservation, leather tanning, pigments, and chemical manufacturing industries [1, 2]. They can also present in rocks, soils, plants, and animals. This heavy metal occurs in the environment in two oxidation states: trivalent Cr(III) and hexavalent Cr(VI). Cr(III) is considered as an essential trace nutrient for human, while Cr(VI), in turn, is highly toxic [3, 4]. Because of its mutagenic and carcinogenic properties, it includes skin irritation to lung cancer, as well as kidney, liver, and gastric damage [5].

Owing to the different toxicities of Cr(VI), there is a great interest in the speciation and determination of chromium species in environment. A number of treatment methods for the removal of chromium ions from aqueous solutions have been reported, mainly reduction, ion exchange, electrodialysis, electrochemical precipitation, evaporation, solvent extraction, reverse osmosis, chemical precipitation, and adsorption. Most of these methods suffer from drawbacks such as high operational costs and incomplete removal or the disposal of the residual metal sludge [6].

Adsorption by activated carbon is one of the effective techniques for Cr(VI) ion removal from wastewater because of the high surface area, highly porous character, and relatively low cost of the adsorbent [7, 8]. Activated carbon is especially known for the effective removal of organic chemicals, inorganic and heavy metal ion pollutants from wastewater in the laboratory as well as in various industries [9, 10]. Activated carbon can be synthesized by physical treatment, in which the surface of the carbonaceous material is exposed to a stream of gases at high temperature or chemical one where the carbonaceous material is exposed to activation agents such as acids, hydroxides, and zinc chloride at low temperature. The major raw materials for production of activated carbon are wood [11], coal [12], nutshells [13–15], and fruit stones [16, 17]. The main disadvantage of activated carbon is the weak mechanical properties of its surface and that it is easily burned at high operation temperature [18].

Some low cost activated carbons used for removing of Hexavalent Chromium ions such as groundnut husk [19], agrowaste [20], neem leaves [21], sawdust [22], wheat bran [23], rice bran [24], sago waste [25], green coconut shell [26], hazelnut shell [27], olive stone [28], gingelly oil cake [29], and peanut shell [30, 31] have all been reported as useful for preparing adsorbents.

Activated carbons derived bamboo wastes have shown great potential for the removal of organic and inorganic waste from the aqueous solution. In present research we have used bamboo waste to develop activated carbon by chemical activation method using KOH for the removal of Hexavalent Chromium ion.

2. Materials and Method

2.1. Preparation of Bamboo Waste Activated Carbon (BWAC)

Bamboo (Oxytenanthera abyssinica) waste was collected from Hosanna furniture manufacturing house, which is 230 Km from Addis Ababa (Ethiopia). The waste was air-dried for one month before use. Then it was cut into pieces approximately 1 × 1 cm² in size. It was washed with distilled water and dried at 378 K for 12 hrs. This bamboo precursor was immersed in a potassium hydroxide solution (25% by weight/volume). The mixture was dried in an oven overnight at 378 K. The dried bamboo/KOH mixture then was put on a crucible placed in an electrical furnace (Model Nabertherm (R)) for carbonization. The heating rate of carbonization was 10°C/min and continues until the final temperature of 1078 K was reached and it was kept at this temperature for 3 hrs. The produced activated carbon was then cooled down to room temperature. To remove remaining impurities such as ash, the synthesized BWAC was washed with 5% aqueous solution of HCl, followed by washing with distilled water several times until the pH of the washing solution was neutral. Prior to adsorption study HCl-treated activated carbon then was dried at 378 K for 12 hrs and ground into fine particle of 150 μm (sieve size) [32].

2.2. Preparation of Stock Solution

All chemicals used in this study were of analytical reagent grade and were used without further purification. Salt of K₂Cr₂O₇ was used for the preparation of the standard solutions for the study. The working solutions with different concentrations of the metal ions were prepared by appropriate dilutions of the stock solution with distilled water before use. The initial pH of the solution was adjusted accordingly with a pH meter. Thermostated water bath (Model Grant GLS400, England) was used as the medium for the process. The concentrations before and after adsorption of each metal ion were determined using atomic absorption spectroscopy (AAS) (Model Analytik Jena Nov AA 300).

2.3. Characterization of the Adsorbent

Fourier transform infrared (FT-IR) spectra of dried unloaded BWAC and Hexavalent Chromium loaded BWAC were recorded at 400–4000 cm⁻¹ using Spectrum 65, Perkin Elmer model FT-IR spectrophotometer, to determine the surface functional groups. Proximate analysis of total ash content, moisture content, volatile matter, and fixed carbon was also performed.

2.4. Adsorption Study

The adsorption study was carried out by contacting 0.25 g of the activated carbon with 25 mL of the metal ion solution under different conditions for a period of time in a boiling tube. The adsorption studies are conducted at 300 K using thermostated water bath to determine the effect of pH, contact time, and initial metal ion concentration on the adsorption. The residual metal ion was analyzed using atomic absorption spectrophotometer. All experiments were carried out in triplicate, and the concentrations given are average values. The initial metal ion concentration in the test solution and the adsorbent dosage were varied to investigate their effect on the adsorption kinetics. The adsorption studies were carried out at different temperatures. This is used to determine the effect of temperature on the thermodynamic parameters. The amount of adsorption at time , (mg/g), was calculated using the following relation [33]: where is the liquid phase concentrations of metal ion at any time and is the initial concentration of the metal ion in solution. V is the volume of the solution and is the mass of dry adsorbent .

The percentage removal of Hexavalent Chromium solution was calculated by using the following equation: where and are the initial and equilibrium concentrations of Hexavalent Chromium ion in solutions.

3. Result and Discussion

3.1. Characterization of the Adsorbent

Activated carbons are widely used as adsorbents due to their high adsorption capacity, high surface area, microporous structure, and a high degree of surface. Some important physicochemical characteristics of BWAC are given in Table 1. Moisture content of the carbon has no effect on its adsorptive power; it dilutes the carbon which is necessary for the use of additional weight of carbon during the treatment process. The BWAC samples were determined using standard test method for moisture in AC [38]. The lower ash content and volatile matter are attributed to lower inorganic content and higher fixed carbon. Higher value of fixed carbon shows that the adsorbent is having more efficiency and stability [39, 40].

FT-IR spectrum is an essential tool to identify the surface functional groups which can contribute significantly to enhance adsorption efficiency of the activated carbon by surface complexation. The spectra show that the activated carbon spectrum was closely identical to bamboo charcoal. A broad peak around 3458 cm⁻¹ was attributed to O–H stretching vibration of the hydroxyl group. A peak around 2923 cm⁻¹ was attributed to aliphatic methyl asymmetric C–H stretching. The peak observed around 1577 cm⁻¹ was because of CH₂ bending. The peak observed around 1457 cm⁻¹ can be attributed to the CH₃ bending. The bands around 1196 cm⁻¹ region were alcoholic C–O stretching, which produce strong bands. The very weak absorption which was observed at 850 and 603 cm⁻¹ was attributed to the long chain band of aliphatic alkane.

Figure 1 shows the FT-IR spectra of activated carbon before and after adsorption of chromium onto BWAC. It clearly shows that after the adsorption of Hexavalent Chromium on BWAC there is a small shift in frequency values and some of the frequency regions were absent. This observation indicated the participation of adsorption of Hexavalent Chromium on bamboo waste activated carbon (BWAC).

3.2. Effect of pH on Adsorption

The effect of pH on the adsorption of the metal ions was carried out within the range that was not influenced by the metal precipitation. The procedure used is similar to those earlier reported [33].

It can be seen in Figure 2 that the maximum of Hexavalent Chromium adsorption (98.28%) occurs at the lowest pH value. This finding has been reported by several investigators [41, 42], who have found that Hexavalent Chromium removal by activated carbon is enhanced in the acidic range of pH. The favorable effect of low pH can be attributed to the neutralization of negative charges on the surface of the adsorption by excess hydrogen ions, thereby facilitating the diffusion of hydrogen chromate ions and their subsequent adsorption. According to Muhammad et al. [43], is the dominant and ionic form of Hexavalent Chromium between pH 2.0 and 4.0. This ionic form was found to be preferentially adsorbed on the surface of carbon. The negative charges could result from oxygenated functional groups of basic character such as lactones or hydroxyl groups, physically adsorbed at the surface of the pores of activated carbon. In view of this observation the optimum pH for Hexavalent Chromium adsorption is taken to be 2.

3.3. Effect of Contact Time on Adsorption

The adsorptions of the metal ions by activated carbon were studied at various time intervals (3–120 min) and at a concentration of 100 mg/L. Figure 3 shows that chromium uptake is fast for the first 3–20 min, respectively, and, thereafter, they proceed at a slower rate and finally attain saturation. The initial fast reaction may be due to the increased number of vacant sites available at the initial stage; as a result there exists increased concentration gradient between adsorbate in solution and adsorbate in the adsorbent. Generally, by the time adsorption involves a surface reaction process, the initial adsorption is fast. Then, a slower adsorption would follow as the available adsorption site which is gradually decreased. This is due to the fact that a large number of vacant surface sites are available for adsorption during the initial stage, and after a lapse of time the remaining vacant surface sites are difficult to be occupied due to repulsive forces between the solute molecules on the solid and bulk phases [44]. Maximum percentage of adsorption (98.019% in 100 mg/L of solution) occurs at 20 min; after that the percentage adsorption remains uniform.

3.4. Effect of Adsorbent Dosage

Figure 4 depicts effect of adsorbent dosage on the adsorption of chromium on the BWAC. It can be seen that the percent adsorption increases from 97.105 to 98.45% with an increase in the dose of BWAC from 0.1 to 0.25 g and remained nearly constant at adsorbent quantities higher than 0.25 g. This is due to the greater availability of adsorption sites of adsorbent and thus making easier penetration of Cr(VI) to the adsorption sites [44]. Since the quantity of metal ion is constant, an increase in the amount of adsorbent above a quantity that can completely adsorb the available Cr(VI) had no apparent effect on further increase of percent adsorption. The adsorption capacity decreases from 24.28 to 8.2 for Hexavalent Chromium as dosage increased.

3.5. Effect of Initial Concentration on Adsorption

The effect of initial Hexavalent Chromium concentration on the adsorption efficiency of BWAC under optimum conditions of pH and contact time is shown in Figure 5. The adsorption efficiency increased from 92.87 to 98.71% for Hexavalent Chromium with increasing initial concentration from 25 to 150 mg/L but the solution reached equilibrium at 100 mg/L and after that no significant change occurred in adsorption.

The adsorption capacity increases from 9.87 to 59.23 mg/g for Hexavalent Chromium as the initial metal ion concentration increased from 25 to 150 mg/L. This is because a higher initial concentration enhanced the driving force between the aqueous and solid phases and increased the number of collisions between metal ions and adsorbents [45]. However, the actual percentage adsorption of the metal ions from solution increased with the increase in the initial metal ion concentrations. This may be due to the fact that, at lower concentrations, adsorption of the metal ions occurred slowly and further increase in initial metal ion concentration led to a competition for available bonding sites on the BWAC surface by the metal ions and thus increased adsorption. Similar adsorption procedures have also been reported by other researchers [46]. The adsorption capacity of an adsorbent which is obtained from the mass balance equation on the adsorbate in a system with solution volume is often used to acquire the experimental adsorption isotherms [47].

3.6. Effect of Temperature on Adsorption

Temperature is a highly significant parameter in the adsorption process. Experiments were performed at different temperatures (298 K, 300 K, 308 K, and 318 K) at optimum pH and contact time. It was observed that the percentage of adsorption increases from 97.02 to 98.39 for Hexavalent Chromium ions with the rise in temperature from 298 to 318 K. It is evident from Figure 6 that adsorption increases with the rising temperature because this adsorbent is not homogenous, and implying the active energy of adsorption sites is different. Therefore, at low temperature, the adsorption sites with lower active energy were occupied first, and the other sites with higher active energy were occupied as the temperature increases [29].

The rise of adsorption capacity with temperature was due to the increase in kinetic energy of adsorbent particles. Thus the collision frequency between adsorbent and adsorbate increases, which results in the enhanced adsorption onto the surface of the adsorbent. Secondly, at high temperature due to bond rupture of functional groups on adsorbent surface increases active adsorption sites, which may also lead to enhanced adsorption [48].

3.7. Adsorption Isotherms

Isotherm studies are essential to interpret the adsorption process adequately. Several models have been used to describe experimental data for adsorption isotherms. However, among these, the Langmuir and Freundlich isotherms are the most appropriate models for this study. According to the Langmuir isotherm, adsorption occurs at homogenous sites and forms a monolayer. In other words, once adsorbate is attached to a site, no further adsorption can take place [13]. The linear form of Langmuir isotherm equation is given as where (mg/g) is the equilibrium concentration of Hexavalent Chromium in the adsorbed phase and (mg/L) is the equilibrium concentration in the liquid phase. Langmuir constants, which are related to the adsorption capacity and energy of adsorption , can be calculated from the slope of the linear plot of versus ; a straight line with slope and intercept of is obtained. The essential characteristics of the Langmuir equation can be expressed in terms of a dimensionless factor, which is given as where is the highest initial Hexavalent Chromium ion concentration (mg/L). The values of separation factor have its usual significance.

Freundlich isotherm gives the relationship between equilibrium liquid and solid phase capacity based on the multilayer adsorption properties consisting of heterogeneous surface of the adsorbent. This isotherm is derived from the assumption that the adsorption sites are distributed exponentially with respect to the heat of adsorption [17]. The linear form of Freundlich isotherm is where is the amount adsorbed at equilibrium (mg/g), and are the Freundlich constant, is the heterogeneity factor which is related to the capacity and intensity of the adsorption, and is the equilibrium concentration . The values of and can be obtained from the slope and intercept of the plot of log against log . However, present investigation attempted to analyze the above-mentioned isotherm parameters at 300 K and the correlation coefficients were calculated by fitting the experimental equilibrium data for Hexavalent Chromium ion BWAC system using both Langmuir and Freundlich isotherms, which is presented in Table 2.

The results clearly show that the adsorption of Hexavalent Chromium on BWAC fits well with the Freundlich model. The fact that the Freundlich model is a good fit to the experimental adsorption data suggests physical adsorption as well as a heterogeneous distribution of active sites on the BWAC surface. The observed correlation coefficients for Freundlich isotherms were 0.775. If the value of is equal to unity, the adsorption is linear. If the value of constant is below unity, it implies that the adsorption process is unfavorable, and if the value of is above unity, adsorption is favorable [33]. In the present study, the value of at equilibrium was above unity, suggesting favorable adsorption. Furthermore, the values of the dimensionless factor, , were between 0 and 1 which suggest a favorable adsorption between BWAC and Hexavalent Chromium ion.

3.8. Adsorption Kinetic Studies

In order to evaluate the kinetic parameters, pseudo-first-order and pseudo-second-order models were implemented to analyze the experimental data. The pseudo-first-order equation can be expressed as [46] where and represent the amount of adsorbed (mg/g) at equilibrium and at any time t and is the first-order rate constant . From the plots of versus t in Figure 7, can be calculated from the slope and theoretical can be obtained from intercepts.

Pseudo-second-order equation can be given by where is the rate constant of second-order adsorption. The linear plots of versus determine as slope and as intercepts. The linear plots of pseudo-second-order model are shown in Figure 7.

The correlation coefficient, , of pseudo-first-order kinetics was 0.872 but the calculated (mg/g) value obtained from pseudo-first-order kinetics did not agree well with the experimental (mg/g) values as shown in Table 3. Thus it can be concluded that it is not appropriate to use the pseudo-first-order kinetic model to predict the adsorption kinetics for the adsorption of Hexavalent Chromium onto BWAC.

On the contrary, the correlation coefficient, , for the second-order kinetic model was almost equal to unity for all the concentrations signifying the applicability of the model. Moreover, the calculated (mg/g) values obtained from pseudo-second-order kinetics were in good agreement with the experimental (mg/g) values (Table 3). Thus it appeared that the system under study is more suitably described by pseudo-second-order kinetics which was based on the assumption that the rate limiting step may be chemisorptions concerning valances forces through sharing and exchange of electrons. The pseudo-second-order kinetics model has been successfully applied to several adsorption systems as reported in [46].

The amount of Hexavalent Chromium adsorbed per unit mass of adsorbent at time t, , as a function of the square root of the contact time, (Figure 8), was examined using the intraparticle diffusion model (Table 3) which is based on the theory proposed by Weber and Morris [49]: where (mg/g/min) is the intraparticle diffusion coefficient which was calculated from the slope of the linear portion of curves and C (mg/g) is intraparticle diffusion constant, that is, intercept of the line (mg/g). It is directly proportional to the boundary layer thickness. It is assumed that the larger the intercept, the greater the contribution of the surface adsorption in the rate-controlling step.

Intraparticle diffusion plays a significant role in controlling the kinetics of the adsorption process, if the plot of versus yields a straight line passing through the origin, with the slope giving the rate constant, , and . If the lines do not pass through the origin it is indicative of some degree of boundary layer control and this further shows that the intraparticle diffusion is not the only rate limiting step, but other kinetic models may also control the rate of adsorption [34, 50].

3.9. Thermodynamic Study

The thermodynamic parameters that help us to understand the nature of the adsorption of Cr(VI) ion on adsorbents are the standard change in Gibbs free energy (), the standard change in entropy (), and the standard change in enthalpy (). The enthalpy change () from 298.2 to 318.2 K was computed from the following equation: where · and ·· were calculated from the slope and intercept of the linear plot of versus . However, the calculated values of thermodynamic parameters are listed in Table 4. The negative value of enthalpy change confirms the exothermic nature of the adsorption process. The enthalpy value for adsorption process may be used to distinguish between chemical and physical adsorption. For chemical adsorption, values of enthalpy change range from −83 to −830 kJ/mol, while for physical adsorption they range from −8 to −25 kJ/mol. The low values of ΔH give clear evidence that the interaction of Hexavalent Chromium and BWAC was weak suggesting physical adsorption process [50]. The positive value of entropy, ΔS°, represents an increase in the degree of freedom of the adsorbed species which indicates that some changes occur in the internal structure of BWAC during the adsorption process. The negative values of Gibbs free energy, ΔG° demonstrate that the adsorption is rapid and spontaneous. The negative value of ΔG° ensures the feasibility of the process. Generally, ΔG° values range from 0 to −20 KJ/mol for physical adsorption and −80 to −400 KJ/mol for chemical adsorptions [34]. In this study, the ΔG° values ranged from −6.347 to −19.488 KJ/mol, indicating that adsorption is mainly physical.

3.10. Comparison of Hexavalent Chromium Adsorption with Different Adsorbents

The adsorption capacity of the adsorbents for the adsorption of Hexavalent Chromium has been compared with those of others reported in the literature and the values of adsorption capacity as presented in Table 5. The experimental data of the present investigation were compared with reported values. Results of our investigation revealed that BWAC has the highest percent adsorption and adsorption capacity.

4. Conclusion

Experimental findings of this work suggested that the adsorption of Hexavalent Chromium on BWAC is a physical adsorption process attaining equilibrium within 20 min. Both Freundlich and Langmuir models were used to fit the data to estimated model parameters but the overall data is better fitted by Freundlich isotherm. The kinetic studies conducted using the Weber and Morris equation showed that the adsorption mechanism involves intraparticle diffusion but it was not the fully operative mechanism in the adsorption of Hexavalent Chromium by BWAC. The pseudo-second-order kinetic model was found to be a better fit for the adsorption of Hexavalent Chromium by BWAC. Thermodynamic studies predict that the adsorption is feasible, spontaneous, and exothermic in nature at temperatures of 298.2, 308.2, and 318.2 K with negative values of standard change in Gibbs free energy (ΔG°), enthalpy (ΔH°), and positive values of standard entropy change (ΔS°).

Conflict of Interests

The authors declare that there is no conflict of interests.

Acknowledgment

The authors thankfully acknowledge the Department of Chemistry, College of Natural Science, Jimma University, Ethiopia, for providing all necessary facilities required to carry out this work.

References

V. K. Gupta, A. Rastogi, and A. Nayak, “Adsorption studies on the removal of hexavalent chromium from aqueous solution using a low cost fertilizer industry waste material,” Journal of Colloid and Interface Science, vol. 342, no. 1, pp. 135–141, 2010.
View at: Publisher Site | Google Scholar
W.-Q. Wang, M.-Y. Li, and Q.-X. Zeng, “Thermodynamics of Cr(VI) adsorption on strong alkaline anion exchange fiber,” Transactions of Nonferrous Metals Society of China, vol. 22, no. 11, pp. 2831–2839, 2012.
View at: Google Scholar
R. Dobrowolski and M. Otto, “Study of chromium(VI) adsorption onto modified activated carbons with respect to analytical application,” Adsorption, vol. 16, no. 4-5, pp. 279–286, 2010.
View at: Publisher Site | Google Scholar
J. O. Nriagu and E. Nieboer, “Chromium,” in Natural and Human Environment, Wiley, New York, NY, USA, 1988.
View at: Google Scholar
A. Mansri, K. I. Benabadji, J. Desbrières, and J. François, “Chromium removal using modified poly(4-vinylpyridinium) bentonite salts,” Desalination, vol. 245, no. 1–3, pp. 95–107, 2009.
View at: Publisher Site | Google Scholar
E. Demirbas, M. Kobya, E. Senturk, and T. Ozkan, “Adsorption kinetics for the removal of chromium (VI) from aqueous solutions on the activated carbons prepared from agricultural wastes,” Water SA, vol. 30, no. 4, pp. 533–540, 2004.
View at: Google Scholar
A. S. Sartape, P. D. Raut, and S. S. Kolekar, “Efficient adsorption of chromium(VI) ions from aqueous solution onto a low-cost adsorbent developed from limonia acidissima (wood apple) shell,” Adsorption Science and Technology, vol. 28, no. 6, pp. 547–560, 2010.
View at: Publisher Site | Google Scholar
R. A. Shawabkeh, “Adsorption of chromium ions from aqueous solution by using activated carbo-aluminosilicate material from oil shale,” Journal of Colloid and Interface Science, vol. 299, no. 2, pp. 530–536, 2006.
View at: Publisher Site | Google Scholar
L. Monser and N. Adhoum, “Modified activated carbon for the removal of copper, zinc, chromium and cyanide from wastewater,” Separation and Purification Technology, vol. 26, no. 2-3, pp. 137–146, 2002.
View at: Publisher Site | Google Scholar
Y. Jiang, Y. Wu, J. Liu, X. Xia, and D. Wang, “Ammonium pyrrolidinedithiocarbamate-modified activated carbon micro-column extraction for the determination of As(III) in water by graphite furnace atomic absorption spectrometry,” Microchimica Acta, vol. 161, no. 1-2, pp. 137–142, 2008.
View at: Publisher Site | Google Scholar
L. Khezami and R. Capart, “Removal of chromium(VI) from aqueous solution by activated carbons: kinetic and equilibrium studies,” Journal of Hazardous Materials, vol. 123, no. 1–3, pp. 223–231, 2005.
View at: Publisher Site | Google Scholar
J. Gañan, C. González-García, J. González, E. Sabio, A. Macías-García, and M. Díaz-Díez, “Preparation of activated carbons from bituminous coal pitches,” Applied Surface Science, vol. 238, no. 1–4, pp. 347–354, 2004.
View at: Google Scholar
M. Sekar, V. Sakthi, and S. Rengaraj, “Kinetics and equilibrium adsorption study of lead(II) onto activated carbon prepared from coconut shell,” Journal of Colloid and Interface Science, vol. 279, no. 2, pp. 307–313, 2004.
View at: Publisher Site | Google Scholar
S. Babel and T. A. Kurniawan, “Cr(VI) removal from synthetic wastewater using coconut shell charcoal and commercial activated carbon modified with oxidizing agents and/or chitosan,” Chemosphere, vol. 54, no. 7, pp. 951–967, 2004.
View at: Publisher Site | Google Scholar
R. A. Shawabkeh, D. A. Rockstraw, and R. K. Bhada, “Copper and strontium adsorption by a novel carbon material manufactured from pecan shells,” Carbon, vol. 40, no. 5, pp. 781–786, 2002.
View at: Publisher Site | Google Scholar
M. Kobya, E. Demirbas, E. Senturk, and M. Ince, “Adsorption of heavy metal ions from aqueous solutions by activated carbon prepared from apricot stone,” Bioresource Technology, vol. 96, no. 13, pp. 1518–1521, 2005.
View at: Publisher Site | Google Scholar
C. J. Durán-Valle, M. Gómez-Corzo, J. Pastor-Villegas, and V. Gómez-Serrano, “Study of cherry stones as raw material in preparation of carbonaceous adsorbents,” Journal of Analytical and Applied Pyrolysis, vol. 73, no. 1, pp. 59–67, 2005.
View at: Publisher Site | Google Scholar
S. Yenisoy-Karakaş, A. Aygün, M. Güneş, and E. Tahtasakal, “Physical and chemical characteristics of polymer-based spherical activated carbon and its ability to adsorb organics,” Carbon, vol. 42, no. 3, pp. 477–484, 2004.
View at: Publisher Site | Google Scholar
S. P. Dubey and K. Gopal, “Adsorption of chromium(VI) on low cost adsorbents derived from agricultural waste material: a comparative study,” Journal of Hazardous Materials, vol. 145, no. 3, pp. 465–470, 2007.
View at: Publisher Site | Google Scholar
X. J. Wang, Y. Wang, X. Wang et al., “Microwave-assisted preparation of bamboo charcoal-based iron-containing adsorbents for Cr(VI) removal,” Chemical Engineering Journal, vol. 174, no. 1, pp. 326–332, 2011.
View at: Publisher Site | Google Scholar
B. V. Babu and S. Gupta, “Adsorption of Cr(VI) using activated neem leaves: kinetic studies,” Adsorption, vol. 14, no. 1, pp. 85–92, 2008.
View at: Publisher Site | Google Scholar
S. S. Baral, S. N. Das, and P. Rath, “Hexavalent chromium removal from aqueous solution by adsorption on treated sawdust,” Biochemical Engineering Journal, vol. 31, no. 3, pp. 216–222, 2006.
View at: Publisher Site | Google Scholar
M. Nameni, M. R. Alavi Moghadam, and M. Arami, “Adsorption of hexavalent chromium from aqueous solutions by wheat bran,” International Journal of Environmental Science and Technology, vol. 5, no. 2, pp. 161–168, 2008.
View at: Google Scholar
E. A. Oliveira, S. F. Montanher, A. D. Andrade, J. A. Nóbrega, and M. C. Rollemberg, “Equilibrium studies for the sorption of chromium and nickel from aqueous solutions using raw rice bran,” Process Biochemistry, vol. 40, no. 11, pp. 3485–3490, 2005.
View at: Publisher Site | Google Scholar
N. Vennilamani, K. Kadirvelu, Y. Sameena, and S. Pattabhi, “Utilization of activated carbon prepared from industrial solid waste for the removal of chromium(VI) ions from synthetic solution and industrial effluent,” Adsorption Science and Technology, vol. 23, no. 2, pp. 145–160, 2005.
View at: Publisher Site | Google Scholar
G. H. Pino, L. M. S. De Mesquita, M. L. Torem, and G. A. S. Pinto, “Biosorption of heavy metals by powder of green coconut shell,” Separation Science and Technology, vol. 41, no. 14, pp. 3141–3153, 2006.
View at: Publisher Site | Google Scholar
M. Kobya, E. Demirbas, and M. Bayramoglu, “Modelling the effects of adsorbent dose and particle size on the adsorption of Cr(VI) ions from aqueous solutions,” Adsorption Science and Technology, vol. 22, no. 7, pp. 583–594, 2004.
View at: Google Scholar
A. A. Attia, S. A. Khedr, and S. A. Elkholy, “Adsorption of chromium ion (VI) by acid activated carbon,” Brazilian Journal of Chemical Engineering, vol. 27, no. 1, pp. 183–193, 2010.
View at: Google Scholar
K. B. Nagashanmugama and K. Srinivasanb, “Removal of chromium (VI) from aqueous solution by chemically modified gingelly oil cake carbon,” Indian Journal of Chemical Technology, vol. 18, no. 3, pp. 207–219, 2011.
View at: Google Scholar
L. C. Romero, A. Bonomo, and E. E. Gonzo, “Peanut shell activated carbon: adsorption capacities for copper(II), zinc(II), nickel(II) and chromium(VI) ions from aqueous solutions,” Adsorption Science and Technology, vol. 22, no. 3, pp. 237–243, 2004.
View at: Publisher Site | Google Scholar
Z. A. ALOthman, M. Naushad, and R. Ali, “Kinetic, equilibrium isotherm and thermodynamic studies of Cr(VI) adsorption onto low-cost adsorbent developed from peanut shell activated with phosphoric acid,” Environmental Science and Pollution Research, vol. 20, no. 5, pp. 3351–3365, 2013.
View at: Google Scholar
S. Hirunpraditkoon, N. Tunthong, A. Ruangchai, and K. Nuithitikul, “Adsorption cpacities of activated carbons prepared from bamboo by KOH activation,” World Academy of Science, Engineering and Technology, vol. 54, pp. 647–651, 2011.
View at: Google Scholar
P. Thamilarasu and K. Karunakaran, “Kinetic, equilibrium and thermodynamic studies on removal of Cr(VI) by activated carbon prepared from Ricinus communis seed shell,” Canadian Journal of Chemical Engineering, vol. 91, no. 1, pp. 9–18, 2013.
View at: Publisher Site | Google Scholar
B. K. Hamad, A. M. Noor, and A. A. Rahim, “Removal of 4-chloro-2-methoxyphenol from aqueous solution by adsorption to oil palm shell activated carbon activated with K₂CO₃,” Journal of Physical Science, vol. 22, no. 1, pp. 39–55, 2011.
View at: Google Scholar
M. Owlad, M. K. Aroua, and W. M. A. Wan Daud, “Hexavalent chromium adsorption on impregnated palm shell activated carbon with polyethyleneimine,” Bioresource Technology, vol. 101, no. 14, pp. 5098–5103, 2010.
View at: Publisher Site | Google Scholar
P. K. Ghosh, “Hexavalent chromium [Cr(VI)] removal by acid modified waste activated carbons,” Journal of Hazardous Materials, vol. 171, no. 1–3, pp. 116–122, 2009.
View at: Publisher Site | Google Scholar
W. Wang, X. Wang, X. Wang et al., “Cr(VI) removal from aqueous solution with bamboo charcoal chemically modified by iron and cobalt with the assistance of microwave,” Journal of Environmental Sciences, vol. 25, no. 9, pp. 1726–1735, 2013.
View at: Google Scholar
Annual Book of ASTM Standards, Standard Test Method for Moisture in Activated Carbon D2867-95.15.01. United State of America, 2004.
Annual Book of ASTM Standards, Standard Test Method for Total Ash Content of Activated Carbon. D2866-94. 15.01. United State of America, 1999.
Annual Book of ASTM Standards, Standard Test Method for Volatile Matter Content of Activated Carbon Samples D5832-95. 15.01. United State of America, 2003.
V. K. Garg, R. Gupta, R. Kumar, and R. K. Gupta, “Adsorption of chromium from aqueous solution on treated sawdust,” Bioresource Technology, vol. 92, no. 1, pp. 79–81, 2004.
View at: Publisher Site | Google Scholar
K. Selvi, S. Pattabhi, and K. Kadirvelu, “Removal of Cr(VI) from aqueous solution by adsorption onto activated carbon,” Bioresource Technology, vol. 80, no. 1, pp. 87–89, 2001.
View at: Publisher Site | Google Scholar
S. Muhammad, A. B. Alaadin, and N. A. Muhammad, “Electrocoagulation for the treatment of Wastewater for reuse in irrigation and plantation (Report),” Journal of Basic & Applied Sciences, vol. 7, no. 1, pp. 11–20, 2011.
View at: Google Scholar
D. Mohan, K. P. Singh, and V. K. Singh, “Trivalent chromium removal from wastewater using low cost activated carbon derived from agricultural waste material and activated carbon fabric cloth,” Journal of Hazardous Materials, vol. 135, no. 1–3, pp. 280–295, 2006.
View at: Publisher Site | Google Scholar
S. Li, X. Lu, X. Li et al., “Preparation of bamboo-like PPy nanotubes and their application for removal of Cr(VI) ions in aqueous solution,” Journal of Colloid and Interface Science, vol. 378, no. 1, pp. 30–35, 2012.
View at: Publisher Site | Google Scholar
N. Tewari, P. Vasudevan, and B. K. Guha, “Study on biosorption of Cr(VI) by Mucor hiemalis,” Biochemical Engineering Journal, vol. 23, no. 2, pp. 185–192, 2005.
View at: Publisher Site | Google Scholar
X. L. Jiang and Y. H. Jiang, “Evaluation of the adsorption of Cr(VI) by modified bamboo shells,” Applied Mechanics and Materials, vol. 361–363, pp. 709–715, 2013.
View at: Google Scholar
Z. Hu, L. Lei, Y. Li, and Y. Ni, “Chromium adsorption on high-performance activated carbons from aqueous solution,” Separation and Purification Technology, vol. 31, no. 1, pp. 13–18, 2003.
View at: Publisher Site | Google Scholar
J. W. Weber and J. C. Morris, “Kinetics of adsorption on carbon from solution,” Journal of the Sanitary Engineering Division, vol. 89, no. 2, pp. 31–60, 1963.
View at: Google Scholar
P. N. Dave, N. Pandey, and H. Thomas, “Adsorption of Cr(VI) from aqueous solutions on tea waste and coconut husk,” Indian Journal of Chemical Technology, vol. 19, no. 2, pp. 111–117, 2012.
View at: Google Scholar

Copyright

Copyright © 2014 Tamirat Dula et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

8231

Downloads

2339

Citations